ABSTRACT:
BACKGROUND OF THE INVENTION
The invention relates to Niobium (Nb)-silicide based composite compositions. In particular, the invention relates to Nb-silicide based composite compositions with chemistries that permit the Nb-silicide based composite compositions to find applications in turbine components.
Turbines and their components (hereinafter “turbine components”), such as, but not limited to, aeronautical turbines, land-based, turbines, marine-based turbines, and the like, have typically been formed from nickel (Ni)-based materials, which are often referred to as Ni-based superalloys. Turbine components formed from these Ni-based superalloys exhibit desirable chemical and physical properties under the high temperature, high stress, and high-pressure conditions generally encountered during turbine operation. For example, turbine components, such as an airfoil, in modern jet engines can reach temperatures as high as about 1,150° C., which is about 85% of the melting temperatures (T
m
) of most Ni-based superalloys.
Because Ni-based superalloys have provided the level of performance desired in such applications, the development of such Ni-based superalloys has been widely explored. Consequently, the field has matured and few significant improvements have been realized in this area in recent years. In the meantime, efforts have been made to develop alternative turbine component materials. These alternate materials include niobium (Nb)-based refractory metal intermetallic composites (hereinafter “RMIC”s). Most RMICs have melting temperatures of about 1700° C. If RMICs can be used at about 80% of their melting temperatures, they will have potential use in applications in which the temperature exceeds the current service limit of Ni-based superalloys.
RMICs comprising at least niobium (Nb), silicon (Si), titanium (Ti), hafnium (Hf), chromium (Cr), and aluminum (Al) have been proposed for turbine component applications. These silicide-based RMICs exhibit a high temperature capability that exceeds that of current Ni-based superalloys. Exemplary silicide-based RMICs are set forth in U.S. Pat. No.5,932,033, to M. R. Jackson and B. P. Bewlay, entitled “Silicide Composite with Nb-Based Metallic Phase and Si-Modified Laves-Type Phase” and U.S. Pat. No. 5,942,055, to Jackson and Bewlay, entitled “Silicide Composite with Nb-Based Metallic Phase and Si-Modified Laves-Type Phase”.
Some known Nb-silicide based composites—including silicide-based RMJCs—possess adequate oxidation resistance characteristics for turbine applications. These materials have compositions within the following approximate ranges. 20-25 atomic percent titanium (Ti), 1-5 atomic percent hafnium (Hf), and 0-2 atomic percent tantalum (Ta), where the concentration ratio (Nb+Ta):(Ti+Hf) has a value of about 1.4; 12-21 atomic percent silicon (Si), 2-6 atomic percent germanium (Ge), and 2-5 atomic percent boron (B), where the sum of the Si, B, and Ge concentrations is in the range between 22 atomic percent and 25 atomic percent; 12-14 atomic percent chromium (Cr) and 0-4 atomic percent iron (Fe), where the sum of the Fe and Cr concentrations is between 12 atomic percent and 18 atomic percent; 0-4 atomic percent aluminum (Al); 0-3 atomic percent tin (Sn); and 0-3 atomic percent tungsten (W). Other known Nb-based silicide composites—including silicide-based RMIC materials—have adequate creep-rupture resistance for turbine component applications. These materials have compositions within the following approximate ranges: 16-20 atomic percent Ti, 1-5 atomic percent Hf, and 0-7 atomic percent Ta, where the concentration ratio (Nb+Ta):(Ti+Hf) has a value of about 2.25; 17-19 atomic percent Si, 0-6 atomic percent Ge, and 0-5 atomic percent B, where the sum of the Si, B, and Ge concentrations is in the range between 17 atomic percent and 21 atomic percent; 6-10 atomic percent Cr and 0-4 atomic percent Fe, where the sum of the Fe and Cr concentrations is in the range between 6 atomic percent and 12 atomic percent; 0-4 atomic percent Al; 0-3 atomic percent Sn; 0-3 atomic percent W; and 0-3 atomic percent Mo. In addition, other known Nb-silicide based composites—including silicide-based RMIC materials—have adequate fracture toughness for turbine component applications. These materials contain greater than or equal to about 30 volume percent of metallic phases present in such components.
Although the above Nb-silicide based composite alloys and Nb-silicide based RMIC materials possess beneficial mechanical and chemical properties, they do not adequately balance oxidation resistance properties with toughness and creep resistance properties. Thus, a single Nb-silicide based RMIC alloy material composition that can provide adequate creep, oxidation resistance, and toughness for turbine component applications is currently not available.
While the oxidation performance and creep-rupture resistance for turbine component applications of known RMICs are desirable, these materials and their properties may still be further improved for turbine component applications. For example, the chemistries and compositions of the RMIC material may be modified to enhance oxidation resistance for applications that subject the turbine component to high stresses at temperatures ranging from about 1300° F. to about 1700° F. (about 700° C. to about 925° C.) over extended periods of time.
Therefore, what is needed is a Nb-silicide based RMIC material having a composition, chemistry, and properties that are suitable for various applications such as, but not limited to, turbine components, in which high stresses at elevated temperatures are encountered over long periods of time.
SUMMARY OF THE INVENTION
Accordingly, one aspect of the present invention is to provide a turbine having at least one component formed from a niobium silicide refractory intermetallic composite comprising: between about 14 atomic percent and about 26 atomic percent titanium; between about 1 atomic percent and about 4 atomic percent hafnium; up to about 6 atomic percent tantalum; between about 12 atomic percent and about 22 atomic percent silicon; up to about 5 atomic percent germanium; up to about 4 atomic percent boron; between about 7 atomic percent and about 14 atomic percent chromium; up to about 3 atomic percent iron; up to about 2 atomic percent aluminum; between about 1 and about 3 atomic percent tin; up to about 2 atomic percent tungsten; up to about 2 atomic percent molybdenum; and a balance of niobium.
A second aspect of the present invention is to provide a niobium silicide refractory intermetallic composite adapted for use in a turbine component. The niobium silicide refractory intermetallic composite comprises: between about 14 atomic percent and about 26 atomic percent titanium; between about 1 atomic percent and about 4 atomic percent hafnium; up to about 6 atomic percent tantalum; between about 12 atomic percent and about 22 atomic percent silicon; up to about 5 atomic percent germanium; up to about 4 atomic percent boron; between about 7 atomic percent and about 14 atomic percent chromium; up to about 3 atomic percent iron; up to about 2 atomic percent aluminum; between about 1 and about 3 atomic percent tin; up to about 2 atomic percent tungsten; up to about 2 atomic percent molybdenum; and a balance of niobium, wherein a ratio of a sum of atomic percentages of niobium and tantalum present in the niobium silicide refractory intermetallic composite to a sum of atomic percentages of titanium and hafnium present in the niobium silicide refractory intermetallic composite has a value between about 1.4 and about 2.2 (i.e., 1.4<(Nb+Ta):(Ti+Hf)<2.2).
A third aspect of the present invention is to provide a turbine component formed from a niobium silicide refractory intermetallic composite, comprising: between about 14 atomic percent and about 26 atomic percent titanium; between about 1 atomic percent and about 4 atomic percent hafnium; up to about 6 atomic percent tantalum; between about 12 atomic percent and about 22 atomic percent silicon; up to ab
Bewlay Bernard Patrick
Jackson Melvin Robert
Zhao Ji-Cheng
General Electric Company
Ip Sikyin
Johnson Noreen C.
Santandrea Robert P.
LandOfFree
Niobium-silicide based composites resistant to low... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Niobium-silicide based composites resistant to low..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Niobium-silicide based composites resistant to low... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2847641