Mixed iron powder for powder metallurgy

Details Mixed iron powder for powder metallurgy Mixed iron powder for powder metallurgy

1995-07-24

1997-02-04

Wyszomierski, George

Specialized metallurgical processes, compositions for use therei

Compositions

Loose particulate mixture containing metal particles

75232, 75234, 75254, C22C 3812

Patent

active

055993770

ABSTRACT:
A mixed iron powder for powder metallurgy containing less than about 0.1 wt % of Mn, about 0.08 to 0.15 wt % of S, a total of about 0.05 to 0.70 wt % of one or more compounds selected from MoO.sub.3 and WO.sub.3, about 0.50 to 1.50 wt % of graphite powder, and the balance Fe and incidental impurities. The mixed iron powder can be manufactured by an atomizing process using water, and be used to manufacture a sintered steel having excellent machinability, strength and toughness without forming soot, even if sintered in a hydrogen-containing atmosphere.

REFERENCES:
patent: 4098608 (1978-07-01), Matty et al.
patent: 4859238 (1989-08-01), Weise et al.
patent: 5356453 (1994-10-01), Takata

Affiliated with

Also associated with

Rating

Mixed iron powder for powder metallurgy does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Mixed iron powder for powder metallurgy, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Mixed iron powder for powder metallurgy will most certainly appreciate the feedback.

Rate now

Comments { 0 }

Profile ID: LFUS-PAI-O-674682