Coating processes – Electrical product produced – Metal coating
Reexamination Certificate
1999-07-26
2001-07-03
Tung, T. (Department: 1743)
Coating processes
Electrical product produced
Metal coating
C204S421000, C204S424000, C427S229000, C427S265000, C427S299000, C427S376700, C427S383500, C427S404000, C427S419100, C427S443100, C427S443200
Reexamination Certificate
active
06254926
ABSTRACT:
BACKGROUND OF THE INVENTION
1. Field of the Invention
The present invention relates to an oxygen sensor element which can be used in an air-fuel ratio control for an automobile engine, and further relates to a method of producing such an oxygen sensor element.
2. Description of the Prior Art
In the exhaust system of an automobile engine, an oxygen sensor is provided for measuring the oxygen concentration in the exhaust gas so as to perform an air-fuel ratio control based on measured values of the oxygen concentration.
The oxygen sensor includes an oxygen sensor element for detecting the oxygen concentration. The oxygen sensor element includes a solid electrolyte and electrodes provided on the solid electrolyte. The electrodes include an internal electrode exposed to a reference gas and an external electrode exposed to a gas to be measured.
For providing the foregoing electrodes at electrode forming portions of the solid electrolyte, the following method has been used:
First, noble metal nuclei are adhered to the electrode forming portions of the solid electrolyte to form nucleus forming portions. Then, metal plating is applied to the nucleus forming portions to form plating films. Thereafter, the plating films are burned to form the foregoing electrodes on the solid electrolyte.
The foregoing nucleus forming portions are achieved by spraying particles of noble metal such as platinum (Pt), onto the electrode forming portions of the solid electrolyte.
As shown in
FIGS. 24A and 24B
, a large number of fine holes or cavities are formed on the surface of the solid electrolyte. Accordingly, when the noble metal particles are applied onto the surface of the solid electrolyte at the electrode forming portions thereof, the noble metal particles enter the cavities of the solid electrolyte to form the nucleus forming portions. Thus, upon plating the nucleus forming portions, a plating liquid reacts with the noble metal particles within the cavities so that the plating films are organically tangled with particles of the solid electrolyte to achieve a strong adhesion force therebetween based on an anchor effect. Then, by burning the plating films, the electrodes are achieved which are hard to peel off from the surface of the solid electrolyte.
However, there is the following problem in the foregoing method of forming the nucleus forming portions:
Specifically, there may be formed a complicated pattern, as the foregoing electrode, on the surface of the solid electrolyte as shown, for example, in FIG.
2
A and FIG.
9
. Accordingly, in the foregoing forming method employing spraying of the noble metal particles, it is necessary to partially mask the surface of the solid electrolyte and thus it is difficult to produce the electrode of a complicated shape.
Japanese First (unexamined) Patent Publication No. 4-95766 discloses another forming method, wherein a solution containing a noble metal compound is applied to the electrode forming portions of the solid electrolyte to form coating films and then, by heating the coating films at a high temperature, those components (for example, a binder) other than the noble metal in the solution are volatilized or decomposed so that only the noble metal nuclei are deposited to form nucleus forming portions.
In the latter forming method, the nucleus forming portion can be easily provided at the electrode forming portion of a desired shape using, for example, screen printing, stamp printing, pad printing, roll transfer, dip method, spray method or dispenser method.
However, the latter forming method has the following problem:
Specifically, since the heating of the coating films is carried out at a high temperature, i.e. about 700° C. or higher, flocculation of the noble metal advances so that the mean particle diameter of the noble metal nuclei becomes 0.1 &mgr;m to 0.8 &mgr;m. Hence, as shown in
FIG. 24A
, the noble metal nuclei
92
can not enter the fine cavities
21
formed on the surface of the solid electrolyte
2
, but stay at entrances of the fine cavities
21
.
In this case, as shown in
FIG. 24B
, the plating film
119
can not advance into the fine cavities
21
so that the adhesion force based on the anchor effect can not be achieved between the plating film
119
and the solid electrolyte
2
.
Further, as shown in
FIG. 24A
, in the latter forming method, the noble metal nuclei
92
are localized on the surface of the solid electrolyte
2
. This means that distances between the adjacent noble metal nuclei
92
become large. As appreciated, the adhesion force between the plating film
119
and the solid electrolyte
2
can not be achieved at portions where no noble metal nuclei
92
exist, and thus, in the latter forming method, those portions where the adhesion force can not be achieved exist largely on the surface of the solid electrolyte
2
.
Consequently, in the latter forming method, such an oxygen sensor element tends to be produced, wherein the peeling-off of the electrode is liable to occur and the surface resistance at an interface between the electrode and the solid electrolyte
2
is excessively large to disable outputs required for detection of the oxygen concentration.
SUMMARY OF THE INVENTION
Therefore, it is an object of the present invention to provide an oxygen sensor element, wherein an electrode is hard to peel off from a solid electrolyte and the surface resistance at an interface between the electrode and the solid electrolyte is small.
It is another object of the present invention to provide a method of producing such an oxygen sensor element.
According to one aspect of the present invention, an oxygen sensor element comprises a solid electrolyte having cavities on a surface thereof; and an electrode formed on the surface of the solid electrolyte, the electrode deeply entering the cavities for ensuring adhesion of the electrode relative to the surface of the solid electrolyte.
It may be arranged that the electrode is in the form of a plating film produced via noble metal nuclei provided on the surface of the solid electrolyte, the noble metal nuclei having a mean particle diameter which is small enough for the noble metal nuclei to deeply enter the cavities.
It may be arranged that the mean particle diameter of the noble metal nuclei is 0.05 &mgr;m or smaller.
It may be arranged that each of the cavities has finer cavities therein, and that the electrode further enters the finer cavities.
According to another aspect of the present invention, a method of producing an oxygen sensor element which includes a solid electrolyte having cavities on a surface thereof and an electrode formed on the surface of the solid electrolyte, comprises the steps of: applying a solution containing a noble metal compound for nucleus formation to the surface at an electrode forming portion of the solid electrolyte to form a coating film; heat-treating the coating film by heating to form a nucleus forming portion where noble metal nuclei are deposited: plating the nucleus forming portion to form a plating film, the plating film deeply entering the cavities; and burning the plating film to form the electrode so that the electrode deeply enters the cavities.
It may be arranged that the noble metal nuclei have a mean particle diameter which is small enough for the noble metal nuclei to deeply enter the cavities.
It may be arranged that the mean particle diameter of the noble metal nuclei is 0.05 &mgr;m or smaller.
It may be arranged that the coating film is heat-treated at a temperature in the range of 200° C. to 600° C.
It may be arranged that the noble metal compound is an organic noble metal compound.
It may be arranged that a concavo-convex treatment is applied to the surface of the solid electrolyte for promoting irregularities to be formed on the surface.
It may be arranged that a concentration of the noble metal compound relative to the solution is 0.05% by weight to 0.4% by weight.
It may be arranged that noble metal in the noble metal compound is at least one selected from the group consisting of Pt, Pd, Au and Rh.
REFERENCES:
patent: 393
Katafuchi Toru
Kobayashi Kiyomi
Miwa Naoto
Saito Toshitaka
Sano Hiromi
Denso Corporation
Pillsbury & Winthrop LLP
Tung T.
LandOfFree
Method of producing oxygen sensor element does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Method of producing oxygen sensor element, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Method of producing oxygen sensor element will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2519694