Compositions – Durable finishes for textile materials – or processes of... – Oil or water repellent or soil resistant or retardant
Reexamination Certificate
2002-02-06
2003-09-09
Green, Anthony J. (Department: 1755)
Compositions
Durable finishes for textile materials, or processes of...
Oil or water repellent or soil resistant or retardant
C252S008610, C252S008810
Reexamination Certificate
active
06616856
ABSTRACT:
TECHNICAL FIELD
The present invention relates to compositions for use in finishing and protecting nylon fibers and to methods of manufacturing such compositions.
BACKGROUND OF THE INVENTION
Carpets today are commonly formed of polyamide fibers such as nylon that are woven into yarns and tufted. The tufted material is then colored with dyes and finished with softeners, fixing agents, stainblockers and fluorocarbon soil repellents. Until the middle 1980s, the primary carpet finishing process was the application of fluorocarbon polymer emulsions which imparted water and oil repellency. These fluorocarbon products were sprayed or foamed into the carpet fibers. At that time, however, nylon carpets were still susceptible to staining by natural and artificial acidic colorants commonly found in many foods and drinks such as in red wine, Kool Aid and coffee.
Due to the need to provide acid colorant stain protection in nylon carpet, a finishing technique was introduced to the carpet industry by DuPont under the name Stain Master in the middle 1980s. The Stain Master fit technique involves the application of sulfonated polymers known either as snytans, sulfonated novolacs, or sulfonated aromatic aldehyde condensation products (SAC) to carpet products. These colorless, polymeric, aromatic sulfonates are commonly referred to as “stainblockers” in the carpet industry. Stainblockers are generally water soluble anionic polymers with some being formulated with methacrylate polymers. Such polymeric salts are regularly described in articles of the American Association of Textile Chemists and Colorists (AATCC) magazine, the
Textile Chemist and Colorist
, an example of which is entitled Stain Resist Chemistry for Nylon 6 Carpet from the November 1989 issue, Volume 21, Number 11.
Currently, during manufacture, nylon carpets are conveyed onto continuous dye machines in which the stainblockers, for stain resistance, and fluorocarbons, for anti-soiling, are applied to the fabrics in two separate steps. Sulfonated stainblockers and fluorocarbons had not been capable of being applied in a single step since fluorocarbon emulsion repellents coalesce in the presence of stainblockers.
In order to minimize the need for equipment, manpower, and overhead as a result of implementing two separate finishing processes, efforts continued to consolidate the two finishing processes into one. To this end, U.S. Pat. No. 4,875,901 to Payet et. al. disclosed a single step method in which nylon fibers were imparted with stain resistance, and water and oil repellency by contacting the fiber with an aqueous solution of a stainblocker, a fluorocarbon, and a divalent metal salt. Although Payet et. al. does disclose a single step process, the process has not gained commercial acceptance, primarily due to the resultant carpet water and oil repellency being inconsistent and often below acceptable industry standards. This inconsistency results from the stainblocker's tendency to interfere with the fluorocarbon curing process, that process being a thermal reorientation of the fluorocarbon molecules.
When fluorocarbon emulsion products are mixed with stainblockers, the fluorocarbon emulsion destabilizes and a semi-solid mass forms. This is due to the fluorocarbon emulsion contacting the stainblocker. It is well known that emulsions are easily destabilized by the addition of salts. Essentially, the salts act as a coalescing agent causing an agglomeration of the emulsion. Since stainblockers are a form of salt, they destabilize the fluorocarbon emulsions as would a common salt. For instance, the addition of sodium chloride or sodium sulfate to a fluorocarbon emulsion results in the destabilization of the fluorocarbon emulsion and the formation of an unusable semi-solid mass.
Payet et. al. relies on the proposition that in a dilute aqueous solution the destabilizing effect should not occur, so that the stainblocker polymers and fluorocarbon polymer emulsions should give the same results in a one step application process as they do in a two step application process. Although this proposition applies to chemical combinations which fix or cure in aqueous solutions, such as stainblockers, it does not apply to chemical combinations which require heat for curing and which consequently cause the evaporation of water. For instance, in fluorocarbon polymer combinations which require heat for curing, the addition of salt adversely affects the fluorocarbon polymer performance. If a chemical combination includes one chemical requiring heat for curing, and that chemical combination is not compatible when mixed in concentrated form, poor performance will result even if the chemicals are compatible in dilute aqueous form. The rationale here is that as water evaporates from the dilute solution, the concentrations of the chemicals increase until they finally reach a level in which they are incompatible. In carpet products this occurs on the fibers and, though not visually observed, the adverse affect on the carpet can be measured by standard test methods. In a fluorocarbon/stainblocker polymer combination, it is always the performance of the fluorocarbon that is affected rather than that of the stainblocker. It is likely that these adverse effects result from the fluorocarbon having to be heat cured to give performance results, while stainblockers normally fix under aqueous conditions.
Improved stain resistance of carpets has remained an important but elusive industry objective as measurable by AATCC Test Method 175-1992. Water and oil repellency, however, has since the mid 1980s been dominated by the desired property of carpets to resist soiling, as measured by AATCC test methods 122-1989 and 123-1989, and the ability of a carpet to be cleaned, as measured by AATCC test method 171-1989. Just as in water and oil repellency, soil resistance (anti-soiling) and cleaning are achieved by the use of anionic and non-ionic fluorocarbon emulsions. They are both liquids dispersed in immiscible liquids in colloidal size liquid droplets. Therefore, these carpet finishes continue to be applied in a two-step process with stainblockers in order to avoid the formation of the before mentioned mass.
More recently it was discovered that when a naphthalene sulfonated salt is added to a combination of a stainblocker and at least one type of fluorocarbon-based repellant, the naphthalene sulfonated salt functions as a fluorocarbon anti-coalescing agent. As explained in U.S. Pat. No. 5,843,328, the resultant composition is stable for a lengthy period of time, forming a product that gives acceptable stain and soil resistance in nylon carpet fibers and yarns. The composition is produced by mixing the naphthalene sulfonated salt with at least one fluorocarbon-based repellant and then mixing the resulting combination with a stainblocker. Alternatively, the naphthalene, sulfonated salt is mixed with the stainblocker and then the resulting combination mixed with the fluorocarbon-based repellant(s). Either way the result is a chemical composition that provides both fluorocarbon-based repellency (either water and oil repellency, soiling or cleaning repellency, or a combination thereof) and stainblocker protection, without agglomeration of the fluorocarbon-based repellant(s). The naphthalene sulfonated salt effectively slows down the agglomeration process to allow for the curing of both the stainblocker and the fluorocarbon-based repellant.
Unfortunately, the stainblockers disclosed in U.S. Pat. No. 5,843,328 tend to yellow when exposed to light, ozone, and/or nitrogen oxide gases. This can become a problem on light shades of carpets. This yellowing problem on light shades of carpet caused by sulfonated stainblockers was earlier addressed in U.S. Pat. No. 4,937,123. That patent teaches that the use of polymethacrylic acid, copolymers of methacrylic acid and combinations thereof, all here defined as methacrylate type, impart to polyamide fibers improved stain resistance to acid colorants such as those found in food and drink products.
Methacrylate type stainblockers have advant
Pacifici Joseph A.
Sims Daniel G.
Donelson Baker
Green Anthony J.
Simco Products, Inc.
LandOfFree
Nylon fiber protective finishing compositions and methods of... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Nylon fiber protective finishing compositions and methods of..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Nylon fiber protective finishing compositions and methods of... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3061980