ABSTRACT:
BACKGROUND OF THE INVENTION
1. Field of the Invention
The present invention is directed to a method of generating or modifying a pattern of topically specific magnetic properties in a planar magnetic surface and to magnetic storage devices comprising one or more surfaces provided with such patterns.
2. Discussion of the Prior Art
Magnetic devices for recording and storing electronic information have come a long way from magnetic tapes to current storage devices, such as state-of-the-art hard disks with capacities in the Gigabyte range.
Generally, increases of storage capacity in the past were due, at least in part, to an increase of the storage density, e.g. as expressed in terms of bits per square centimeter (b/cm
2
). For example, the first magnetic disc introduced by IBM in 1956 had a storage density of about 300 b/cm
2
(10
2
); a first “magic” threshold of 100 000 b/cm
2
(10
5
) was reached about twenty years later. Currently, storage densities of hard disks and other commercially available planar magnetic media are in the range of hundred million b/cm
2
(10
8
) so that even an “entry level” hard disc of an every-day computer has a storage capacity of several Gigabytes.
While it is expected that technological progress will generally continue at such rates, physical limits of the storage density of planar magnetic media can be predicted because of the finite size of the smallest magnetic entities, or “domains”, and the limits of clear discrimination between the unit areas, i.e. the capability of clearly distinguishing between one stored bit and its immediate neighbors. In fact, an upper limit of the order of 10 Gigabits/cm
2
(10
10
) could be expected because of the “paramagnetic limit” yet increases of storage density in redesigned planar magnetic devices of several orders of magnitude seem possible.
In an attempt to increase data storage density in magnetic recording, Chappert, C. et al (Science, 280 (1998), 1919-1922) in a report about planar patterned media (this report being incorporated herein for all purposes by way of reference,) have proposed to produce magnetic patterns by impacting cobalt-platinum (Co—Pt) sandwich structures and multilayers with ion irradiation, i.e. impacting with atomic particles, through a lithographic resist mask for magnetic patterning without significant modification of roughness and optical properties of the sandwich or multilayer structures. It has been argued that bombardment (this term being used synonymously with “irradiation” and including irradiation with confined or “narrow” beams as well as with broad beams) with such atomic particles changes the Pt concentration profile at each Co layer interface which suggests the possibility of locally changing magnetic properties by a technique similar in effect to that of semiconductor doping, i.e. by irradiation through a lithographically defined mask. A simple sandwich structure was irradiated at a fluence or dose of 10
16
ions/cm
2
with 30 keV He
+
ions, i.e. a bombardment of sufficient intensity to make the irradiated area in the particular sample paramagnetic at room temperature.
The authors concluded that magnetic patterning induced by bombardment with such atomic particles would allow to create adjoining regions with differing magnetic properties, such as perpendicular versus in-plane magnetization, or paramagnetic, or stripe domain structures in an otherwise optically smooth film.
SUMMARY OF THE INVENTION
However, since both applicability as well as effectiveness of bombardment with atomic particles, such as ions, for magnetic patterning may be limited, it is a main object of the present invention to extend the possibilities of generating or modifying patterns of topically specific magnetic orientation in a planar magnetic surface, or film, and to provide improved magnetic storage and recording devices comprising one or more surfaces provided with such patterns.
We have found that this object and further improvements can generally be achieved according to the invention by subjecting magnetic materials to the impact of energized subatomic particles, namely electrons, neutrons or photons (X-rays). It has been found that such irradiation is capable of causing irreversible changes of magnetic properties, such as magnetic anisotropies as well as domain pinning behavior.
Further, we have established that bombardment with energized subatomic particles, notably in the form of electron radiation, can be used advantageously to magnetically pattern films by irradiating the material either by a narrow or broad beam of subatomic particles, or by shining such a beam through a layer of a material that is substantially opaque to the radiation used except for openings where the radiation is to impact the layer to be treated according to the invention, e.g. a shadow mask or a patterned resist, such as patterned by lithographic means.
The method according to the invention can be extended to include sequential patterning of multilayer films as they are grown in order to optimize their magnetic properties. In view of considerations of energy exchange properties, it is expected that energized subatomic particles other than electrons, i.e. high-energy photons such as X-ray radiation, as well as energized neutrons, will be of similar utility according to the invention as electron radiation.
Thus, according to a first general aspect, the invention provides for a method of generating or modifying a pattern of topically specific magnetization including but not limited to magnetic spin orientation in a surface of a material, preferably in the form of a thin or ultrathin layer, which material is, at least potentially, ferromagnetic; the method according to the invention comprises the step of subjecting the surface to a controlled impact of energized subatomic particles directed at the surface for producing a predetermined pattern of discrete magnetized areas on the surface.
According to a second general aspect, the invention provides for novel magnetic recording or storage devices, such as hard disks or readers for magnetically coded information comprising at least one magnetic surface provided with a pattern of topically specific modifications in a ferromagnetic surface. The pattern comprises a plurality of magnetic domains obtainable by impacting the surface with energized subatomic particles selected from the group consisting of electrons, photons, and neutrons; in a preferred group of such magnetic devices the discrete magnetized area has a largest planar dimension in the order of 0.1-5 &mgr;m.
The following definitions of terms believed to be essential for understanding the invention will be used herein:
The term “topically specific” is intended to refer to a specific site, or plurality of specific sites (also termed “pattern”), on and in a surface which may be positioned substantially at the top of an electronic recording and/or storage device structure so as to form an interface with the surrounding atmosphere or with a lubricating outermost layer of the type known per se in the art; alternatively, the site or pattern may be situated in a stack of layers of an electronic recording and/or storage device structure, it being implied that such structures are formed of normally solid materials.
The terms “magnetization” and “magnetic modification” are intended to include any type of magnetic orientation, or change of a given magnetic orientation, in a material that is, or can be made, magnetic. A magnetic modification also includes but is not restricted to a change from one magnetic state, e.g. ferromagnetic or ferrimagnetic, into any other magnetic state or nonmagnetic state, such as paramagnetic, and vice versa comprising at least one magnetic surface provided with a pattern of topically specific modifications in a ferromagnetic surface, said pattern comprising a plurality of magnetic domains obtainable by impacting said surface with energized subatomic particles selected from the group consisting of electrons, photons, and neutrons.
For brevity, the term “ferromagnetic” will be used herein to incl
Allenspach Rolf
Bischof Andreas
Duerig Urs T.
Faber Alan T.
McGinn & Gibb PLLC
Underweiser, Esq. Marian
LandOfFree
Patterning of magnetic media does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Patterning of magnetic media, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Patterning of magnetic media will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2839989