Active solid-state devices (e.g. – transistors – solid-state diode – Combined with electrical contact or lead – Of specified configuration
Reexamination Certificate
2000-11-28
2003-12-02
Chaudhuri, Olik (Department: 2823)
Active solid-state devices (e.g., transistors, solid-state diode
Combined with electrical contact or lead
Of specified configuration
C257S774000, C438S598000, C438S622000, C438S637000
Reexamination Certificate
active
06657306
ABSTRACT:
BACKGROUND OF THE INVENTION
To improve the performance and, particularly, speed of an electronic circuit system constituted by a plurality of semiconductor chips, it has become increasingly important to reduce the length of the interconnections between the semiconductor chips to a minimum.
For this purpose, a technique of minimizing the interconnections between a plurality of semiconductor chips by stacking them has been studied instead of the conventional method of mounting a plurality of semiconductor chips two-dimensionally on a multilayer board. Such a semiconductor device formed by stacking a plurality of semiconductor chips is called a multichip module.
In addition, with the use of a multichip module of this type, different types of semiconductor chips manufactured by different processes can be stacked on each other into one hybrid semiconductor device.
To manufacture a multichip module, vertically stacked semiconductor chips must be electrically connected. For the realization of such connection, the present inventors have already proposed the use of connection plugs (chip-through plugs) that extend through vertically stacked semiconductor chips to connect them (Japanese Patent Application No. 9-305784).
BRIEF SUMMARY OF THE INVENTION
A paste according to the present invention is characterized by containing solids having a conductive substance and a resin, and a solvent for dissolving the resin, wherein a solids content is not less than 60 vol %.
In the present invention, the solids content indicates the ratio of solids (e.g., metals, glass, and resins) in a paste, which are left on a substrate upon hardening the paste to the total paste (solids+solvent). In the following description, this ratio indicates the volume ratio unless otherwise specified.
In the present invention, the solids content of a paste is set to 60 vol % or more for the following reason. When a paste is hardened (dried) after it is buried in a trench with a squeegee, the solvent in the paste volatilizes.
Upon this volatilization of the solvent, the volume of the paste reduces. If the volume reduction of the paste is large, the trench cannot be filled with the paste. A deterioration in buried shape due to such a volume reduction can be effectively prevented by increasing the solids content of the paste.
When the solids content is set to 60 vol % or more as in the present invention, in particular, occurrence of a volume reduction that causes connection failures and the like can be effectively prevented, and the trench can be filled with the paste with a good buried shape.
In addition, another paste according to the present invention is characterized by containing solids having a conductive substance and a resin, and a solvent for dissolving the resin, wherein a viscosity ratio is not more than 2.
In the present invention, the viscosity ratio of a paste indicates the ratio of viscosity changes in a case wherein the viscosity of the paste is measured with a rotational viscometer at rotational speeds that differ by one order of magnitude.
Assume that the viscosity of a given paste is measured with the rotational viscometer at different rotational speeds, and viscosities of 200 Pa·s and 100 Pa·s are respectively measured at 10 rpm and 100 rpm. In this case, the viscosity ratio is 200 Pa·s/100 Pa·s =2. The burying ratio of a viahole is the ratio of the paste to the sectional area of the viahole when the cross-section of the viahole is observed after a paste burial test.
In the present invention, the viscosity ratio of a paste is set to 2 or less for the following reason. When the viscosity ratio is high, the viscosity of the paste receiving force from the squeegee becomes low. When the paste receives no force, the viscosity increases. For this reason, when the paste is buried in a trench with the squeegee, the viscosity of the paste becomes high at the bottom portion of the trench. This makes it difficult to bury the paste.
If, however, the viscosity ratio is set to 2 or less as in the present invention, an increase in the viscosity of the paste at the bottom portion of the trench can be effectively suppressed. This prevents formation of voids that cause a connection failure and an increase in resistance. Hence, the trench can be filled with the paste.
Furthermore, still another paste according to the present invention is characterized by containing solids having a conductive substance and a resin, and a solvent for dissolving the resin, wherein a solids content is not less than 60 vol % and a viscosity ratio is not more than 2.
The trench can be filled with this paste with a good buried shape.
In consideration of the buried shape, the viscosity of the above paste is preferably 200 pas or less. In addition, if the paste is to be used for a connection plug, the main component of the paste should be a conductive substance.
A connection plug according to the present invention is a connection plug made of a paste containing powder particles having different average sizes and buried in a connection hole. This connection plug is characterized in that the paste contains 10% or more of a powder having an average particle size of 3 &mgr;m or more.
In this case, the paste preferably contains 10% or more of a powder having an average particle size of 1 &mgr;m or more. The powder may be the main component of the paste or another component. For example, the connection hole is a through hole extending through a semiconductor chip.
The viscosity of the paste is determined by the total surface area of powder particles in the resin contained in the paste. As the total surface area increases, the viscosity decreases. With the use of a connection plug containing a powder of a large average particle size as in the present invention, therefore, the paste as the connection plug can be buried in a trench with a good buried shape. In addition, according to the study conducted by the present inventors, it was found that the occurrence rate of cracks could be reduced sufficiently by setting the content of such a powder to 10% or more.
A burying method according to the present invention is characterized in that a paste according to the present invention is buried in a trench formed in the surface of a substrate.
With this arrangement, a good buried shape can be realized even by a burying method using a squeegee.
In addition, the burying method according to the present invention is characterized in that a powder dispersion is applied on a region including a trench formed in the surface of a substrate, and the powder is precipitated in the solution, thereby filling the trench with the powder.
According to this arrangement, since the trench is filled with the small-volume powder that precipitates, a deterioration in buried shape, e.g., formation of a void, is suppressed.
In this case, as the above dispersion, a solution to which a resin is added is preferably used. With the use of such a solution, the powder particles can be temporarily fixed with the resin.
In addition, the powder preferably partially contains glass. With the use of this powder, the glass melts in a calcination process to fill the trench without any recess.
A method of manufacturing a semiconductor device according to the present invention is characterized by comprising the steps of forming a trench in a surface of a substrate, filling the trench with a calcination type paste formed inside and outside the trench, temporarily hardening the paste, removing an excess portion of the paste outside the trench, and calcining the paste.
In the present invention, the excess portion of the paste is removed in the step of temporarily hardening the paste, in which the paste can be easily removed, instead of the step after calcination in which the paste is difficult to remove. Even if, therefore, the width of the trench increases, and the amount of paste increases, an excess paste portion can be removed without taking much time.
According to the present invention, therefore, even if the width of the trench is increased to decrease the resistance of the connection plug, a
Hayasaka Nobuo
Hisatsune Yoshimi
Kimura Manabu
Sasaki Keiichi
Brewster William M.
Chaudhuri Olik
Finnegan Henderson Farabow Garrett & Dunner L.L.P.
LandOfFree
Paste including a mixture of powders, connection plug,... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Paste including a mixture of powders, connection plug,..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Paste including a mixture of powders, connection plug,... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3154950