Plastic and nonmetallic article shaping or treating: processes – With step of cooling to a temperature of zero degrees c. or...
Reexamination Certificate
2001-06-22
2004-12-28
Vargot, Mathieu D. (Department: 1732)
Plastic and nonmetallic article shaping or treating: processes
With step of cooling to a temperature of zero degrees c. or...
C264S297800, C264S334000
Reexamination Certificate
active
06835336
ABSTRACT:
FIELD OF THE INVENTION
The present invention relates to biopolymer sponge tubes and the use thereof in surgery.
BACKGROUND OF THE INVENTION
Surgical staple guns are widely used in the haemostasis and subsequent sealing of tissue following surgical procedures. For example, in the sealing of tissue following lung volume reductions for patients with emphysema.
Typically, the linear surgical staplers have two separate barrels of differing dimensions, namely a staple cartridge and an anvil, which close together during the stapling. The Burdorff, U.S. Pat. No. 5,697,543 issued Dec. 16, 1997, the Bittner et al., U.S. Pat. No. 5,673,842 issued Oct. 7, 1997, and the Schulze et al., U.S. Pat. No. 5,065,929 issued Nov. 19, 1991, each of which are incorporated herein by reference, provide examples of surgical staplers.
Often surgical staplers are indicated for use with a buttressing material, such as bovine pericardium, which surgeons use to reinforce staple lines and prevent leaks. According to current surgical procedure, the pericardium is wrapped around the barrels of the stapler prior to use. In use, the two barrels of the staple gun are placed on either side of the tissue that requires sealing. The stapling action brings together the two barrels with the pericardium, which is stapled into position at the appropriate site. The pericardium then acts as a seal to prevent exudate/air leakage.
The use of bovine pericardium in the above stapling procedure suffers from the drawbacks of possible antigenicity of the bovine pericardium, and lack of control over the precise shape, configuration and thickness of the bovine pericardium.
It is known to use pledgets of material to achieve hemostasis along a staple line as shown in the Trumbell et al., U.S. Pat. No. 5,263,629, issued Nov. 23, 1998 and incorporated herein be reference. Trumbell et al. provide rectangular pledgets of a fabric-like material, preferably having hemostatic properties, between the anvil and the staple cartridge in a surgical stapler. Staples are fired through both the pledget and the tissue to adhere the pledget to the tissue along the staple line. Placement and retention of the pledgets in the stapler can be quite tricky.
It is known to provide collagen tubes by the extrusion of a collagen gel into a coagulating bath. Such tubes have been used in micro-surgery, and for vascular prostheses. Implanted collagen films and/or collagen sponges have been suggested as slow-release matrices for therapeutic agents. The properties and applications of collagen biomaterials have been reviewed by A. Huc in Journal of American Leather Chemists Association, Vol. 80, pages 195-212 (1985).
U.S. Pat. No. 3,157,524 describes forming porous collagen tubes by freezing an aqueous collagen slurry in a tubular mold, followed by solvent drying in an anhydrous isopropanol bath.
Alternatively, the slurry may be frozen onto the outside of a tube through which a suitable refrigerant is passed, followed by solvent drying. The sponges are said to control bleeding in surgery through the application of pressure and coagulating material such as thrombin. No specific applications are disclosed.
It has now been found that biopolymer sponge tubes are highly suitable for replacing bovine pericardium and rectangular pledgets in the surgical stapling procedure described above.
SUMMARY OF THE INVENTION
Accordingly, the present invention provides a biopolymer sponge tube closed at one end.
The biopolymer sponge tube is closed at one end to enable it to be fitted over a barrel of a staple gun without sliding too far along the barrel.
The present invention also provides a surgical stapler comprising a staple cartridge and an anvil, and having a biopolymer sponge tube (which need not be closed at one end) fitted over the staple cartridge and/or over the anvil. Preferably, biopolymer sponge tubes are fitted over each of the staple cartridge and the anvil. Preferably, the biopolymer sponge tube or tubes are closed at one end.
The present invention further provides the use of a biopolymer sponge tube for the preparation of a surgical stapler as above for use in surgery.
The biopolymer used to make the sponge tubes may be any biocompatible and bioabsorbable polymer. Preferably, the biopolymer is selected from the group consisting of structural proteins, cellulose derivatives (including oxidised regenerated cellulose), starch derivatives, chitin, chitosan, glycosaminoglycans, and mixtures thereof. Preferred structural proteins include gelatin, all collagen types, keratin, laminin, fibrin or fibronectin. The phrase “all collagen types” encompasses type I and type II collagen, atelocollagen and other modified collagens. Suitable cellulose derivatives include carboxymethyl cellulose and hydroxyethyl cellulose, in addition to oxidised regenerated cellulose. Suitable alginates include sodium alginate, calcium alginate and mixtures thereof. Suitable glycosaminoglycans include hyaluronic acid, chondroitin sulphate, heparin and heparan sulphate.
The biopolymer sponge tube may be reinforced by a biopolymer matrix, such as a Vicryl (registered trade mark) polylactide/polyglycolide mesh. However, preferably, the biopolymer sponge is not reinforced.
Preferably, the biopolymer sponge tube consists essentially of one of more collagen types. The collagen may be chemically cross-linked to modify its physical properties and rate of resorption in vivo. Collagen is the preferred biopolymer because of its easy availability, low cost, low antigenicity, and well-understood properties, which enable the collagen sponge to be prepared with controlled physical and biological behaviour.
The biopolymer sponge tube is preferably sterile. Preferably, the biopolymer sponge tube comprises less than 10% by weight of water to enable it to be stored indefinitely without decomposition. The biopolymer sponge tube preferably further comprises a therapeutic compound selected from the group consisting of antiseptics, such as chlorhexidine, antibiotics such as streptomycin, analgesics such as ibuprofen, steroids, cell growth factors and wound healing factors. Preferably, the therapeutic compound is present in amount of 0.01% to 2% by weight, based on the weight of the biopolymer sponge tube.
Preferably, the biopolymer sponge tube is fully bioabsorbable in the mammalian body. This makes it especially suitable for use in conjunction with surgical stapling procedures, especially in endoscopic surgery. The rate of bioabsorption of the biopolymer can be controlled by cross-linking the biopolymer.
The biopolymer sponge tubes according to the present invention preferably have substantially uniform internal and external cross-sections. Preferably, the wall thickness of the tubes is also substantially constant.
Preferably, the internal and external cross-sections are both substantially circular or rectangular. Preferably, the average internal diameter of the biopolymer sponge tubes is from 3 mm to 30 mm, or preferably 5 mm to 20 mm, and the wall of the biopolymer sponge tube has a substantially uniform uncompressed wall thickness in the range of 1 to 4 mm. Preferably, the ratio of the length to the average external diameter of the biopolymer sponge tubes is in the range of 2:1 to 10:1, preferably 3:1 to 5:1. These preferred shapes and dimensions are especially suitable for fitting the biopolymer sponge tube over one or other barrel of a surgical stapler.
The biopolymer sponge tubes for use in the present invention are preferably prepared by a process comprising: providing an aqueous dispersion of the biopolymer; introducing the dispersion into a tube-shaped mold, following by freezing the dispersion to provide a shaped frozen dispersion; and freeze-drying or solvent-drying the shaped frozen dispersion to form the biopolymer sponge tube.
Preferably, the aqueous dispersion comprises 0.05-2.5% w/v of the biopolymer. The aqueous dispersion may be buffered to an optimum pH, and may also comprise therapeutic active agents for incorporation into the final biopolymer sponge tube. The aqueous dispersion may also contain emulsifi
Ethicon Inc.
Shatynski Theodore
Vargot Mathieu D.
LandOfFree
Methods for making biopolymer sponge tubes does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Methods for making biopolymer sponge tubes, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Methods for making biopolymer sponge tubes will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3301901