Metal deforming – By shot-blasting
Reexamination Certificate
2002-06-20
2003-12-09
Jones, David (Department: 3725)
Metal deforming
By shot-blasting
C029S090700, C451S039000
Reexamination Certificate
active
06658907
ABSTRACT:
FIELD OF THE INVENTION
This invention relates to a method for the treatment of shot peening and a treated article obtained by the process.
DESCRIPTION OF THE RELATED ART
It is conventionally known that to lengthen the life cycle of a metal product, a metal substance is to be treated by shot peening. A variety of materials are known as the peening materials used for the shot peening; however, among them a peening material made of cast steel has been conventionally and widely used. This peening material made of cast steel can give a high residual compressive-stress to the metal substance by increasing the speed of peening. However, there had been a problem in that due to the increased speed of peening, the surface of the metal substance might be damaged.
When the surface hardness of the metal substance is increased by heat treatment, it is difficult to give it a high residual compressive-stress by increasing the speed of peening to the-maximum. This is because the peening material is crushed. For this reason, the cases have been increasing where a peening material made of cemented carbide is used. (For example, see the Gazette of Japanese Patent Early-publication No. Hei. 08-323626.) When the peening material made of cemented carbide is used, a metal substance having a high surface hardness can be provided with a high residual compressive-stress. But, still in this case there is a problem in that the surface of the metal substance can be sometimes damaged.
A so-called treatment of double peening, which at first treats a metal substance with the peening material having a larger diameter, then treats it with the peening material having a smaller diameter, is a commonly used technique. But, there has been a problem in that plural peening equipment is indispensable for it. Proposed is a so-called mixed peening, which peens a metal substance by using a peening material having a larger diameter and a peening material having a smaller diameter. However, this technique has a variety of unsolved problems, such as the mixing ratio of the two peening materials, the control of the grain size, and the like, and it has not led to a practical use.
SUMMARY OF THE INVENTION
This invention has been accomplished to solve the above problems. The invention provides a method for the treatment of shot peening that provides a metal substance having a relatively high hardness as well as a low hardness, and with a high residual compressive-stress, and readily provides a smaller surface roughness of a treated article. The invention also provides a treated article obtained by this method. The invention further provides a peening material and a method of its use.
The invention aims to solve the problems in the conventional treatment of shot peening from the aspect of the peening material. The inventions comprise the following inventions, 1-8.
1) One of the methods for the treatment of shot peening of the invention is characterized in that a peening material having a Vickers hardness (Hv) in the range of 900-1100 and a Young's modulus of 200,000 MPa or less (more preferably a Young's modulus in the range of 50,000-150,000 MPa) is used.
2) One of the methods for the treatment of shot peening in the invention is characterized in that an iron-based amorphous spherical particle is used as a peening material having a Vickers hardness and Young's modulus in the above ranges.
3) One of the methods for the treatment of shot peening of the invention is characterized in that by using the peening material (more preferably the iron-based amorphous spherical particle) having a Vickers hardness and Young's modulus in the above ranges, a substance having a Vickers hardness of 950 or less (more preferably in the range of 650-950) is subject to the treatment of shot peening.
4) One of the methods for the treatment of shot peening of the invention is characterized in that by using a peening material having a Vickers hardness and Young's modulus in the above ranges, the above substance is treated by peening at a speed of peening of 100 m/s or less (more preferably 50-70 m/s).
5) One embodiment of the invention is a method of treating a substance made of steel having a Vickers hardness of 950 or less by shot peening, wherein the process is carried out by using an iron-based amorphous spherical particle as a peening material, so that the treated article has the characteristics of a maximum residual compressive-stress of 1600 MPa or more, and a surface roughness of 5 &mgr;m or less.
6) A treated article of the invention is a material treated by any one of the above methods.
7) A peening material of the invention is one having a Vickers hardness in the range of 90-1100 and a Young's modulus of 200,000 MPa or less (preferably an average particle diameter of 0.02 to 1.5 mm).
8) One of the methods of using a peening material in the invention is one that uses a peening material having a Vickers hardness in the range of 900 to 1100 and a Young's modulus of 200,000 MPa or less for the treatment of shot peening.
DETAILED EXPLANATION OF THE INVENTION
In the invention, “substance” means the material or the part made of metal that is to be subject to the treatment of shot peening. In the invention, a “treated article” means the substance which has been subject to the treatment of shot peening of the invention.
As in this invention, “shot peening” is well known to one skilled in the art. It is a kind of cold-work, and means an improvement of the mechanical properties of the substance.
As for the peening material used in the invention, iron-based amorphous metals are given. Among them, an iron-based amorphous spherical particle is preferable for the peening material of the invention because it can be manufactured relatively easily and at lower cost than in the conventional method.
The average diameter of the iron-based amorphous spherical particle used in the invention is not specifically limited. But, if the average diameter is in the range of 0.05-0.5 mm, the amorphous peening material having a Young's modulus of 50,000-150,000 can be manufactured by the Atomize method at relatively lower cost. If the average diameter of the particle is in the range of 0.05-0.3 mm, it can be manufactured more easily. However, if the average diameter of the particle is from 0.02 to 1.5 mm, it can still be manufactured. As the particle diameter becomes larger, it gets increasingly difficult to obtain spherical amorphous particles. When the diameter is greater than 1.5 mm, it is difficult to have the shape of it be spherical. Thus, it is further preferable that the average diameter of the peening material used in the invention be 0.05 mm to 1.5 mm.
It is preferable that the content of iron in the iron-based amorphous spherical particle used in the invention be 45 to 55 wt %. Also, the iron-based amorphous spherical particle used in the invention may comprise other metals. It may comprise, for example, nickel, cobalt, or the like.
As for the substance used in the invention, one having a Vickers hardness of 950 or less before the treatment of shot peening is preferable. For such hardness, by the treating process of the invention, the substance can be provided with a high residual compressive-stress, and a small surface roughness thereof can be achieved. On the other hand, even if the Vickers hardness of the substance is 650 or less, an effect similar to the above can be obtained. However, such a substance can be provided with a residual stress not based on the method of the invention, namely, by using a peening material of another type of material.
As for the substance used in the invention, carburized parts like a gear and a variety of molds, for example, fall under it. As for a material of it, for example, SKD, SUP, SCM, SNCM (by the Japanese Industrial Standards), and the like are given. Also, the shape of the substance is not limited, and, further, whether it is treated by heat, and the types of heat treatment, are not limited.
In this invention, the speed of peening is a concept which includes the speed of projection
Inoue Akihisa
Kajita Kouji
Kurosaki Junkou
Okumura Kiyoshi
Finnegan Henderson Farabow Garrett & Dunner LLP
Jones David
Sintokogio Ltd.
LandOfFree
Method of shot peening processing and article processed... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Method of shot peening processing and article processed..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Method of shot peening processing and article processed... will most certainly appreciate the feedback.