Plastic and nonmetallic article shaping or treating: processes – Optical article shaping or treating – Optical fiber – waveguide – or preform
Reexamination Certificate
1999-05-25
2001-06-26
Vargot, Mathieu D. (Department: 1732)
Plastic and nonmetallic article shaping or treating: processes
Optical article shaping or treating
Optical fiber, waveguide, or preform
C264S573000, C264S040300, C422S131000, C425S149000
Reexamination Certificate
active
06251311
ABSTRACT:
BACKGROUND OF THE INVENTION
A. Field of the Invention
The present invention relates to optical fibers, and an improved process and apparatus for production of the same. More particularly, the present invention relates to optical fibers having good optical properties and improved apparatus and batch process for production of the same.
B. Description of the Related Art
In the production of Large Core Polymeric Optical Fibers (LCPOF), two processes are known for such production: (1) batch and (2) continuous. The present invention is described using the batch process that uses claddings to essentially provide a mold for the light transmitting core. During the batch process, the claddings are filled with highly purified monomer mixtures and placed inside a reactor where polymerization of the monomer mixture occurs. Claddings are usually made of materials which are rather expensive and at times difficult to handle. Therefore, there is a desire to reduce cladding costs through thinner cladding walls as well as using other cladding arrangements and cladding materials.
The present batch methods of production can cause imperfections at the core-clad interface when the core becomes separated from the cladding during and after polymerization. Furthermore, voids and bubbles may form in the light transmitting core during formation. Separation of the light transmitting core from the cladding as well as the formation of voids and bubbles reduce light transmission and are undesirable.
With reference to
FIG. 1
, in order to avoid voids and imperfections that may occur during the polymerization reaction the cladding
20
wall is made relatively thick in the prior art. The reason is that the polymerizing mass that becomes the core
22
exerts an inward force onto the interior surface of the cladding
20
—a pseudo-adhesion—during the reaction. Most monomer mixtures shrink extensively during polymerization, exerting a force inward onto the cladding
20
that they are attached to, in most cases a fluoropolymer tubing. The cladding is preferably made from fluoropolymers that inherently possess a lower refractive index. Such fluoropolymers offer many advantages such as chemical inertness, smooth (highly glossy) surface, high heat resistance and relatively low refractive indices among other attributes. Nonetheless, fluoropolymers are relatively expensive ($0.03 to 0.04/gr.), and, due to inward force exerted by the polymerizing mass, have had to be used in relatively thick wall thicknesses to retain shape (roundness). Substantial cost savings can be realized if the fluoropolymer claddings wall thickness can be extensively minimized (less than 0.1 mm) while retaining the other positive attributes. Nonetheless, fluoropolymer claddings with such thin walls, even when encased in a relatively thick manufacturing jacket, deform during the core manufacturing. The latter results from the pressure exerted inward during the polymerization of the monomer mixtures (shrinkage of the polymerizing mass).
If the force pulling inward is greater than the structural force of the cladding
20
or the force holding the cladding to the manufacturing jacket
24
, then the cladding
20
is separated from the manufacturing jacket
24
and deformed—the radial uniformity along the optic is thereafter compromised. This phenomenon can be noted as de-lamination of fluoropolymer cladding
20
away from the manufacturing jacket
24
, and in short “de-lamination”, see FIG.
1
.
Another cause of de-lamination is where a cladding arrangement is collapsed due to the external pressure experienced from the loading of claddings on top of each other as adversely encountered in some manufacturing operations. The pressure exerted from the upper claddings on the lower claddings force the lower claddings to deform, and when the upper claddings are lifted, the fluoropolymer cladding separates from the manufacturing jacket causing de-lamination.
A way to resolve the de-lamination problem is to introduce means to create a force inside the cladding, such as pressurizing the polymerizing mass inside the cladding. In addition, such pressurization is useful in reducing the number of voids and bubbles in the light transmitting core. However, there is a limit to how much pressure can be exerted onto the polymerizing mass due in part to the strength of the cladding material in which over pressurization results in bursts in, or other damage to, the cladding. Similarly, under pressurization may result in separation of the cladding from the manufacturing jacket.
The limits on the amount of pressure applied to the core, imposed by the strength of the cladding, are undesirable. The cladding strength can be improved by the use of a manufacturing jacket in which the cladding is surrounded by a jacket that is made from a stronger material than the cladding to bolster the cladding walls under higher pressures. However, the manufacturing jacket increases the cost of materials to manufacture the LCPOF and must be removed following formation of the light transmitting core. Thus, there is a need to create optics under relatively higher pressures where the optic core is made relatively free of bubbles and voids and the core-cladding interface is essentially defect free to maximize light transmission. Furthermore, it is desirable to reduce the manufacturing costs by conserving the amount of cladding material used and eliminating or reducing the need for manufacturing jackets.
SUMMARY OF THE PRESENT INVENTION
It is an object of the present invention to provide a light transmitting core which has improved light transmission properties.
It is a further object of the present invention to reduce the costs of the cladding and reduce or eliminate the need for a manufacturing jacket.
It is an advantage of the present invention to increase the absolute pressure exerted upon the polymerizing mass to reduce the number of voids and bubbles thereby improving the light transmitting properties.
It is a further advantage of the present invention to utilize relatively thin wall claddings to contain the pressurized polymerizing mass and without the need for a manufacturing jacket.
It is a feature of the present invention to provide an inner pressure upon the interior of the cladding containing the polymerizing mass and an outer pressure upon the exterior of the cladding in which the inner pressure is higher relative to the exterior pressure thereby creating a pressure differential.
The present invention is directed to an improved LCPOF with improved light transmitting properties in the light transmitting core and an improved batch process and reactor for pressuring the polymerizing mass to reduce the bubbles and voids in the light transmitting core thereby providing improved optical properties. The batch process of the present invention utilizes a cladding and polymerizing mass in a reactor in which an inner pressure is applied to the interior chamber of the cladding containing the polymerizing mass and an exterior pressure is applied to the outer surface of the cladding. The exterior pressure has a value less than the interior pressure resulting in a pressure differential between the interior and exterior pressures.
The pressure differential is determined relative to the wall thickness of the cladding and is a value less than that required to burst, or otherwise deform, the cladding wall, yet sufficiently high to prevent separation of the light transmitting core from the cladding. Thus, a relatively low pressure differential permits the use of a cladding having a correspondingly thin wall thickness and eliminates or reduces the need for a manufacturing jacket. Even a relatively small pressure differential when compared to the pressure values of the inner and outer pressures is desired given that pressure applied to the cladding wall reduces the incidents of separation of the cladding from the light transmitting core. The use of interior and exterior pressures reduces the manufacturing costs by reducing the amount of material needed to produce a thin walled cladding and by reducing or e
Dill Scott D.
Zarian James R.
Lumenyte International Corp.
Small Larkin, LLP
Vargot Mathieu D.
LandOfFree
Optical fibers and processes and apparatus for making the same does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Optical fibers and processes and apparatus for making the same, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Optical fibers and processes and apparatus for making the same will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2524979