Nickel catalyst

Details Nickel catalyst Nickel catalyst

2001-05-01

2003-02-25

Silverman, Stanley S. (Department: 1754)

Catalyst, solid sorbent, or support therefor: product or process

Catalyst or precursor therefor

Metal, metal oxide or metal hydroxide

C502S327000, C502S332000, C502S335000, C208S142000, C208S217000

Reexamination Certificate

active

06524994

ABSTRACT:

FIELD OF THE INVENTION
The invention is directed to a nickel catalyst, more in particular to a nickel catalyst mainly consisting of nickel, with very advantageous structural properties.
BACKGROUND OF THE INVENTION
Nickel catalysts have been used already for a long time in various catalytic applications, such as hydrogenation and desulfurization. Traditionally either supported nickel catalysts or so-called Raney nickel catalysts are used. The supported catalyst are generally based on a ceramic support, such as silica, alumina and the like, on the surface of which an amount of nickel is present. These amounts of nickel may vary widely, from as low as 5 wt. % up to amounts of more than 75 wt. %. Supported catalysts have the advantage that it is relatively easy to provide a suitable catalyst structure. By first structuring the support, before applying the active material, it is possible to maintain the structure of the support. This applies especially to catalysts having a not too high nickel loading. At loadings of over about 75 wt. %, it becomes increasingly difficult to provide a suitable catalyst structure, more in particular to provide a catalyst having a reasonably high nickel surface area in combination with large pores. This would, however, be highly desirable as catalysts having the combination of these properties are expected to be highly active and selective in various reactions. Furthermore, catalysts with such a high nickel content have a high capacity for sulfur uptake in desulfurisation systems and generally have a good sedimentation behaviour. This latter point is especially important in reactions that are carried out in the slurry phase, such as hydrogenations of fatty materials.
Quite often, highly loaded supported nickel catalysts have the disadvantage that at high temperatures during reduction, calcination or use the nickel sinters to large crystallites, thereby losing surface area.
An alternative for the supported nickel catalysts is Raney nickel. Raney nickel has a high nickel content, i.e. more than 90 wt. %, but the pore sizes of Raney nickel tend to be rather small, namely typically between 4.5 and 6.5 nm, and the total pore volume is typically about 0.15 ml/g.
When seeking to produce nickel catalysts with as high as possible nickel content, an obvious solution would be to prepare unsupported nickel catalysts, for example by precipitating nickel precursor from a suitable solution of a nickel salt. This does not result in a stable (i.e. sinter resistant) material that can be converted to a catalyst having a high nickel surface area. Even if the nickel precursor (e.g. nickel-carbonate) has a high BET surface area, after calcination and reduction the material has sintered to a dramatically low nickel surface area, which may be as low as about 1 m
2
/g.
Accordingly there is a need for nickel catalysts having a high nickel loading and a high nickel surface area, combined with good structural properties, i.e. wide pores and a high porosity (pore volume), which also have the advantages of good sedimentation and high sulfur capacity.
BRIEF SUMMARY OF THE INVENTION
The present invention is based on the surprising discovery that the use of only a small amount of a structural promoter in the preparation of high nickel content catalysts makes it possible to produce nickel catalysts having a high nickel loading, a good nickel surface area in combination with good sinter resistance and wide pores.
The invention is accordingly directed to a nickel catalyst comprising 0.1 to 12.5 wt. % of at least one structural promoter, selected from the group of oxides of metals and metalloids and combinations thereof, and 87.5 to 99.9 wt. % of nickel, calculated on the weight of nickel and the structural promoter together, the catalyst having an nickel surface area, as defined herein, of at least 10 m
2
/g catalyst and an average pore diameter, as defined herein, of 10 to 60 nm.
It has been found that already very small amounts of promoter improves the structure of the catalyst. High amounts still provide a stable, sinter resistant material, but result in a decrease in the pore size to lower levels. Furthermore, these high amounts result in decreased sedimentation properties and sulfur uptake capacity.
DETAILED DESCRIPTION OF THE INVENTION
The structural promoter can be any material that provides a binding, structure promoting effect on the catalyst. More in particular, oxides of metal and metalloids are suitable, such as silica, silica-alumina, alumina, zirconia, titania, magnesia or ceria. Preferred materials are alumina, silica and silica-alumina. In the case of alumina it is preferred to use amounts, calculated on the weight of nickel (metal) and alumina of not more than 6.35 wt. %. Higher amounts are not necessary and may lead to a decrease in pore size. Most preferred amounts for the structural promoter are up to 5 wt. %. These amounts provide the possibility of a very high nickel loading in a stable material, in combination with the very advantageous pore structure.
The structural promoter is included in the catalyst during the preparation thereof, for example by adding the structural promoter during or after the precipitation of nickel precursor, such as nickel carbonate. An especially suitable method comprises first precipitating the nickel precursor, ageing the precipitate and adding a solution or suspension of the (precursor) of the structural binder to the precipitate, optionally followed by further ageing. Subsequently the material is further treated to produce a catalyst, which may include drying, calcining, reducing and passivating. These steps are conventional in the preparation of nickel catalysts.
Suitable sources for the structural promoter that may be added during the preparation of the catalyst are clay, metasilicate, colloidal silica, waterglass and sililic acid ether.
The type of material used as (precursor for) the structural promoter depends on the required properties of the catalyst. In the first place the structural promoter may influence the acid-base properties of the catalyst. In this way it is possible to provide a catalyst having more acidic properties by using a clay binder as promoter. Such a catalyst may have a very good selectivity in the hydrogenation of unsaturated fatty nitrils to produce unsaturated fatty amines, without substantial hydrogenation of the unsaturation.
On the other hand it is also possible to provide a more alkaline catalyst, for example by using a silicate solution as precursor for the structural promoter. Such a catalyst has a better selectivity than Raney nickel towards primary amines in the hydrogenation of fatty nitrites.
The nickel surface area of the catalyst will generally be between 10 and 65 m
2
/g of catalyst. To determine the nickel surface area hydrogen chemisorption measurements are performed with a dynamic pulse method similar to that described and discussed by Wanke et.al. (Can. J. Chem. Eng. vol 59, June 1981, 357). From the hydrogen chemisorption the nickel surface area is calculated according to a method as described by Bartholomew et.al. (
Journal of Catal.
65 (1980) 390).
The BET surface area, as determined by single point adsorption using the BET equation (as e.g. described by G. Sandstede et.al.,
Chem. Ing. Tech.
32 (1960), 413), is in general at least 15 m
2
/g catalyst. This surface area will generally be up to about 100 m
2
/g .
An important aspect of the catalyst is the pore structure. The advantageous pore structure of the catalyst of the present invention is characterised by wide pores in combination with a good porosity. The average pore diameter of the catalyst is at least 10 nm, preferably between 10 and 60 nm. This average pore diameter is calculated from the pore volume by the formula PV*4000/SA, in which PV is the pore volume as defined underneath, and SA is the single point BET surface area. For example for silica containing materials, this is quite contrary to the usual pore size of 4 nm. At higher amounts of structural promoter, these typical values are found again. In this respect it is t

Affiliated with

Also associated with

Rating

Nickel catalyst does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Nickel catalyst, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Nickel catalyst will most certainly appreciate the feedback.

Rate now

Comments { 0 }

Profile ID: LFUS-PAI-O-3170196