Nickel powder dispersion, method of producing nickel power...

Specialized metallurgical processes – compositions for use therei – Processes – Producing or purifying free metal powder or producing or...

Reexamination Certificate

Rate now

  [ 0.00 ] – not rated yet Voters 0   Comments 0

Details

C075S343000

Reexamination Certificate

active

06620220

ABSTRACT:

FIELD OF THE INVENTION
This invention relates to an ultrafine nickel powder dispersion and, more particularly, to an ultrafine nickel powder dispersion for preparing an electrically conductive paste, for example, such a paste for forming internal electrodes of multilayer ceramic capacitors, to a process for preparing the ultrafine nickel powder dispersion, and also to a process for preparing a highly dispersible electrically conductive paste using the nickel powder dispersion.
PRIOR ART
Powders of precious metals such as silver, palladium, platinum, and gold, and also of base metals such as nickel, cobalt, iron, molybdenum, and tungsten have hitherto been used in forming electrically conductive paste as electronic material, especially as conductive paste for forming internal electrodes of multilayer ceramic capacitors. In general, a multilayer ceramic capacitor is made up of a plurality of dielectric ceramic layers and a plurality of metal layers that form internal electrodes laminated in an alternate arrangement, and two external electrodes formed at both ends of the two outermost dielectric ceramic layers for connection to the metal layers of the internal electrodes. The material to be used in forming the dielectric members is one consisting mainly of a material of high dielectric constant, such as barium titanate, strontium titanate, or yttrium titanate. For the metal to constitute the internal electrodes, powders of the above-mentioned precious and base metals have usually been used. More recently, weight has been placed on the base metal powders to meet the demand for less expensive electronic materials. In particular, the multilayer ceramic capacitors with electrodes of dielectric ceramic layers of nickel powder films are under active development.
The multilayer ceramic capacitors using electrodes of nickel powder coated films are commonly manufactured in the following way. First, dielectric powder of barium titanate or the like is mixed with an organic binder to form a suspension, and the suspension is spread to a sheet form by the doctor blade method to obtain dielectric green sheets. In the meantime nickel powder to form internal electrodes is mixed and dispersed with organic compounds such as organic solvent, plasticizer, and organic binder to form nickel powder paste. The paste is printed by screen printing onto the green sheets. The printed sheets are then dried, laminated, and compressed with other members, and the organic ingredients are removed by heat treatment. The multilayer structure is sintered at around or above 1300° C., and finally external electrodes are baked onto both outermost ends of the laminated dielectric ceramic layers, whereby a multilayer ceramic capacitor is obtained.
The multilayer ceramic capacitors are extensively used in cellular phones, personal computers, and other electronic articles. In recent years rapid progress has been made in the reduction of weight and size of the electronic components and in the improvement and expansion of their functions. To keep pace with the progress there has been growing demand for multilayer ceramic capacitors of smaller sizes and larger capacities. The trend calls for multilayer units of hundreds of layers each, with consequent reduction of the thickness of individual electrode layers and further lowering of resistance. Nowadays each electrode layer is as thin as from 1 to 2 &mgr;m, and even thinner layers will certainly be required in the future.
In the manufacture of multilayer ceramic capacitors, nickel powder is mixed with and dispersed in a paste-forming dispersant to form electrodes. At this stage, if coarse nickel particles are present or if the nickel particles during the course of mixing or dispersing aggregate to form secondary nickel particles larger in diameter than the thickness of each electrode layer that ranges from 1 to 2 &mgr;m, the resulting electrode layer surfaces will be uneven, with the consequence that the multi-layer ceramic capacitors thus obtained will be too susceptible to shortcircuiting for practical use. Moreover, in the stage of evaporating the organic ingredients from the nickel powder paste and in the subsequent stage of sintering, a volumetric change of the sintered product can take place because of the expansion or shrinkage of the metal powder. The dielectric material too can undergo a similar volumetric change as a result of the sintering. Thus simultaneous sintering of the two different materials, dielectric and nickel powder, causes volumetric changes of the two materials with expansion and shrinkage at different temperatures during the course of sintering. These volumetric changes present a problem of the fracture of laminated mono-lithic structure called delamination, in the form of cracking or separation of the laminated films. The phenomenon of delamination occurs remarkably when there are coarse nickel particles or excessively aggregated nickel particles as noted above.
As means for solving the delamination problem, various methods have heretofore been proposed. For example, Japanese Patent Application Kokai (Public Disclosure) No. 8-246001 teaches that the possibility of delamination is decreased by the use, as the material for electrodes of multilayer ceramic capacitors, of the ultrafine nickel powder produced by the vapor phase hydrogen reduction of nickel chloride vapor and which has a mean particle diameter between 0.1 and 1.0 &mgr;m and a tap density that satisfies conditions represented by a specific formula.
Problems That the Invention is to Solve
The above-mentioned technique of the prior art is effective to some extent in preventing delamination. However, nickel powder is not always fully dispersible when it is mixed and dispersed with a paste-forming dispersant. The nickel particles tend to aggregate, with the result that the increased proportion of coarse particles renders it difficult to decrease the thickness of internal electrodes and makes the electrode surface uneven, leading to shortcircuiting. In extreme cases these factors can combine to cause delamination. Thus there is room for improvement in the dispersibility of nickel particles in a dispersant for forming an electrically conductive paste of nickel powder.
It may be considered possible to provide a nickel powder dispersion prepared by dispersing nickel powder in water beforehand instead of adding nickel powder directly to a paste-forming dispersant. In practice, however, the degree of dispersion of nickel powder at the time of forming a nickel powder paste is far from satisfactory.
It is therefore an object of the present invention to provide a nickel powder which, when used together with a paste-forming dispersant to form an electrically conductive paste, exhibits excellent dispersibility and, when used in a multilayer ceramic capacitor, permits the prevention of shortcircuiting and delamination due to unevenness of electrode surfaces.
It is another object of the invention to provide a process for preparing an electrically conductive paste in which nickel powder is thoroughly and highly dispersed.
Means of Solving the Problems
After our intensive search for ways of realizing the above objects of the invention, it has now been found that a dispersion obtained by adding an organic solvent to a aqueous dispersion of ultrafine nickel powder exhibits very high dispersibility of the nickel powder when it is added to an electrically conductive paste-forming dispersant, and is suitable for applications as conductive paste, especially as a conductive paste for multilayer ceramic capacitors. The present invention is predicated upon this discovery.
In brief, the invention provides a nickel powder dispersion comprising an aqueous nickel powder dispersion composed of superfine nickel powder having a mean particle diameter of no more than one micrometer and an aqueous solvent, and an organic solvent added to the aqueous dispersion in such form that said organic solvent replaces at least a part of the aqueous solvent. A surface active agent may further be added to the dispersion.
The invention also

LandOfFree

Say what you really think

Search LandOfFree.com for the USA inventors and patents. Rate them and share your experience with other people.

Rating

Nickel powder dispersion, method of producing nickel power... does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Nickel powder dispersion, method of producing nickel power..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Nickel powder dispersion, method of producing nickel power... will most certainly appreciate the feedback.

Rate now

     

Profile ID: LFUS-PAI-O-3021403

  Search
All data on this website is collected from public sources. Our data reflects the most accurate information available at the time of publication.