On-chip pad conditioning for chemical mechanical polishing

Details On-chip pad conditioning for chemical mechanical polishing On-chip pad conditioning for chemical mechanical polishing

1999-08-03

2001-10-09

Potter, Roy (Department: 2822)

Semiconductor device manufacturing: process

Chemical etching

Combined with the removal of material by nonchemical means

C438S691000, C438S693000

Reexamination Certificate

active

06300248

ABSTRACT:

FIELD OF THE INVENTION
The present invention generally relates to a method for polishing pad conditioning in a chemical mechanical polishing process and more particularly, relates to a method for on-chip polishing pad conditioning in a chemical mechanical polishing process by incorporating built-in dummy patterns on a semiconductor wafer wherein the patterns have a thickness of at least 2,000 Å for supplementing localized conditioning of the polishing pad.
BACKGROUND OF THE INVENTION
Apparatus for polishing thin, flat semiconductor wafers is well-known in the art. Such apparatus normally includes a polishing head which carries a membrane for engaging and forcing a semiconductor wafer against a wetted polishing surface, such as a polishing pad. Either the pad, or the polishing head is rotated and oscillates the wafer over the polishing surface. The polishing head is forced downwardly onto the polishing surface by a pressurized air system or, similar arrangement. The downward force pressing the polishing head against the polishing surface can be adjusted as desired. The polishing head is typically mounted on an elongated pivoting carrier arm, which can move the pressure head between several operative positions. In one operative position, the carrier arm positions a wafer mounted on the pressure head in contact with the polishing pad. In order to remove the wafer from contact with the polishing surface, the carrier arm is first pivoted upwardly to lift the pressure head and wafer from the polishing surface. The carrier arm is then pivoted laterally to move the pressure head and wafer carried by the pressure head to an auxiliary wafer processing station. The auxiliary processing station may include, for example, a station for cleaning the wafer and/or polishing head; a wafer unload station; or, a wafer load station.
More recently, chemical-mechanical polishing (CMP) apparatus has been employed in combination with a pneumatically actuated polishing head. CMP apparatus is used primarily for polishing the front face or device side of a semiconductor wafer during the fabrication of semiconductor devices on the wafer. A wafer is “planarized” or smoothed one or more times during a fabrication process in order for the top surface of the wafer to be as flat as possible. A wafer is polished by being placed on a carrier and pressed face down onto a polishing pad covered with a slurry of colloidal silica or alumina in de-ionized water.
A schematic of a typical CMP apparatus is shown in
FIGS. 1A and 1B
. The apparatus
10
for chemical mechanical polishing consists of a rotating wafer holder
14
that holds the wafer
10
, the appropriate slurry
24
, and a polishing pad
12
which is normally mounted to a rotating table
26
by adhesive means. The polishing pad
12
is applied to the wafer surface
22
at a specific pressure. The chemical mechanical polishing method can be used to provide a planar surface on dielectric layers, on deep and shallow trenches that are filled with polysilicon or oxide, and on various metal films. CMP polishing results from a combination of chemical and mechanical effects. A possible mechanism for the CMP process involves the formation of a chemically altered layer at the surface of the material being polished. The layer is mechanically removed from the underlying bulk material. An altered layer is then regrown on the surface while the process is repeated again. For instance, in metal polishing, a metal oxide may be formed and removed repeatedly.
A polishing pad is typically constructed in two layers overlying a platen with the resilient layer as the outer layer of the pad. The layers are typically made of polyurethane and may include a filler for controlling the dimensional stability of the layers. The polishing pad is usually several times the diameter of a wafer and the wafer is kept off-center on the pad to prevent polishing a non-planar surface onto the wafer. The wafer is also rotated to prevent polishing a taper into the wafer. Although the axis of rotation of the wafer and the axis of rotation of the pad are not collinear, the axes must be parallel. Polishing heads of the type described above used in the CMP process are shown in U.S. Pat. Nos. 4,141,180 to Gill, Jr., et al.; U.S. Pat. No. 5,205,082 to Shendon et al; and, U.S. Pat. No. 5,643,061 to Jackson, et al. It is known in the art that uniformity in wafer polishing is a function of pressure, velocity and the concentration of chemicals. Edge exclusion is caused, in part, by a non-uniform pressure applied on a wafer. The problem is reduced somewhat through the use of a retaining ring which engages the polishing pad, as shown in the Shendon et al patent.
Referring now to
FIG. 1C
, wherein an improved CMP head, sometimes referred to as a Titan® head which differs from conventional CMP heads in two major respects is shown. First, the Titan® head employs a compliant wafer carrier and second, it utilizes a mechanical linkage (not shown) to constrain tilting of the head, thereby maintaining planarity relative to a polishing pad
12
, which in turn allows the head to achieve more uniform flatness of the wafer during polishing. The wafer
10
has one entire face thereof engaged by a flexible membrane
16
, which biases the opposite face of the wafer
10
into face-to-face engagement with the polishing pad
12
. The polishing head and/or pad
12
are moved relative to each other, in a motion to effect polishing of the wafer
10
. The polishing head includes an outer retaining ring
14
surrounding the membrane
16
, which also engages the polishing pad
12
and functions to hold the head in a steady, desired position during the polishing process. As shown in
FIG. 1C
, both the retaining ring
14
and the membrane
16
are urged downwardly toward the polishing pad
12
by a linear force indicated by the numeral
18
which is effected through a pneumatic system.
The polishing pad
12
is a consumable item used in a semiconductor wafer fabrication process. For instance, under normal wafer fab conditions, the polishing pad must be replaced after a usage of between 12 and 18 hours. Polishing pads may be hard, incompressible pads or soft pads. For oxide polishing, hard, incompressible and thus stiffer pads are generally used to achieve planarity. Softer pads are frequently used to achieve improved uniformity and smooth surfaces. The hard pads and the soft pads may also be combined in an arrangement of stacked pads for customized applications.
A problem frequently encountered in using polishing pads in a CMP process for oxide planarization is the rapid deterioration in polishing rates of the oxide with successive wafers. The cause for the deterioration has been shown to be due to an effect known as “pad glazing” wherein the surface of the polishing pads become smooth such that the pads can no longer hold slurry in-between the fibers. This has been found to be a physical phenomenon on the surface, and is not caused by any chemical reactions between the pad and the slurry.
To remedy the pad glazing effect, numerous techniques of pad conditioning or scrubbing have been proposed to regenerate and restore the pad surface and thereby, restoring the polishing rates of the pad. The pad conditioning techniques include the use of silicon carbide particles, diamond emery paper, blade or knife for scrapping the polishing pad surface. The goal of the conditioning process is to remove polishing debris from the pad surface, reopen the pores, and thus forms micro scratches in the surface of the pad for improved life time of the pad surface. The pad conditioning process can be carried out either during a polishing process, i.e., known as concurrent conditioning, or after a polishing process.
While the pad conditioning process improves pad consistency and its lifetime, conventional apparatus of a conditioning disk is frequently not effective in conditioning a pad surface. For instance, a conventional conditioning disk for use in pad conditioning is shown in
FIGS. 1A and 1B
. The conditioning disk
30
is formed by embedding o

Affiliated with

Also associated with

Rating

On-chip pad conditioning for chemical mechanical polishing does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with On-chip pad conditioning for chemical mechanical polishing, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and On-chip pad conditioning for chemical mechanical polishing will most certainly appreciate the feedback.

Rate now

Comments { 0 }

Profile ID: LFUS-PAI-O-2575353