Synthetic resins or natural rubbers -- part of the class 520 ser – Synthetic resins – From carboxylic acid or derivative thereof
Reexamination Certificate
2000-06-26
2003-03-04
Szekely, Peter (Department: 1714)
Synthetic resins or natural rubbers -- part of the class 520 ser
Synthetic resins
From carboxylic acid or derivative thereof
C528S060000, C528S074500, C528S295500, C528S335000
Reexamination Certificate
active
06528613
ABSTRACT:
BACKGROUND OF THE INVENTION
1. Field of the Invention
The present invention relates to resins or waxes made by reacting isocyanates with selected nucleophiles such as fatty acid reactants and amines. The nucleophiles are used to achieve certain desirable properties in urethane polyamide resins. The present invention also relates to solid imaging materials used in the rapid prototyping industry, as well as to phase change ink compositions, both generally and in specific compositions, containing such resins and/or waxes. Still further, the present invention relates to the process of using such phase change compositions containing such resins and/or waxes in a printing device.
2. Description of the Relevant Art
In general, phase change materials or inks (sometimes referred to as “hot melt inks”) are in the solid phase at ambient temperature, but exist in the liquid phase at the elevated operating temperature of an ink jet printing device. At the jet operating temperature, droplets of liquid ink are ejected from the printing device and, when the ink droplets contact the surface of the printing media, they quickly solidify to form a predetermined pattern of solidified ink drops. Phase change inks have also been investigated for use in other printing technologies such as gravure printing as referenced in U.S. Pat. No. 5,496,879 and German patent publications DE 4205636AL and DE 4205713AL assigned to Siegwert Farbenfabrik Keller, Dr. Rung and Co.
Phase change inks for color printing generally comprise a phase change ink carrier composition which is combined with a phase change ink compatible colorant. Preferably, a colored phase change ink will be formed by combining the above-described ink carrier composition with compatible subtractive primary colorants. Subtractive primary colored phase change inks can comprise four component dyes, namely, cyan, magenta, yellow and black. U.S. Pat. Nos. 4,889,506; 4,889,761; and 5,372,852 teach that the subtractive primary colorants employed typically may comprise dyes from the classes of Color Index (C.I.) Solvent Dyes, Disperse Dyes, modified Acid and Direct Dyes, and a limited number of Basic Dyes. The colorants can also include pigments as exemplified in U.S. Pat. No. 5,221,335, assigned to Coates Electrographics Ltd. U.S. Pat. No. 5,621,022 assigned to Tektronix, Inc., is directed to the use of a specific class of polymeric dyes in phase change ink compositions.
Phase change inks are desirable for ink jet printers since they remain in a solid phase at room temperature during shipping, long-term storage, and the like. Also, the problems associated with nozzle clogging due to ink evaporation are largely eliminated, thereby improving the reliability of ink jet printing. Furthermore, in the above-noted prior art phase change ink jet printers where the ink droplets are applied directly onto the printing medium, the droplets solidify immediately upon contact with the substrate, migration of ink along the printing medium is prevented and dot quality is improved. More recently, the use of phase change solid imaging material with ink jet print heads has permitted the rapid prototyping and manufacturing industry to increase speed, reduce costs and improve part quality. This is also true of the processes and solid imaging compositions described herein.
In addition to the above-referenced U.S. patents, many other patents describe materials for use in phase change ink jet inks. Some representative examples include U.S. Pat. Nos. 3,653,932; 4,390,369; 4,484,948; 4,684,956; 4,851,045; 4,889,560; 5,006,170; and 5,151,120; as well as EP Application Nos. 0187352 and 0206286. These materials can include paraffins, microcrystalline waxes, polyethylene waxes, ester waxes, fatty acids and other waxy materials, fatty amide-containing materials, sulfonamide materials, resinous materials made from different natural sources (tall oil rosins and rosin esters are an example) and many synthetic resins, oligomers, polymers and co-polymers.
Separately, PCT patent application WO 94/14902, which was published on Jul. 7, 1994 and is assigned to Coates Brothers PLC, teaches a hot melt ink containing a colorant and, as a vehicle for the hot melt ink an oligourethane having a melting point of at least 65° C. and obtained by reacting an aliphatic or aromatic diisocyanate with at least a stoichiometric amount of either: (I) a monohydric alcohol component; or (ii) a monohydric alcohol component followed by another different alcohol component; or (iii) a monohydric alcohol component, followed by a dihydric alcohol component, followed by a monohydric alcohol component.
This PCT patent application defines the monohydric alcohol component as either a monohydric aliphatic alcohol (e.g. C
1
to C
22
alcohols), an etherified dihydric aliphatic alcohol [e.g. propylene glycol methyl ether (PGME), dipropylene glycol methyl ether (DPGME), ethylene glycol butyl ether (EGBE), diethylene glycol butyl ether (DPGBE), tripropylene glycol butyl ether (PGBE) and propylene glycol phenyl ether (PPL)]; esterified dihydric aliphatic alcohol [e.g. the esterifying acid may be an ethylenically unsaturated acid (such as acrylic acid or methacrylic acid), thereby introducing ethylenic unsaturation into the oligourethane and rendering it suitable for eventual further additional polymerization (curing) after having been applied to a substrate by hot-melt printing], or dihydric polyakylene glycol. This PCT application further defined the dihydric alcohol component as a dihydric aliphatic alcohol or a dihydric polyalkylene glycol [e.g. ethylene glycol, polyethylene glycol (PEG 1500), polypropylene glycol (PPG 750), 1000 and 1500), trimethylene glycol, dipropylene glycol, methylpropanediol and 1.6-hexanediol].
Another PCT patent application, WO 97/12003 also assigned to Coates Brothers PLC, discloses hot melt ink jet base materials that are urethane-amide reaction products obtained from the reaction of isocyanates with one or more functional amides. The urethane-amides are intended to have improved compatibility with viscosity modifying additives.
Also, PCT Patent Application WO 94/04619, assigned to the General Electric Company, teaches the use of ionomeric materials in combination with image forming agents to form a hot melt ink jet ink. The ionomeric materials can include many different types of copolymeric or polymeric ionomers, including carboxyl-functional polyurethanes prepared from a diol or polyol and a hydroxyl acid. Many other carrier materials and colorants for the image forming agent of the invention are included in this PCT application.
There is still a need for new materials for novel and different applications of phase change materials. There is also a need for relatively low viscosity resins, including nonpolymeric resins, and waxes designed for phase change ink jet and other forms of phase change material printing and rapid prototyping applications. These needs are solved by the present invention by providing a means to create a solubilizing agent that is an isocyanate-derived material for specific applications.
BRIEF SUMMARY OF THE INVENTION
It is an aspect of the present invention that a urethane compound comprising the reaction product of selected isocyanates with selected fatty acid reactants and selected amines are obtained.
It is another aspect of the present invention that a urethane compound comprising the reaction product of selected isocyanates with selected amines or mixtures of selected amines and fatty acid reactant are obtained.
It is still another aspect of the present invention that a phase change solid imaging material or a phase change ink carrier composition which is an admixture of a viscosity modifying agent, a tackifier, a urethane polyamide compound, and a polyamide resin is obtained.
It is still a further aspect of the present invention that a phase change ink composition comprising an admixture of (a) a phase change carrier composition containing at least one isocyanate-derived resin or wax, and (b) a phase change ink compatible colorant is
Bui Loc V.
Nguyen My T.
3-D Systems, Inc.
D'Alessandro Ralph
Szekely Peter
LandOfFree
Phase change solid imaging material does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Phase change solid imaging material, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Phase change solid imaging material will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3049180