Optical waveguides – Optical fiber waveguide with cladding
Reexamination Certificate
2000-05-16
2002-07-23
Palmer, Phan T. H. (Department: 2874)
Optical waveguides
Optical fiber waveguide with cladding
C385S124000, C385S127000
Reexamination Certificate
active
06424776
ABSTRACT:
BACKGROUND OF THE INVENTION
The present invention relates to a dispersion-shifted single-mode optical fiber suitable for being used in wavelength division multiplexed transmission systems having high data rates.
Single-mode fibers must have characteristics that correspond to the requirements both of cable-makers and of system designers: firstly they must have good “cablability”, i.e. putting the fiber in a cable must give rise to only very low additional attenuation; and secondly they must have large effective areas to avoid non-linear effects, and suitable values for the zero-dispersion wavelength &lgr;
0
.
The use of such fibers in wavelength division multiplexed transmission systems using RZ, NRZ, or soliton-type pulses involves further constraints, particularly with increasing number of transmitted channels, data rate per channel, and post-amplifier power, and with decreasing spacing between channels. It is preferable to have a fiber that has non-zero chromatic dispersion at the transmission wavelengths so as to avoid non-linear effects, and in particular four-wave mixing (FWM) in the presence of a plurality of channels. Non-zero dispersion-shifted fibers (NZ-DSFs) are therefore used that have zero chromatic dispersion wavelengths &lgr;
0
that lie outside the ranges of the channels of the multiplexes so as to avoid the problems caused by four-wave mixing.
In addition, the use of such fibers for wavelength division multiplexed systems involves looking for a shallow chromatic dispersion gradient so as to retain propagation characteristics that are similar for the various channels.
Numerous index profiles have been proposed for such dispersion-shifted single-mode optical fibers. The index profile is generally described as a function of the appearance of the curve representing the refractive index as a function of the radius of the fiber. Conventionally, distance r to the center of the fiber is plotted along the x-axis, and index, defined by its difference relative to the index of the cladding of the fiber, is plotted up the y-axis in relative value (&Dgr;n) or in percentage (&Dgr;n %=100×&Dgr;n
).
The index profile is thus said to be “stepped”, “trapezium-shaped” or “triangular” for curves representing the variation of refractive index as a function of radius that are respectively stepped, trapezium-shaped, or triangular.
The article entitled “Transmission characteristics of a coaxial optical fiber line”, Journal of Lightwave Technology, vol. 11 No. 11, November 1993, describes a reference profile of the “central trough” type.
One of the fiber profiles proposed in that article has a zero chromatic dispersion wavelength in the vicinity of 1450 nm with an effective area greater than 60 &mgr;m
2
. Those two characteristics make it possible to satisfy the requirements in terms of non-linear effects and of four-wave mixing. However, a fiber having such a profile cannot be used in high data rate telecommunications systems because it has bending losses that are very high, and in practice considerably higher than those required by all specifications.
Document EP-0 724 171 is also known, and it proposes a plurality of dispersion-shifted single-mode optical fiber profiles that can be used in high data rate telecommunications systems. Those fibers make it possible to convey a plurality of channels in the vicinity of 1550 nm while avoiding non-linear effects by means of an effective area that is greater than 60 &mgr;m
2
.
Unfortunately, because their zero chromatic dispersion wavelength lies in the vicinity of 1530 nm or of 1560 nm, those fibers have chromatic dispersion that is very low at the transmission wavelengths of the window situated around 1550 nm. As a result, the four-wave mixing phenomenon is not avoided in such fibers.
Finally, the article entitled “Maximum effective area for non-zero dispersion-shifted fiber” (OFC'98 —Feb. 22 to 27, 1998 —pp 303-304) describes a dispersion-shifted single-mode optical fiber having an effective area greater than 60 &mgr;m
2
, low losses, and a zero chromatic dispersion wavelength in the vicinity of 1490 nm. There too, at the transmission wavelengths, the chromatic dispersion is too low to avoid four-wave
SUMMARY OF THE INVENTION
An object of the present invention is thus to develop a dispersion-shifted optical fiber that is optimized for high data rates, i.e. that has a large effective area, low losses, and a zero chromatic dispersion wavelength that is distinct from 1550 nm, making it possible to avoid the four-wave mixing phenomenon.
To this end, the present invention provides a dispersion-shifted single-mode optical fiber having an effective area greater than or equal to 60 &mgr;m
2
;
characterized in that it has a zero chromatic dispersion wavelength &lgr;
0
lying in the range 1400 nm to 1480 nm, and bending losses of less than 0.05 dB at 1550 nm for a winding of 100 turns of the fiber around a radius of 30 mm.
The fiber of the invention is a dispersion-shifted single-mode fiber having low bending losses and a large effective area, as well as chromatic dispersion that, for the wavelengths situated in the transmission window around 1550 nm, is both low enough not to give rise to information losses during transmission, and also high enough to avoid the four-wave mixing phenomenon over the entire transmission window. In addition, the chromatic dispersion gradient of the fiber of the invention is shallow.
Advantageously, the fiber is single-mode in fiber.
For high data rate systems, it is also useful for the fiber to provide single-mode propagation of the channels of the multiplex. ITU-T G 650 gives a definition of the cutoff wavelength in cable. The theoretical cutoff wavelength of the fiber is generally greater by several hundred nanometers than the cutoff wavelength in cable. The propagation in an optical fiber can be single-mode even if the theoretical cutoff wavelength is greater than the wavelength of the signals used: beyond a distance of a few meters or a few tens of meters, which is short compared with the propagation distances in optical-fiber transmission systems, the secondary modes disappear because of attenuation that is too great. The propagation in the transmission system is then single-mode.
In a preferred embodiment of the invention, the wavelength &lgr;
0
for which chromatic dispersion is zero lies in the range 1450 nm to 1480 nm, and preferably in the vicinity of 1475 nm.
Advantageously, the fiber has chromatic dispersion lying, in absolute terms, in the range 1 ps
m.km to 6 ps
m.km for a wavelength of 1550 nm.
The fiber has a chromatic dispersion gradient lying, in absolute terms, in the range 0.045 ps
m
2
.km to 0.09 ps
m
2
.km, and preferably in the range 0.045 ps
m
2
.km to 0.075 ps
m
2
.km for wavelengths of 1550 nm. These values for the chromatic dispersion gradient guarantee, in the range in which the fiber is used, that the chromatic dispersion remains substantially constant. The fiber is thus suitable for use under wavelength division multiplexing, and has chromatic dispersion values that are substantially equal over the band of the multiplex.
Preferably, the attenuation of the fiber is less than or equal to 0.23 dB/km at 1550 nm. Such an attenuation value guarantees that transmission losses are limited.
In a first embodiment of the invention, the fiber has an index profile comprising a central portion of index n
1
less than the index n
S
of the cladding of the fiber, an inner ring of index n
2
greater than the index of the cladding and extending around said central portion, an outer ring of index n
4
greater than the index of the cladding and extending around said inner ring, and, between said inner ring and said outer ring, an annular portion of index n
3
less than or equal to the indices of said inner ring and of said outer ring.
In which case, the difference &Dgr;n
1
between the index of the central portion of the fiber and the index of the cladding preferably lies within a range of −3.8×10
−3
±10%.
The radius a
1
of the central portion of the fiber
de Montmorillon Louis-Anne
Nouchi Pascale
Rousseau Jean-Claude
Alcatel
Palmer Phan T. H.
Sughrue & Mion, PLLC
LandOfFree
Monomode optical fiber with optimized dispersion shift for... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Monomode optical fiber with optimized dispersion shift for..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Monomode optical fiber with optimized dispersion shift for... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2881978