Stock material or miscellaneous articles – Web or sheet containing structurally defined element or... – Including a second component containing structurally defined...
Reexamination Certificate
1999-02-26
2002-04-23
Copenheaver, Blaine (Department: 1771)
Stock material or miscellaneous articles
Web or sheet containing structurally defined element or...
Including a second component containing structurally defined...
C428S421000, C428S422000
Reexamination Certificate
active
06376062
ABSTRACT:
BACKGROUND OF THE INVENTION
1. Field of the Invention
This invention relates to plastics-based overlay materials, in particular for bearing bushes, and to use thereof and to a composite ultilayer material in which this overlay material is used.
2. Description of Related Art
Bearing materials with plastics-based overlays are known as single-layer, two-layer or three-layer composite materials: solid plastics bearings, bearings with an outer metallic backing and directly applied or adhered plastics, other such with internal wire cloths, as well as three-layer bearings of backing metal, a sintered porous metal layer and a covering layer formed on and in the pores. All these bearings are generally used in areas in which the use of lubricants is impossible or undesirable. For this reason, they must provide these lubricants themselves when in operation.
Multilayer materials differ from solid plastics materials, for example by a negligible tendency towards cold flow under load, by substantially better heat conductivity and, in connection therewith, by markedly higher possible pv values. However, solid plastics materials may also be advantageous in certain cases, e.g. for reasons of cost.
Among three-layer materials, it is possible to distinguish further between those with overlays based on fluorothermoplastics, such as PTFE, FEP etc., and those with overlays based on other plastics, such as PEEK for example. The latter two groups differ in their manner of operation: while, in the case of PTFE-based materials, the bronze intermediate layer is the “active” component of the overlay and acts like a filler, the other plastics materials use it only as an anchoring means. If there is sufficient affinity to the metal backing, these plastics materials permit the production of true two-layer materials, but they may also be applied with the aid of an adhesive. On the active overlay itself the thermoset or thermoplastics material then assumes the supporting role of the bronze.
Bearing materials of filled fluorothermoplastic films adhered to metal or other such materials with wire cloths incorporated in the plastics are also known, which may likewise be adhered to a metal backing or may also be used without a rigid metal backing.
For universal applicability and ease of production, the most advantageous materials are three-layer materials based on fluorothermoplastics such as PTFE, which also exhibit the highest performance and temperature-resistance. In the production process, homogeneous PTFE/filler pastes are produced by means of a plastics dispersion and the final composite material is produced by a concluding step comprising sintering of the PTFE subsequent to rolling thereof onto the backing material.
Some of the most commonly used fillers for such materials are lead and molybdenum disulphide, these materials providing virtually equal performance levels. These fillers may also be used in the presence of lubricants.
If a solution to constructional problems is sought using maintenance-free, space-saving plain bearings with a PTFE overlay, careful note must be taken of their upper loading limits, since, in the case of the above-mentioned materials comprising lead or MoS
2
alone, these have a pv value of less than 2 MPa m/s in the average load and speed range (0.5-100 MPa and 0.02-2 m/s).
It is known from DE 41 060 01 A1 and DE 195 066 84 A1 that the use of PbO as a filler may also result in higher performance materials, but the use of materials such as lead which may be potentially damaging to health is becoming increasingly unacceptable. In the food processing industry it is out of the question.
Although the possibility of using poly-(p-phenyleneterephthalamide) as a filler in self-lubricating PTFE-based bearing materials is often mentioned, it is used without exception in the form of fibres, such as in GB 2291879 A for example.
WO 95/02772 describes a special type of fibrillated fibre, which is incorporated into the PTFE matrix. The fibrous form causes problems with homogeneous incorporation into the PTFE matrix and necessitates corresponding special production devices. Moreover, such fibres exhibit the disadvantage that they contain inhalable particles and are suspected of being carcinogenic.
The fibres are incorporated into the matrix in the manner of irregular wickerwork and so reduce shattering and erosion of the otherwise soft PTFE matrix.
References to aramid fibres repeatedly occur, e.g. in WO 97/03299 or GB 21 77 099 A, as a neutral element in fibrous form which may be replaced by other fibres and is therefore clearly not essential to the achievement of any particular characteristic.
A fundamental reason for the suitability and use of such fibres is their exceptional mechanical characteristic values—very high tensile strength and modulus of elasticity—which find their basis in the particularly high degree of molecular orientation in the longitudinal direction of the fibres and the strong physical parallel linkage of the individual rigid molecular strands.
SUMMARY OF THE INVENTION
The object of the invention is to provide an overlay material which extends the above-mentioned advantages of materials containing PTFE to the effect that they may be more heavily loaded without its being necessary to resort to the use of lead or lead compounds.
This object is achieved according to the first variant of the invention by an overlay material which contains at least one powder-form polyaramid, the content of which, based on the total amount of PTFE (polytetrafluoroethylene) or of the mixture of PTFE and the other fluorothermoplastics and the polyaramid, amounts to 10-50 vol. %.
According to a second variant of the invention, this overlay material may be incorporated into a matrix material comprising a different plastics material from that mentioned above, wherein the content of the matrix material based on the total overlay material amounts to 60-95 vol. %. The matrix material may be polyphenylene sulfide (PPS), polyamide (PA), polyvinylidene fluoride (PVDF), polysulfone (PSU), polyethersulfone (PES), polyetherimide (PEI), polyether etherketone (PEEK) and/or polyimide (PI).
DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENT
It has surprisingly been found that the addition of polyaramid powder, preferably of poly-(p-phenyleneterephthalamide) (PPTA) and/or poly-(p-benzamide) (PBA) is sufficient significantly to increase the wear resistance and load carrying capacity of materials with overlays comprising a PTFE-based solid lubricant composition.
It has proven possible to increase performance so much that pv values of over 4 MPa m/s may be achieved for the average load and speed range under lubricant-free conditions.
Investigation of the properties, for example of the two-component system PTFE/PPTA, has shown that the mixture must contain 10-50 vol. % PPTA and 50-90 vol. % PTFE to achieve said advantageous properties. Particularly advantageous properties are achieved if the mixture contains 10 to 30 vol. % PPTA. It was also possible to confirm these results for other polyaramids.
The particle size of the powder used may be 100 &mgr;m but is preferably <50 &mgr;m.
Ratios other than those according to the invention have proved unable to provide any substantial improvements in relation to the prior art. However, it is possible to use additional suitable components within the framework of the limits imposed on the polyaramid content, the polyaramid content preferably not falling below 10 vol. % based on the total amount of PTFE or the mixture of PTFE and the other fluorothermoplastics as well as the polyaramid and the further components. These further components may, for instance, comprise thermosets or high temperature thermoplastics, e.g. polyimides or polyamide imides, other solid lubricants, e.g. boron nitride or molybdenum sulphide, pigments, e.g. coke or iron oxide, fibrous materials, e.g. graphite or aramid fibres, or hard materials such as boron carbide or silicon nitride for example.
Suitable fluorothermoplastics whose melting point exceeds 260° C. for use in combination with PTFE are PFA (per
Copenheaver Blaine
Federal-Mogul Wiesbaden GmbH & Co. KG
Reising Ethington Barnes Kisselle Learman & McCulloch PC
Ruddock Ula C.
LandOfFree
Overlay material and composite multilayer material does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Overlay material and composite multilayer material, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Overlay material and composite multilayer material will most certainly appreciate the feedback.