Stock material or miscellaneous articles – Coated or structually defined flake – particle – cell – strand,... – Particulate matter
Reexamination Certificate
2001-11-20
2003-05-13
Acquah, Samuel A. (Department: 1711)
Stock material or miscellaneous articles
Coated or structually defined flake, particle, cell, strand,...
Particulate matter
C264S004100, C264S004300, C264S004330, C264S004400, C428S402210, C428S403000
Reexamination Certificate
active
06562460
ABSTRACT:
TECHNICAL FIELD
This invention relates to microencapsulated particles. In a more specific aspect, this invention relates to microencapsulated particles that are useful in electroluminescent applications. This invention also relates to a process for the microencapsulation of these particles.
This invention will be described in detail with specific reference to the microencapsulation of phosphor particles. However, this invention will be understood as applicable to the microencapsulation of other substance particles, such as pharmaceuticals, organic solvents, organic oils, pigments, dyes, epoxy resins, inorganic salts, etc.
BACKGROUND OF THE INVENTION
Microencapsulated particles are known in the prior art. Bayless et al. U.S. Pat. No. 3,674,704 (1972) discloses a process for manufacturing minute capsules, en masse, in a liquid manufacturing vehicle wherein the capsules contain water or aqueous solutions. This patent discloses a specific process for manufacturing minute capsules wherein the capsule wall material is poly (ethylene-vinyl acetate) that is hydrolyzed to a narrowly specified degree (38-50 percent hydrolyzed).
Bayless U.S. Pat. No. 4,107,071 (1978) discloses microcapsules having a capsule core material surrounded by a relatively impermeable, densified protective wall and also discloses a process of manufacturing such microcapsules.
General encapsulating processes which utilize a liquid-liquid phase separation to provide a capsule wall material which envelops the capsule core material to be encapsulated are disclosed in Miller et al. U.S. Pat. No. 3,155,590; Powell et al. U.S. Pat. No. 3,415,758; and Wagner et al. U.S. Pat. No. 3,748,277.
Other prior art references disclose the encapsulation of electroluminescent phosphors; for example, see Budd U.S. Pat. No. 5,968,698 (1999). Additionally, the prior art discloses the coating of luminescent powders with a coating which comprises silicon dioxide; see Opitz et al. U.S. Pat. No. 5,744,233(1998).
Phosphor particles are used in a variety of applications, such as flat panel displays and decorations, cathode ray tubes, fluorescent lighting fixtures, etc. Luminescence or light emission by phosphor particles may be stimulated by applications of heat (thermoluminescence), light (photoluminescence), high energy radiation (e.g., x-rays or e-beams) or electric fields (electroluminescence).
For various reasons, the prior art fails to provide microencapsulated particles having the desired properties of impermeability to moisture and extended release capabilities. Thus, there is a need in the industry for microencapsulated particles having significantly improved properties.
SUMMARY OF THE INVENTION
Briefly described, the present invention provides microencapsulated particles which have an increased resistance to the adverse effects of moisture and which are able to function over an extended period of time (i.e., extended release capabilities). The present invention also provides a process for the microencapsulation of these particles.
The above-described advantages of the microencapsulated particles of this invention are evident when compared to similar microencapsulated particles manufactured according to the prior art (that is, not manufactured according to the present invention).
As used in this application, the following terms have the indicated definitions:
“Impermeability to moisture”—the ability to prevent or substantially eliminate the intake of moisture and thereby avoid the adverse effects of moisture.
“Improved”—as compared to microencapsulated particles that are disclosed in the prior art and are not microencapsulated according to the present invention.
As will be seen in greater detail below, the microencapsulated particles of this invention have other characteristics that are either equivalent to, or significantly improved over, the corresponding characteristics of the prior art microencapsulated particles.
Accordingly, an object of this invention is to provide microencapsulated particles.
Another object of this invention is to provide microencapsulated particles having improved impermeability to moisture.
Another object of this invention is to provide microencapsulated particles having extended release capabilities.
Still another object of this invention is to provide microencapsulated phosphor particles.
Still another object of this invention is to provide microencapsulated phosphor particles having improved impermeability to moisture.
Still another object of this invention is to provide microencapsulated phosphor particles having extended release capabilities.
Still another object of this invention is to provide a process for the microencapsulation of particles.
Still another object of this invention is to provide a process for the microencapsulation of particles to produce microencapsulated particles having improved impermeability to moisture.
Still another object of this invention is to provide a process for the microencapsulation of particles to produce microencapsulated particles having extended release capabilities.
Yet still another object of this invention is to provide a process for the microencapsulation of phosphor particles.
Yet still another object of this invention is to provide a process for the microencapsulation of phosphor particles to produce microencapsulated phosphor particles having improved impermeability to moisture.
Yet still another object of this invention is to provide a process for the microencapsulation of phosphor particles to produce microencapsulated phosphor particles having extended release capabilities.
These and other objects, features and advantages of this invention will become apparent from the following detailed description.
BRIEF DESCRIPTION OF THE DRAWINGS
FIG.
1
FIG. 1
is a chart showing the effect of exposure (measured in hours) on brightness (measured in foot lamberts) of microencapsulated electroluminescent phosphors and electroluminescent phosphors which have not been microencapsulated.
With reference to
FIG. 1
, when tested in a humidity cabinet for 1,000 hours, lamps containing phosphors that have been microencapsulated according to this invention showed only 34% degradation, which is 60% less degradation than shown by electroluminescent lamps containing phosphors that have not been encapsulated.
In addition, when electroluminescent lights containing phosphors that have been microencapsulated according to this invention and incandescent lighting were tested as runway lights, the electroluminescent lamps produced no halos or glare and could be seen almost 3 times farther away than the incandescent lighting. This same result was observed under artic conditions.
FIG.
2
FIG. 2
is a graphical representation of the relation between capsule quality and percent hydrolysis as applied to poly (ethylene-vinyl acetate), partially hydrolyzed. For reasons not entirely understood, the change in quality with change of percent hydrolysis is quite pronounced and remarkable. At hydrolysis of less than about 38 percent, the separated phase prepared according to established liquid-liquid phase separation techniques is not adequately viscous to form useful capsule walls, and the walls which are formed are sticky and generally unmanageable in attempts to isolate the capsules. Capsules made using materials having less than 38 percent hydrolysis have a tendency to agglomerate during the microencapsulation process, because a lack of vinyl alcohol groups prevents adequate cross-linking across hydroxyl groups.
At hydrolysis of greater than about 55 percent, the separated phase is too viscous and exists as a semi-solid, stringy, precipitous phase. The change from “good” to “no-good” is abrupt and appears to be complete within a few percent.
At hydrolysis between 38 and 43 percent, quality capsules can be prepared with the quality improving as 43 percent hydrolysis is approached.
Between 43 and 53 percent hydrolysis, the capsule quality is excellent for this invention, and the capsules are particularly suited for containing phosphors, polar liquids and other substance particles for extended per
Acquah Samuel A.
Baker, Donelson Bearman & Caldwell
Encap Technologies, LLC
LandOfFree
Microencapsulated particles and process for manufacturing same does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Microencapsulated particles and process for manufacturing same, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Microencapsulated particles and process for manufacturing same will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3086788