Synthetic resins or natural rubbers -- part of the class 520 ser – Synthetic resins – Processes of preparing a desired or intentional composition...
Reexamination Certificate
1997-10-21
2001-03-13
Yoon, Tae (Department: 1714)
Synthetic resins or natural rubbers -- part of the class 520 ser
Synthetic resins
Processes of preparing a desired or intentional composition...
C524S190000, C524S485000, C524S486000, C524S484000, C525S932000, C428S913000
Reexamination Certificate
active
06201045
ABSTRACT:
TECHNICAL FIELD
The present invention concerns a non-birefringence optical resin material which can be used as a material for various optical elements, that is, an optical resin material showing no substantial birefringence or showing only the birefringence to such an extent as giving no effect in view of practical use and a member for a liquid crystal device using the resin material.
BACKGROUND ART
In recent years, polymeric resins have been used more and more in place of existent glass materials, as usual optical components such as spectacle lenses or transparent plates, as well as material for optical components for opto-electronics, for example, optical components for laser equipment such as optical disc devices for recording sounds, video images and character information. This is because the optical material comprising the polymeric resin, that is, optical resin material, is light in weight, excellent in impact resistance and, further, excellent in fabricability and mass productivity due to easy applicability of molding techniques such as injection molding or extrusion molding, as compared with the glass optical material. Such characteristics are useful for various kinds of optical components as described above and are particularly useful in the case of using the optical resin material for various kinds of members constituting a liquid crystal device which is a main constituent element of a liquid crystal display. The liquid crystal display has been used generally as a display element in various kinds of electronic equipment and, along with generalization of the application use, further reduction in the weight and thickness has been demanded and also for the improvement of strength performance such as impact resistance and such demands can be satisfied by effectively taking advantage of the characteristics of the polymeric optical material.
As described above, the optical resin material has a possibility of providing excellent characteristics as optical components for which a wide variety of application uses for optical components have been expected. However, they are not actually utilized as expected. One of major reasons is that products obtained by applying the molding technique to the optical resin material show considerable birefringence, which may sometimes deteriorate their function as optical components.
Birefringence present in the polymeric resin material has been generally known together with the reasons thereof.
FIG. 1
is a view for briefly explaining this. As shown in the figure, a polymeric optical material after a molding step is generally in a state in which a plurality of units (monomers)
1
constituting the polymer chain are bonded in a sterically specific orienting direction. In most of the polymeric materials usually used as the optical material, each of the units
1
has an optical anisotropy regarding refractive Index. Namely, the refractive index npr with respect to a polarization phase component in a direction parallel with the orienting direction is different from the refractive index nvt with respect to a polarization phase component in a direction perpendicular to the orienting direction.
As is well known, the optical anisotropy can be expressed by a index ellipsoid. In
FIG. 1
, an ellipsoidal mark
2
attached to each bonded unit
1
is in accordance with such expression. For example, in the case of polymethyl methacrylate (PMMA), the refractive index for each unit
1
(methyl methacrylate) is relatively smaller in the orienting direction and relatively larger in a direction perpendicular to the orienting direction. Accordingly, an index ellipsoid
3
in view of a macroscale is elongate as shown in the figure. That is, npr<nvt in the case of polymethyl methacrylate. The difference between both of them: &Dgr;n=npr−nvt is referred to as a birefringence value. Table 1 shows birefringence values with respect to typical optical resin materials.
TABLE 1
Double Refraction Value of Polymeric
Resin Matrix Material
Birefringence value
Material
&Dgr;n = npr − nvt
Polystyrene
−0.100
Polyphenylene oxide
+0.210
Polycarbonate
+0.106
Polyvinyl chloride
+0.027
Polymethyl methacrylate
−0.0043
Polyethylene terephthalate
+0.105
Polyethylene
+0.044
For example, &Dgr;n=−0.0043 for polymethyl methacrylate shown in
FIG. 1
, and &Dgr;n=−0.100 for polystyrene. Further A n shows a positive value as &Dgr;n=+0.044 for polyethylene. Hereinafter, the birefringence due to orientation of a polymer Is referred to as orientational birefringence, and the direction of the index ellipsoid along a major axis is referred to as orientation birefringence direction. Further, when the sign for &Dgr;n is positive (&Dgr;n>0), it is expressed as “the sign of birefringence is positive”, while when the sign for &Dgr;n is negative (&Dgr;n<0), it is expressed as “sign for birefringence is negative”.
Such orientation birefringence particularly will cause a problem in an application where the polarization characteristic is important. An example is an optical component in a write/erase type opto-magnetic disc developed in recent years. That is, since a polarization beam is used for a reading beam or a writing beam in the write/erase type opto-magnetic disc, if a double refractive optical element (disc itself, lens or the like) is present in an optical path, it gives an undesired effect on the reading or writing accuracy.
Further, a liquid crystal device is mentioned in which birefringence of members used gives the most significant effect. As is well known, the liquid crystal device has a structure of controlling permission/inhibition of the light by rotating the plane of polarization light by a liquid crystal layer between a polarizer and an analyzer arranged as crossed nicols or parallel nicols. Accordingly, in a liquid display device, birefringence of each member constituting the device gives a significant problem, which hinders a generalized application of the optical resin material to the liquid crystal device.
For the orientation birefringence, various attempts have hitherto been made for eliminating the same, typical examples of which are as shown below.
(1) A method disclosed in the specification of U.S. Pat. No. 4,373,065; directed to obtain a non-birefringence optical resin material by blending two types of polymeric resins which have orientation birefringence with signs opposite to each other and which are compatible to each other completely.
(2) A method as disclosed in Japanese Patent Laid-Open Sho 61-19656; utilizing a method of mixing an aromatic polycarbonate and a specific styrenic copolymer at a ratio within a specified range and utilizing the thus obtained aromatic polycarbonic resin composition.
(3) A method as disclosed in Japanese patent Laid-Open Sho 62-240901; for obtaining a non-birefringence optical resin material comprising a mixture of a polymer mainly comprising aromatic vinyl monomeric units and polyphenylene ether, a block copolymer comprising polymeric portions of both of them or a mixture thereof.
(4) A method as disclosed in Japanese Patent Laid-Open Sho 61-108617 of random copolymerizing, graft polymerizing or block copolymerizing two or more monomers constituting positive and negative constituent units having a main polarity difference of not less than 50×10
−25
d by an absolute value.
(5) A method as disclosed in the Journal of “Optics”, vol. 20, No. 20, pages 80 (30th)-81 (31th) (issued February 1991); proposed by the present inventor for obtaining a non-birefringence optical resin material by copolymerizing a monomer mixture of methyl methacrylate (MMA) and trifluoroethyl methacrylate (3FMA) or a monomer mixture of methyl methacrylate (MMA) and benzyl methacrylate (BzMA). In summary, monomers having opposite signs for orientation birefringence as a basis for giving a polymer are mixed and copolymerized in this method.
(6) A method of molding so as not to cause orientation in the polymer; which is a method adopted based on experience
McDermott & Will & Emery
Yoon Tae
LandOfFree
Non-birefringence optical resin material, a production... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Non-birefringence optical resin material, a production..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Non-birefringence optical resin material, a production... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2458313