ABSTRACT:
FIELD OF THE INVENTION
The present invention relates generally to synthetic filaments and to their processes and systems for manufacture. More specifically, the present invention relates to processes and systems for making melt-spun, synthetic polymeric yarns of bulked continuous filaments (BCF), especially carpet yarns comprised of nylon BCF.
BACKGROUND AND SUMMARY OF THE INVENTION
I. Definitions
As used herein, certain terms have the following meanings:
“Filament” or “filaments” mean fibrous strands of extreme or indefinite length. In contrast, “staple fibers” mean fibrous strands of definite and short lengths.
“Yarn” means a collection of numerous filaments which may or may not be entangled, twisted or laid together.
“One-step” means a process for making yarn whereby no intermediate winding of the yarn occurs between the spinning, drawing and texturing processes.
“Texturing” means any operation on filaments which results in crimping, looping or otherwise modifying such filaments to increase cover, resilience, bulk or to provide a different surface texture or hand. A “bulked continuous filament” is therefore a “filament” which has been subjected to one or more “texturing” operation(s).
“Morphologically stable” means a bulked continuous filament such that yarns of such filaments exhibit a skein shrinkage of less than 0.50 inch, and more preferably about 0.25 inch or less.
II. Background of the Invention
One-step processes for manufacturing melt-spun polymeric yarns of bulked continuous filaments (BCF) are known as evidenced by the following U.S. Pat. Nos. 5,804,115; 5,487,860; 4,096,226; 4,522,774; and 3,781,949 (the entire content of each cited U.S. Patent being incorporated expressly hereinto by reference). In general, such processes involve the continuous sequential operations (i.e., without any intermediate winding of the yarn) of spinning, drawing and texturing. The resulting BCF yarn is thereafter wound on a package either sold as is or subjected to further processing (e.g., coloration, entangling with other yarns, fabric formation, and the like).
Conventional one-step BCF yarn production techniques typically involve the melt-spinning of multiple polymeric filament streams which, when cooled form the precursor (or undrawn) filaments of the later BCF yarn. These undrawn filaments are then typically immediately directed to separated pairs of godet rolls (sometimes referred to as “duos” in art parlance) operating at different rotational speeds. The BCF yarn will therefore be drawn between such duos at a desired draw ratio dependent on the duo speed differential, yarn temperature, yarn speed and the like. The duos are typically heated to the same temperature in order to elevate the filament temperature prior to texturing.
The thus drawn and heated yarn is then subjected to a texturing operation, usually accomplished by feeding the drawn continuous filament yarn into a fluid jet texturing unit at a rate faster than the rate at which the textured yarn is drawn off and subjecting the yarn in the unit to a turbulent region of a fluid jet, usually at elevated temperature (e.g., a so-called fluid jet texturing method). The resulting textured continuous filament yarn exhibits increased bulk as compared to the non-textured yarn being fed into the texturing unit to achieve the BCF yarn which may then be wound up to form a yarn package.
Recently, in commonly owned U.S. Pat. No. 6,447,703 to Waddington et al Jun. 22, 2000 (the entire content of which is expressly incorporated hereinto by reference), there are disclosed methods and systems for making melt-spun, drawn and textured BCF yarns, wherein prior to texturing the yarn is subjected to differential temperature condition. Most preferably, such differential temperature condition is accomplished using the duo rolls employed in drawing the BCF, such that one of the rolls is maintained at a greater temperature as compared to the other of the rolls. The morphology of the BCF yarn can thus be variably controlled.
III. Summary of the Invention
Broadly, the present invention is embodied in morphologically stable BCF yarns, and the methods and systems for making such BCF yarns. More specifically, according to the present invention, the BCF yarn is melt-spun, drawn and textured, wherein the yarn texturizing includes operating a fluid jet texturizer at a sufficiently low fluid jet velocity and a sufficiently high fluid jet temperature to obtain a yarn skein shrinkage of less than about 0.50 inch, more preferably less than about 0.25 inch. Especially preferred embodiments of the present invention include filaments formed of nylon-6 having an alpha-crystalline content of at least about 45%, more preferably between about 45% to about 55%.
These and other aspects and advantages will become more apparent after careful consideration is given to the following detailed description of the preferred exemplary embodiments thereof.
REFERENCES:
patent: 6113825 (2000-09-01), Chuah
patent: 6447703 (2002-09-01), Waddington et al.
patent: 6635345 (2003-10-01), Ilg et al.
Ilg Otto M.
Sferrazza Randall A.
LandOfFree
Methods for making morphologically stable bulked continuous... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Methods for making morphologically stable bulked continuous..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Methods for making morphologically stable bulked continuous... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3268849