ABSTRACT:
BACKGROUND OF THE INVENTION
The present invention relates to a monolithic ceramic gas diffuser for injecting gas into a molten metal bath, and more particularly relates to such a diffuser that includes a portion through which injection gas will preferentially flow.
When making metal and metal alloy products, it is often necessary to create a bath of molten metal that will later be cast into molds of various shapes and sizes. With certain specific alloys, such as aluminum alloys, the molten aluminum is highly sensitive to the presence of hydrogen gas, which tends to form voids in the cast product. Additionally, molten aluminum oxidizes freely when exposed to air, and the resultant aluminum oxide has a density very similar to the metal itself This results in aluminum oxide being suspended in the melt, causing “hard spots” upon solidification, an undesirable result.
In an attempt to prevent both problems, it is conventional to inject a “cleansing gas” such as argon, nitrogen, chlorine, or freon into the molten aluminum in the form of gas bubbles. The hydrogen in the molten aluminum is either absorbed or attaches to the cleansing gas bubbles, which rise to and exit from the surface of the molten aluminum. Additionally, any aluminum oxide suspended in the molten aluminum can be floated to the surface by the gas bubbles. This is a mechanical process, and is basically independent of the type of gas used.
FIG. 1
shows a holding box
1
that contains molten metal
2
therein. Gas injection nozzles or spargers
3
are located at various positions in communication with the molten metal to inject gas, supplied from a gas supply line
4
, into the molten metal.
FIG. 2
shows an example of an existing sparger that typically would be positioned in the floor of holding box
1
. The sparger
5
includes a highly permeable ceramic member
6
encased in a steel can
7
through an interposed refractory or mortar adhesive
8
. A gas supply pipe
9
supplies gas to the permeable ceramic member
6
to inject gas into the molten metal.
The problem with the sparger shown in
FIG. 2
is that it requires the presence of steel can
7
to encase the permeable ceramic member
6
to insure that gas bubbles are injected only through the end face of permeable ceramic member
6
into the molten metal. Consequently, the sparger shown in
FIG. 2
is relatively expensive to manufacture. Moreover, the sparger is susceptible to cracking at the interfaces between permeable ceramic member
6
, mortar
8
and steel can
7
, due to the differences in thermal expansion coefficient among the various materials. Still further, the permeable ceramic member
6
used in such conventional spargers have large pore size, generally greater than
30
microns in diameter, and thus the size of the gas bubbles injected into the molten metal is relatively large. It would be preferred to inject smaller gas bubbles as they would be more effective in removal of the hydrogen gas contained in the molten metal, thus requiring less gas volume to accomplish degassing of the molten metal.
FIG. 3
shows another example of a gas injection mechanism in the form of a generally cylindrical graphite lance
10
. The lance is immersed in the molten metal and gas is introduced through the relatively large opening
11
formed in the end of the lance. The problem with such graphite or other ceramic lances is similar to the problem associated with the sparger shown in
FIG. 2
, in that it is difficult to inject small gas bubbles into the molten metal using such a device. Moreover, graphite tends to oxidize and corrode, and is also rather fragile; thus it requires frequent replacement.
FIG. 4
shows an example of a rotary degasser developed by Blasch Precision Ceramics, Inc. The rotary degasser
12
includes an elongate shaft
13
having an axial bore
14
extending therethrough, and an impeller
15
integrated with one end of shaft
13
. The impeller has a plurality of blades
16
extending radially outwardly from the axis of shaft
13
, and gas ports
14
a
passing radially outwardly through the impeller. The rotary degasser is immersed in molten metal and rotated by a drive member (not shown) while gas is injected into the molten metal through ports
14
a
and a large opening
17
formed in the end face of impeller
15
. Rotation of the impeller facilitates mixing of the injected gas with the molten metal. The problem with this rotary degasser, however, is that the size of the gas bubbles introduced into the molten metal is still quite large, and thus relatively inefficient for degassing the molten metal.
It would be desirable to provide a gas diffuser that is (1) highly resistant to cracking due to thermal cycling and other factors encountered during molten metal manufacturing, (2) capable of injecting uniform, relatively small gas bubbles into a bath of molten metal, and (3) relatively easy and inexpensive to manufacture. The gas diffusers to date, however, have not been able to fulfill all of these requirements.
SUMMARY OF THE INVENTION
It is an object of the present invention to provide a gas diffuser that overcomes all the drawbacks associated with the prior art discussed above.
In accordance with a first object of the present invention, a monolithic, fired ceramic gas diffuser is provided, which includes a first portion, a second portion integrated with the first portion, and a bore passing through the second portion and communicating with the first portion for supplying injection gas to the first portion. At least the first portion has a network of interconnected pores that provide preferential gas flow (i.e., a path of least resistance) through the first portion to inject gas into the molten metal bath.
The gas diffuser of the present invention is highly resistant to cracking as a result of thermal cycling since it is produced as a monolithic ceramic body. There are no lamination interfaces of substantially dissimilar material, such as in the sparger shown in
FIG. 2
, that would invite cracking problems. Additionally, the network of interconnected pores in the first portion of the gas diffuser can be engineered quite easily to enable the injection of very uniform, small bubbles of gas into the molten metal. Still further, the gas diffuser of the present invention is relatively easy and inexpensive to manufacture, as it can be produced using conventionally available materials and conventionally recognized processing techniques, such as those disclosed in U.S. Pat. Nos. 4,246,209 and 4,569,920, the entireties of which are incorporated herein by reference.
In accordance with a preferred embodiment of the present invention, the gas flow characteristics of the first and second portions of the monolithic ceramic gas diffuser are controlled to provide preferential gas flow through the first portion of the diffuser. More preferably, the gas flow characteristics are controlled by varying the permeability and/or thickness (in the gas flow direction) of the first and second portions. It is most preferable that the permeability of the second portion is less than the permeability of the first portion, so that the first portion defines a so-called path of least resistance in the gas diffuser through which the injection gas is more likely to pass. Accordingly, the specific geometry of the gas diffuser can be selected so that the first portion thereof is located in a position that will provide the most efficient injection of gas into the molten metal.
It is another object of the present invention to provide a monolithic, fired ceramic rotary gas diffuser for injecting gas into a molten metal bath, which includes an elongate shaft having an axial bore passing therethrough and an impeller integrated with one end of the shaft. At least a portion of the impeller has a network of interconnected pores that provide preferential gas flow (i.e., a path of least resistance) from the bore through the impeller portion to inject gas into the molten metal bath. This embodiment of the present invention incorporates the inventive gas diffuser into a rotary shaft/impeller c
Larsen David A.
Rexford Donald G.
Webster, Jr. Earle R.
Blasch Precision Ceramics, Inc.
Burr & Brown
Bushey C. Scott
LandOfFree
Monolithic ceramic gas diffuser for injecting gas into a... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Monolithic ceramic gas diffuser for injecting gas into a..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Monolithic ceramic gas diffuser for injecting gas into a... will most certainly appreciate the feedback.