Specialized metallurgical processes – compositions for use therei – Compositions – Loose particulate mixture containing metal particles
Reexamination Certificate
2002-01-17
2003-10-21
Mai, Ngoclan (Department: 1742)
Specialized metallurgical processes, compositions for use therei
Compositions
Loose particulate mixture containing metal particles
C361S528000
Reexamination Certificate
active
06635100
ABSTRACT:
BACKGROUND OF THE INVENTION
1. Field of the Invention
This invention relates to a particle size and shape of a niobium powder, and to an anode for a solid electrolytic capacitor made therefrom.
2. Description of the Related Art
In recent years, niobium powder has been attracting an attention as an anode material for a solid electrolytic capacitor having a high electrostatic capacitance.
In the prior art, a niobium powder used for solid electrolytic capacitors has a mean primary particle diameter of 0.011-0.025 &mgr;m and a narrow particle size distribution. For example, in Japanese Patent Laid-Open Sho 64-73009, a method is disclosed for manufacturing high purity Ta or Nb powder for a solid electrolytic capacitor. In this method, Ta or Nb is converted to metal halide by halogen gas, and this metal halide is reduced by hydrogen gas to obtain a metallic powder at a reducing temperature of 800-1000° C. The amount of hydrogen gas used is 30-500 times that of Ta or Nb in terms of molar ratio. In the embodiments, only a primary particle diameter of 0.0109-0.249 &mgr;m (10.9-24.9 nm) is disclosed for the niobium particles obtained. If such superfine niobium particles are used for the anode of a solid electrolytic capacitor, niobium will be consumed in the anodic oxidation step in which an oxide film as dielectric is formed on niobium. In a certain portion of the niobium, all the niobium will be transformed into niobium oxide. Therefore, the effective electrode surface area decreases, and it becomes difficult to obtain a capacitor of super-high capacity.
In order to prevent this, Japanese Patent Laid-Open 2000-226607 proposes a tantalum or niobium powder wherein the mean particle diameter of primary particles is 50 nm to 150 nm (0.050-0.150 &mgr;m), the particle size distribution is a logarithmic normal distribution, and the geometric standard deviation thereof is 1.4 or less. In this technique, using a DC plasma CVD device, tantalum powder or niobium powder is manufactured by introducing a tantalum or niobium halide (general formula: TaX
5
or NbX
5
, where X is a halogen element) or a tantalum or niobium alkoxide (general formula: Ta(OR)
5
or Nb(OR)
5
where OR is an alkoxyl group) and hydrogen gas to a plasma arc through a second or a third nozzle of a multi-stage plasma torch. The tantalum or niobium halide is thereby reduced by hydrogen to metallic tantalum or niobium powder. With this technique, the niobium consumption in the anodic oxidation step is suppressed by an amount corresponding to the increase in the average particle diameter of primary particles. However, as a powder having a narrow particle size distribution is used, void in the porous body formed by sintering the niobium powder increases, and the packing density becomes smaller.
If a powder having a wide particle size distribution and a mean particle diameter of primary particles of 0.050-0.150 &mgr;m is used, the packing density of a porous body will become large. The void in the porous body then becomes small, penetration of the solid electrolyte into the void is poor, and the electrostatic capacitance falls.
In the niobium powder according to the related art, the mean particle diameter of primary particles is small, for example, less than 50 nm (0.050 &mgr;m) or 50-150 nm (0.050-0.150 &mgr;m). If such a fine niobium powder is sintered to form an anode, some niobium becomes oxide film and is consumed in the anodic oxidation step, and the amount of niobium which is not oxidized decreases. Therefore, the effective electrode surface area decreases, and a capacitor of super-high capacity cannot be obtained. That is, these fine particles are too small to be used for a sintered powder pellet.
SUMMARY OF THE INVENTION
This invention, which resolves the above-mentioned problem, aims to provide a niobium powder suitable for manufacturing an electrolytic capacitor having a high electrostatic capacitance and small dielectric loss tangent, and an anode for a solid electrolytic condenser using this niobium powder. From the applied voltage, the progression angle of the current in the dielectric may be expressed as (&pgr;/2)−&dgr;. The dielectric loss tangent is tan &dgr;, and both &dgr; and tan &dgr; are small values. As the magnitude of the dielectric loss is proportional to tan &dgr;, this value is important as a value representing characteristics of a dielectric substance.
This invention, which was conceived in order to solve the above-mentioned problems, relates to a niobium powder wherein, for primary particles, the average particle diameter is 0.10-2 &mgr;m, the geometric standard deviation of particle size distribution exceeds 1.4 and the degree of sphericity is 2 or less.
In this invention, a primary particle means a particle which is regarded as a single particle under SEM microscope observation and which is not agglomerated. The mean particle diameter is the 50% particle diameter of the number of particles. This particle diameter is expressed by the typical diameter of a particle. The geometric standard deviation (number basis) is a value obtained by dividing the value of the 50% particle diameter of the particle number shown by the typical particle diameter, by the value of the 15.87% particle diameter. Herein, the typical particle diameter is the projected circular equivalent diameter (diameter of a circle having the same area as the projected area of a particle), and is also referred to as the Heywood diameter.
The degree of sphericity of a particle can be found by using an image analysis device 1P-1000PC (Asahi Chemical Industry Co., Ltd.) to an image of the particles observed by an electron microscope.
Degree of sphericity=(diameter of circle equal to projected area of particle)/(diameter of smallest circle circumcribed around projected image of particle) (1)
The reason for the numerical limitations of this invention is as follows. When the mean particle diameter of a primary particle is less than 0.1 &mgr;m, a solid electrolytic capacitor of high electrostatic capacitance cannot be obtained. On the other hand, when the mean particle diameter exceeds 2 &mgr;m, the particle size is too large and sintering does not proceed well, so when compression of powder is carried out, a sintered powder pellet of high strength is not obtained.
The geometric standard deviation is an index which shows the width of the particle size distribution. When it exceeds 1.4, the packing density of powder is large, and void in the porous substance increases, which is desirable. It is required that the geometric standard deviation is greater than 1.4 and less than 2, and preferably greater than 1.5 and less than 2.
When the degree of sphericity exceeds 2, the amount of niobium consumed as an oxide film in the chemical processing step increases compared with the case when the degree of sphericity is two or less than 2.
This invention also provides an anode for electrolytic capacitors formed by sintering the above niobium powder. If a solid electrolytic capacitor is manufactured using a niobium powder having the above characteristics, there is little decrease of electrode surface, and a highly efficient capacitor having a super-high capacitance can be obtained.
REFERENCES:
patent: 4141719 (1979-02-01), Hakko
patent: 4954169 (1990-09-01), Behrens
patent: 5171379 (1992-12-01), Kumar et al.
patent: 5680685 (1997-10-01), Bischoff
patent: 6139593 (2000-10-01), Kono
patent: 6521013 (2003-02-01), Naito et al.
patent: 0 953 847 (1999-11-01), None
patent: 60 121207 (1985-06-01), None
patent: 01 073009 (1989-03-01), None
patent: A 64-73009 (1989-03-01), None
patent: 2000-226607 (2000-08-01), None
patent: 2000 226607 (2000-08-01), None
Kawatetsu Mining Co. Ltd.
Mai Ngoclan
LandOfFree
Niobium powder and anode for solid electrolyte capacitors... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Niobium powder and anode for solid electrolyte capacitors..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Niobium powder and anode for solid electrolyte capacitors... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3150796