Methods for preparing polyvinylidene fluoride composites

Compositions – Electrically conductive or emissive compositions – Elemental carbon containing

Reexamination Certificate

Rate now

  [ 0.00 ] – not rated yet Voters 0   Comments 0

Details

C264S105000, C524S457000, C524S496000

Reexamination Certificate

active

06746627

ABSTRACT:

FIELD OF THE INVENTION
The invention relates generally to electrically conductive polyvinylidene fluoride composites containing carbon nanotubes, and the methods for preparing them.
BACKGROUND OF THE INVENTION
Polyvinylidene Fluoride
Plastics are synthetic polymers which have a wide range of properties that make them useful for a variety of applications ranging from packaging and building/construction to transportation; consumer and institutional products; furniture and furnishings; adhesives, inks and coatings and others. In general, plastics are valued for their toughness, durability, ease of fabrication into complex shapes and their electrical insulation qualities.
One such widely used plastic is polyvinylidene fluoride (—H
2
C═CF
2
—), (“PVDF”), which is the homopolymer of 1,1-difluoroethylene, and is available in molecular weights between 60,000 and 534,000. This structure, which contains alternating —CH
2
— and —CF
2
— groups along the polymer backbone, gives the PVDF material polarity that contributes to its unusual chemical and insulation properties.
PVDF is a semicrystalline engineered thermoplastic whose benefits include chemical and thermal stability along with melt processibility and selective solubility. PVDF offers low permeability to gases and liquids, low flame and smoke characteristics, abrasion resistance, weathering resistance, as well as resistance to creep and other beneficial characteristics. As a result of its attractive properties, PVDF is a common item of commerce and has a wide variety of applications (e.g., cable jacketing, insulation for wires and in chemical tanks and other equipments).
In addition to forming a homopolymer, PVDF also form co-polymers with other polymer and monomer families, most commonly with the co-monomers hexafluoropropylene (HFP), chlorotrifluoroethylene (CTFE), and tetrafluoroethylene (TFE), as well as terpolymers and olefins. The properties of the copolymers is strongly dependent on the type and fraction of the co-monomers as well as the method of polymerization. For example, HFP makes a homogenous copolymer with PVDF. On the other hand, the PVDF copolymer phase segregates if the other monomer is not fluorinated.
Conductive Plastics
Recently, demand and applications for electrically conductive plastics have grown. In these uses, one seeks to exploit the unique properties of plastics, often as an alternative to metals. For example, electrically conductive polymeric materials are desirable for many applications including the dissipation of electrostatic charge from electrical parts, electrostatic spray painting and the shielding of electrical components to prevent transmission of electromagnetic waves.
Conductivity (i.e., the ability of material to conduct or transmit heat or electricity) in plastics is typically measured in terms of bulk resistivity (i.e., volume resistivity). Bulk resistivity, which is the inverse of conductivity, is defined as the electrical resistance per unit length of a substance with uniform cross section as measured in ohm-cm. Thus, in this manner, the electrical conductivity of a substance is determined by measuring the electrical resistance of the substance.
Electrically conductive plastics can be divided into several categories according to their use. For example, high level of resistivity (i.e., low level of conductivity) ranging from approximately 10
4
to 10
8
ohm/cm generally confer protection against electrostatic discharge (“ESD”) and is referred to as the ESD shielding level of conductivity. This is also the level of conductivity needed for electrostatic painting. The next level of resistivity, which ranges from approximately 10
4
ohm/cm and lower, protects components contained within such plastic against electromagnetic interference (“EMI”) as well as prevents the emission of interfering radiation, and is referred to as the EMI shielding level of conductivity. In order for a plastic article to be used as a conductive element like a current collector or separator plate in an electrochemical cell, resistivity less than 10
2
ohm/cm is required.
The primary method of increasing the electrical conductivity of plastics have been to fill them with conductive additives such as metallic powders, metallic fibers, ionic conductive polymers, intrinsically conductive polymeric powder, e.g., polypyrrole, carbon fibers or carbon black. However, each of these approaches has some shortcomings. Metallic fiber and powder enhanced plastics have poor corrosion resistance and insufficient mechanical strength. Further, their density makes high weight loadings necessary. Thus, their use is frequently impractical.
When polyacrylonitrile (“PAN”) or pitch-based carbon fiber is added to create conductive polymers, the high filler content necessary to achieve conductivity results in the deterioration of the characteristics specific to the original resin. If a final product with a complicated shape is formed by injection molding, uneven filler distribution and fiber orientation tends to occur due to the relatively large size of the fibers, which results in non-uniform electrical conductivity.
Principally because of these factors and cost, carbon black has become the additive of choice for many applications. The use of carbon black, however, also has a number of significant drawbacks. First, the quantities of carbon black needed to achieve electrical conductivity in the polymer or plastic are relatively high, i.e. 10-60%. These relatively high loadings lead to degradation in the mechanical properties of the polymers. Specifically, low temperature impact resistance (i.e., a measure of toughness) is often compromised, especially in thermoplastics. Barrier properties also suffer. Sloughing of carbon from the surface of the materials is often experienced. This is particularly undesirable in many electronic applications. Similarly, outgassing during heating may be observed. This adversely affects the surface finish. Even in the absence of outgassing, high loadings of carbon black may render the surface of conductive plastic parts unsuitable for automotive use.
Taken as a whole, these drawbacks limit carbon black filled conductive polymers to the low end of the conductivity spectrum. For EMI shielding or higher levels of conductivity, the designer generally resorts to metallic fillers with all their attendant shortcomings or to metal construction or even machined graphite.
What ultimately limits the amount of carbon black that can be put into plastic is the ability to form the part for which the plastic is desired for. Depending on the plastic, the carbon black, and the specific part for which the plastic is being made, it becomes impossible to form a plastic article with 20-60 wt % carbon black, even if the physical properties are not critical.
Carbon Fibrils
Carbon fibrils have been used in place of carbon black in a number of polymer applications. Carbon fibrils, referred to alternatively as nanotubes, whiskers, buckytubes, etc., are vermicular carbon deposits having diameters less than 1.0&mgr; and usually less than 0.2&mgr;. They exist in a variety of forms and have been prepared through the catalytic decomposition of various carbon-containing gases at metal surfaces. Such fibers provide significant surface area when incorporated into a structure because of their size and shape. They can be made with high purity and uniformity.
It has been recognized that the addition of carbon fibrils to polymers in quantities less than that of carbon black can be used to produce conductive end products. For example, U.S. Pat. No. 5,445,327, hereby incorporated by reference, to Creehan disclosed a process for preparing composites by introducing matrix material, such as thermoplastic resins, and one or more fillers, such as carbon fibers or carbon fibrils, into a stirred ball mill. Additionally, U.S. Ser. No. 08/420,330, entitled “Fibril-Filled Elastomer Compositions,” also incorporated by reference, disclosed composites comprising carbon fibrils and an elastomeric matrix, and methods of preparing such.
It has also been recognized

LandOfFree

Say what you really think

Search LandOfFree.com for the USA inventors and patents. Rate them and share your experience with other people.

Rating

Methods for preparing polyvinylidene fluoride composites does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Methods for preparing polyvinylidene fluoride composites, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Methods for preparing polyvinylidene fluoride composites will most certainly appreciate the feedback.

Rate now

     

Profile ID: LFUS-PAI-O-3359907

  Search
All data on this website is collected from public sources. Our data reflects the most accurate information available at the time of publication.