Radiation imagery chemistry: process – composition – or product th – Radiation modifying product or process of making – Radiation mask
Reexamination Certificate
2001-03-16
2003-06-24
Rouhanian, M. (Department: 1756)
Radiation imagery chemistry: process, composition, or product th
Radiation modifying product or process of making
Radiation mask
C216S067000
Reexamination Certificate
active
06582861
ABSTRACT:
BACKGROUND OF THE INVENTION
1. Field of the Invention
In general, the present invention relates to a method of reshaping a patterned photoresist. The surface of the patterned photoresist material is “trimmed” and “refinished”, to improve the pattern profile and surface finish of the patterned photoresist. The method is particularly useful in the preparation of reticles which are used in combination with an exposure tool to image photoresist layers overlying a semiconductor substrate. The method may also be used to prepare a photoresist masking layer which is used to transfer a pattern to an underlying hard masking material on a semiconductor substrate. The method is useful for reshaping patterned i-line photoresists and is particularly beneficial when the patterned photoresist is a deep ultra violet (DUV) photoresist.
2. Brief Description of the Background Art
Photoresist compositions are used in microlithographic processes for making miniaturized electronic components, such as in the fabrication of semiconductor device structures. The miniaturized electronic device structure patterns are typically created by transferring a pattern from a patterned masking layer overlying the semiconductor substrate rather than by direct write on the semiconductor substrate, because of the time economy which can be achieved by blanket processing through a patterned masking layer. With regard to semiconductor device processing, the patterned masking layer may be a patterned photoresist layer or may be a patterned “hard” masking layer (typically an inorganic material or a high temperature organic material) which resides on the surface of the semiconductor device structure to be patterned. The patterned masking layer is typically created using another mask which is frequently referred to as a photomask or reticle. A reticle is typically a thin layer of a chrome-containing material deposited on a glass or quartz plate. The reticle is patterned to contain a “hard copy” of the individual device structure pattern to be recreated on the masking layer overlying a semiconductor structure.
A reticle may be created by a number of different techniques, depending on the method of writing the pattern on the reticle. Due to the dimensional requirements of today's semiconductor structures, the writing method is generally with a laser or e-beam. A typical process for forming a reticle may include: providing a glass or quartz plate, depositing a chrome-containing layer on the glass or quartz surface, depositing an antireflective coating (ARC) over the chrome-containing layer, applying a photoresist layer over the ARC layer, direct writing on the photoresist layer to form a desired pattern, developing the pattern in the photoresist layer, etching the pattern into the chrome layer, and removing the residual photoresist layer. When the area of the photoresist layer contacted by the writing radiation becomes easier to remove during development, the photoresist is referred to as a positive-working photoresist. When the area of the photoresist layer contacted by the writing radiation material becomes more difficult to remove during development, the photoresist is referred to as a negative-working photoresist. Advanced reticle manufacturing materials frequently include layers of chromium, chromium oxide, and chromium oxynitride. The photoresist layer upon which the direct writing is carried out is frequently a chemically amplified DUV photoresist material today, because of pattern dimensional requirements.
A patterned chemically amplified DUV photoresist layer frequently exhibits a “foot” at the bottom of the pattern profile, where the photoresist layer interfaces with an underlying ARC layer on the chrome-containing surface. Some developed photoresists exhibit a “t”-top profile. In addition, the surface of the patterned photoresist layer typically exhibits standing waves, due to reflections which occur during the direct writing on the photoresist layer, despite the presence of the underlying ARC layer.
To provide a photomask or reticle capable of accurately producing critical dimensions of 0.15 &mgr;m or smaller, it is highly desirable to trim and resurface (reshape) the patterned DUV photoresist to remove a foot, a t-top, or standing waves remaining after patterning.
FIG. 1A
shows a schematic of a cross-sectional view of a typical starting structure
100
used to form a reticle, including, from bottom to top, a quartz substrate
102
, overlaid with chrome-containing layer
104
, overlaid with an ARC layer
106
, and a photoresist layer
108
. As shown in
FIGS. 1B and 1C
, after patterning of the photoresist layer
108
, there is often a “foot”
110
extending from the lower portion of patterned photoresist layer
108
toward the surface
116
of ARC layer
106
. The presence of a foot (feet)
110
makes it difficult to maintain control of the critical dimensions during subsequent etch transferring of the photoresist pattern through the ARC layer
106
and chrome containing layer
104
. The foot also impacts the metrology capabilities of the lithographer.
FIG. 1C
, which is an enlargement (from
FIG. 1B
) of a portion of the patterned photoresist layer
108
(with underlying ARC layer
106
), shows a line
107
which exhibits “t”-topping
113
in the upper portion of line
107
, feet
110
at the base of line
107
, and ripples (standing waves)
114
on the sidewall
111
surfaces
112
of line
107
. The “t”-topping
113
is believed to be caused by contamination/reaction which occurs at the upper surface of the photoresist layer during processing prior to development of the pattern. The standing waves
114
are generated by reflected radiation within the photoresist material, which occurs during the direct writing of the pattern into photoresist layer
108
. The ARC layer
106
helps reduce the standing wave effect by reducing reflection back from underlying layers and device features into the photoresist layer
108
, but standing waves are generated in varying degrees depending on the imaging system and the material composition of the particular photoresist. When the photoresist is a chemically amplified photoresist, transparency of the photoresist material is particularly high throughout the entire direct writing process; this results in increased reflectivity (greater than that for earlier i-line novolak photoresists), which increases the formation of standing waves
114
.
Since most photoresists are comprised of organic materials, a plasma formed from oxygen (O
2
) gas has been used to remove residual photoresist material remaining on the exposed surface
118
of ARC layer
106
after photoresist patterning. This cleaning of the exposed surface
118
of ARC layer
106
is frequently referred to as “descumming”, since a scum of residual organic material remains over surface
118
after patterning of photoresist layer
108
. A small reduction in the size of feet
110
may occur during the descumming process. However, since a plasma formed from O
2
gas tends to be isotropic in nature, the feet
110
are not removed completely. Or, if the feet
110
are totally removed, this frequently causes a change in the critical dimension (an enlargement in the opened area of the photoresist) of the pattern in patterned photoresist layer
108
by the time the feet
110
are removed.
It would be desirable to provide an effective process for reshaping the patterned photoresist, which process removes the feet at the base of patterned sidewalls and removes the ripples (standing waves) from sidewall surfaces while enabling the control of the photoresist critical pattern dimensions.
SUMMARY OF THE INVENTION
One embodiment of the present invention pertains to a method of selectively reshaping the surface of a patterned photoresist. This method includes providing a patterned photoresist layer overlying a layer of antireflective material, accelerating oxygen-comprising species with directionality normal to a surface of the patterned photoresist, and applying the oxygen-comprising species to the surface of the patterned photores
Buxbaum Alex
Montgomery Melvin W.
Church Shirley L.
Rouhanian M.
LandOfFree
Method of reshaping a patterned organic photoresist surface does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Method of reshaping a patterned organic photoresist surface, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Method of reshaping a patterned organic photoresist surface will most certainly appreciate the feedback.