Metal treatment – Process of modifying or maintaining internal physical... – Processes of coating utilizing a reactive composition which...
Reexamination Certificate
2001-08-23
2003-02-25
Sheehan, John (Department: 1742)
Metal treatment
Process of modifying or maintaining internal physical...
Processes of coating utilizing a reactive composition which...
C148S283000, C106S014210, C252S187200, C252S387000, C252S182330
Reexamination Certificate
active
06524403
ABSTRACT:
BACKGROUND OF THE INVENTION
The automotive industry has for many years utilized zinc plated components. Chromating of zinc deposits is a common way of delaying the appearance of white corrosion products on these components in service. The two most common chromate finishes are transparent “blue” and “iridescent yellow” films (although black and green variations are also well known). More recently, zinc alloys have been introduced and these give improved resistance to the formation of white corrosion products when used in combination with chromating treatments. However, hexavalent chromium is a toxic and carcinogenic substance. This material can “leach” from chromated zinc deposits and cause damage to the environment and people who regularly handle chromated components. Because of this, there is a requirement to find a suitable alternative. Chromate treatments are an extremely cost effective and efficient way to improve the corrosion performance of zinc and zinc alloy coated components. Any suitable replacement would have to be cost effective, simple to use and be easy to effluent treat and maintain.
U.S. Pat. Nos. 5,380,374; 5,952,049; and 6,038,309 disclose the use of acidic solutions containing group IV metal compounds, including titanium, with oxyanions in the absence of fluoride ions for forming conversion coatings on aluminum and its alloys, magnesium and ferrous metals. U.S. Pat. Nos. 6,059,867; 5,951,747; 5,728,233; and 5,584,946 disclose the use of acidic solutions containing group IV metal compounds, including titanium, in conjunction with phosphate and related ions for forming conversion coatings on aluminum and its alloys. U.S. Pat. No. 6,206,982 discloses a method for forming conversion coatings on aluminum using rare earth elements such as cerium. These inventions are typically used to produce an adherent undercoat which will provide good adhesion to paint. The above inventions are generally not suitable for electroplated zinc or zinc alloy deposits where the cosmetic appearance and corrosion protection are particularly important.
There are relatively few examples of chromium free conversion coatings on zinc and its alloys. U.S. Pat. Nos. 5,938,861 and 5,743,971 disclose the use of solutions containing an oxidizing agent, silicate ions or silicon dioxide and a metal selected from the group Ti, Zr, Ce, Sr, V, W and Mo. The pH of the solutions disclosed in this invention are in the acid region (between pH 0.5-6.0). At this pH, silicate ions are not stable and tend to fall out of solution as silicic acid. Likewise, dispersions of silicon dioxide are not stable and tend to coagulate.
U.S. Pat. Nos. 6,217,674; 5,449,414; and 5,342,456 disclose the use of group IV metal compounds in water soluble organic polymer dispersions. These compositions are applied to metal articles by dip or spray techniques. Organic polymer coatings applied in this way tend to be uneven and for many commercial applications this is undesirable.
It is an object of the invention described herein to provide a “chrome free” process which is capable of producing blue or iridescent coatings on zinc and zinc alloy deposits which give excellent salt spray resistance. The process described is inexpensive, the waste solution is easily treated and the process is simple to operate and maintain.
SUMMARY OF THE INVENTION
We have discovered that attractive conversion coatings with good salt spray resistance can be obtained from aqueous acidic solutions comprising:
1. A source of titanium or titanate ions;
2. An oxidant selected from the group consisting of hydrogen peroxide, compounds other than hydrogen peroxide that dissociate in aqueous solution to form O
2−
, nitrates, and mixtures of the foregoing; and
3. A complexing agent selected from the group consisting of fluorides, complex fluorides, organic acids and mixtures of the foregoing.
It has surprisingly been found that the composition and process of this invention produces blue or iridescent coatings on zinc and zinc alloy deposits and provides the treated articles with enhanced corrosion protection.
DETAILED DESCRIPTION OF THE INVENTION
A process for producing conversion coatings on zinc and/or zinc alloy surfaces is proposed which comprises contacting such surfaces with a composition comprising:
a). a source of ions comprising titanium;
b). an oxidant, preferably selected from the group consisting of hydrogen peroxide, sodium persulfate, ammonium persulfate, nitrates and mixtures of the foregoing; and
c). a complexing agent for the ions comprising titanium, preferably selected from the group consisting of fluoride, complexed fluorides, organic acids and mixtures of the foregoing.
The foregoing composition is preferably aqueous and acidic.
The source of ions comprising titanium can be a source of titanium ions themselves, or it can be a source of complexed titanium ions such as titanates. Preferably the source of ions comprising titanium is selected from the group consisting of titanium trichloride, sodium hexafluorotitanate, potassium hexafluorotitanate, and mixtures of the foregoing. The concentration of titanium, as titanium, in the composition may range from 0.01 to 5 g/l but is preferably from 0.05 to 0.2 g/l.
The oxidant is preferably selected from the group consisting of hydrogen peroxide, sodium persulfate, ammonium persulfate, nitrates and mixtures of the foregoing. Most importantly the oxidant must be a compound that dissociates and supplies O
2−
in aqueous solution. Most preferably the oxidant is hydrogen peroxide. If nitrates are used, they are preferably selected from the group consisting of nitric acid, sodium nitrate, potassium nitrate, group II metal nitrates, titanium nitrate and mixtures of the foregoing. If nitrates are used, they are preferably present in the composition in an amount from 0.1 to 50 g/l, more preferably from 5 to 20 g/l. However, as noted the most preferable oxidizer is hydrogen peroxide preferably at concentrations from 0.1 to 20 g/l, more preferably from 0.5 to 4 g/l.
The composition also comprises complexing agents or anions (collectively “complexing agents”) which are sufficient to maintain the ions comprising titanium in solution over an extended period of time. Suitable complexing agents include fluorides, complexed fluorides, organic acids, amino acids and salts of the foregoing such as hydrofluoric acid, sodium fluoride, potassium fluoride, ammonium bifluoride, sodium or potassium bifluoride, fluoroboric acid, fluorosilicic acid, sodium or potassium fluoroborate, sodium or potassium fluorosilicate, oxalic acid, malonic acid, succinic acid, tartaric acid, citric acid, malic acid, maleic acid, gluconic acid, heptonic acid, glycine, aspartic acid, sodium or potassium or ammonium salts of the foregoing acids, and mixtures of the foregoing. When fluoride ions are used they are preferably present in the composition in an amount of from about 0.01 to 4.0 g/l and more preferably from about 0.1 to 0.5 g/l. When complex fluorides are used they are preferably present in an amount from about 0.1 to 40 g/l and more preferably from 1.0 to 15.0 g/l. Organic acids are preferably used at concentrations from about 0.1 to 10 g/l and amino acids are preferably used in the range of from 0.1 to 10 g/l. When combinations of the foregoing compounds are used then the concentrations of each in the combination may be adjusted accordingly. Most preferably, organic acid and/or amino acids are used in combination with fluorides or complexed fluorides. Most preferably, the composition does not contain silicates or silicon dioxide, since at the operating pH of the composition, the foregoing materials are not stable.
In addition to the foregoing ingredients, preferably Group II metal compounds (most preferably chlorides) are added to the composition. These additives have been found to further improve the cosmetic appearance and corrosion resistance of the resultant conversion coating. Most preferably these additives are selected from the group consisting of calcium chloride, strontium chloride, barium chloride and mixtures of the
Bartlett Ian
Long Ernest
Rowan Anthony
LandOfFree
Non-chrome passivation process for zinc and zinc alloys does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Non-chrome passivation process for zinc and zinc alloys, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Non-chrome passivation process for zinc and zinc alloys will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3142854