ABSTRACT:
FIELD OF THE INVENTION
The present invention relates to improvements in an ozone generating electrolysis cell employing lead dioxide as a catalyst in generating ozone through the electrolysis of water, and improvements in a method of fabricating an ozone generating electrolysis cell. More particularly, the present invention relates to improvements in a method of forming the catalyst.
BACKGROUND OF THE INVENTION
A method of industrial production of ozone using an electrolysis cell has been generally known.
FIG. 5
is a typical sectional view of a central part of a conventional electrolysis cell
101
. The electrolysis cell
101
includes a plate-shaped anode (hereinafter referred to as “anodic electrode plate”)
103
, a plate-shaped cathode (hereinafter referred to as “cathodic electrode plate”)
104
, and a proton exchange membrane (hereinafter abbreviated to “PEM”)
102
sandwitched between the anodic electrode plate
103
and the cathodic electrode plate
104
.
The anodic electrode plate
103
is a mesh or porous structure permeable to air and water. A basic material of the anodic electrode plate
103
is titanium. As shown in
FIG. 5
, at least a surface of the anodic electrode plate
103
facing the PEM
102
is coated with a platinum layer
106
. The platinum layer
106
can be formed by a plating process. A catalyst layer
105
containing lead dioxide is interposed between the platinum layer
106
and the PEM
102
.
A basic material of the cathodic electrode plate
104
is a stainless steel or titanium. The cathodic electrode plate
104
is a mesh or porous structure permeable to air and water. As shown in
FIG. 5
, a surface of the cathodic electrode plate
104
facing the PEM
102
is coated with a hydrogen generating catalyst layer
107
containing a metal, such as platinum.
An anode collector plate
108
and a cathode collector plate
109
are attached to the outer surfaces of the electrode plates
103
and
104
, respectively, to connect the electrode plates
103
and
104
to a power source. The components laminated between the anode collector plate
108
and the cathode collector plate
109
are compressed to connect the same electrically. The collector plates
108
and the cathode collector plate
109
are provided with a plurality of openings
110
and a plurality of openings
111
, respectively. Thus, a plurality of water passages or air passages are formed between the exterior of the electrolysis cell
101
and the PEM
102
through the electrode plates
103
and
104
and the collector plates
108
and
109
.
Water is supplied through the plurality of openings
110
to the electrolysis cell
101
and electric current is supplied through the electrode plates
103
and
104
for the electrolysis of water. Then, hydrogen ions migrate from anodic electrode plate
103
through the PEM
102
toward the cathodic electrode plate
104
, electrons are supplied to hydrogen ions by the cathodic electrode plate
104
to produce hydrogen. At the same time, oxygen is produced at the anodic electrode plate
103
. Part of the oxygen is converted by the catalytic action of the catalyst layer
105
containing lead dioxide into ozone.
As mentioned above, the catalyst layer
105
containing lead dioxide of the electrolysis cell
101
augments ozone generation. Therefore, ozone generating efficiency and the reliability of the electrolysis cell
101
are greatly dependent on the condition of the catalyst layer
105
. In the conventional electrolysis cell
101
, a lead dioxide film is deposited on the surface of the anodic electrode plate
103
by electrodeposition. The platinum layer
106
is used to improve the adhesion of lead dioxide deposited on the anodic electrode plate
103
by electrodeposition.
The lead dioxide film thus formed is hard and inflexible. Consequently, the lead dioxide film has a drawback that the same is subject to cracking and comes off the anodic electrode plate
103
. Therefore it is impossible to mass-produce anodic electrode plates of a desired shape by depositing lead dioxide in a lead dioxide film on a surface of a titanium plate having a large area by electrodeposition and cutting the titanium plate coated with the lead dioxide film in the desired shape because of the foregoing drawback of the lead dioxide film. Therefore, a conventional method makes titanium plates of a desired shape by cutting a large titanium plate and individually forming lead dioxide films on the titanium plates by electrodeposition to make anodic electrode plates, which is unsuitable for mass production and increases the manufacturing cost of the electrolysis cell.
Physical irregularities are liable to be formed in a film formed by electrodeposition, a film formed by electrodeposition is liable to have irregular resistance and it is difficult to form a smooth film of a uniform film quality by electrodeposition. When a lead dioxide film having physical irregularities and a non-uniform film quality is pressed against a PEM, portions having different resistance of the lead dioxide film are pressed in different degrees of contact against the PEM. Consequently, the PEM has portions differing from each other in electric conductivity. Portions having a high resistance generate heat when a current flows therethrough. The heat generated by the PEM reduces ozone generating efficiency and it is possible that the heat damages the PEM. Therefore, conditions for electrodeposition including the temperature and the concentration of an electrodeposition solution are controlled severely and the conditions are adjusted minutely by manual operations to form a uniform film by electrodeposition, which increases the manufacturing cost.
Since the electrodeposition of a lead dioxide film is performed in an oxygen atmosphere, the energy level of the crystal lattice of lead dioxide tends to be dependent on how the conditions were during electrodeposition. The energy level of a lead dioxide film as deposited by electrodeposition falls with time and hence the physical properties of lead dioxide are subject to change with time. It is actually experienced that the ozone generating efficiency of the ozone generating electrolysis cell is dependent on time elapsed after incorporation of the lead dioxide film formed by electrodeposition into the electrolysis cell, (i.e., whether a current is supplied immediately after incorporation of the lead dioxide film into the electrolysis cell, or whether a current is supplied some time after incorporation of the lead dioxide film into the electrolysis cell, electrolysis is either started immediately after the commencement of supplying water to the electrolysis cell or electrolysis is started some time after the commencement of supplying water to the electrolysis cell, respectively) and operating conditions of the electrolysis cell. Such performance of the electrolysis cell is a significant problem in the reliability of the electrolysis cell.
To cope with those problems in the electrodeposited lead dioxide film, a technique disclosed in Japanese Patent Laid-Open No. Hei 8-213027 (Inventor: Kato) employs a flexible catalyst sheet containing lead dioxide. More concretely, a catalyst sheet is formed by filling numerous voids in an oriented, porous polytetrafluoroethylene sheet (PTFE sheet) with a mixture of lead dioxide and a solid electrolytic resin, wherein the PEM is also formed from this resin. The catalyst sheet, i.e., anodic catalyst, a PEM and a cathodic layer, i.e. a carbon paper sheet containing platinum, are superposed in that order to form a superposed structure. The superposed structure is compressed and heated at a temperature in the range of 120 to 140° C. by hot pressing to obtain a laminated structure. The laminated structure is sandwiched between an anodic electrode plate and a cathodic electrode plate to complete an electrolysis cell.
A technique disclosed in Japanese Patent Laid-open No. Hei 11-131276 (Inventor: Mitsuta et al.) spreads lead dioxide powder on a PTFE sheet laminated to a PEM to form a catalyst sheet. An anode collector plate, an anodic elect
Gorgos Kathryn
Take-One Office, Ltd.
Tran Thao
Wenderoth , Lind & Ponack, L.L.P.
LandOfFree
Ozone generating electrolysis cell and method of fabricating... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Ozone generating electrolysis cell and method of fabricating..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Ozone generating electrolysis cell and method of fabricating... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2562022