Method of producing fast-fired cordierite bodies

Details Method of producing fast-fired cordierite bodies Method of producing fast-fired cordierite bodies

1998-07-14

1999-12-21

Derrington, James

Plastic and nonmetallic article shaping or treating: processes

Outside of mold sintering or vitrifying of shaped inorganic...

Producing article having plural hollow channels

264639, 264679, 26417712, C04B 3332

Patent

active

060045019

ABSTRACT:
A cordierite body is produced by providing cordierite-forming raw materials as talc, calcined talc, MgO-forming component, magnesium aluminate spinel, SiO.sub.2 -forming component, Al.sub.2 O.sub.3 -forming component, kaolin, calcined kaolin, and/or mullite, such that the quantity R is less than about 1.207. R is

REFERENCES:
patent: 3885977 (1975-05-01), Lachman et al.
patent: 3979216 (1976-09-01), Fritsch, Jr. et al.
patent: 4001028 (1977-01-01), Frost et al.
patent: 4280845 (1981-07-01), Matsuhisa et al.
patent: 4772580 (1988-09-01), Hamanaka et al.
patent: 4869944 (1989-09-01), Harada et al.
patent: 4877670 (1989-10-01), Hamanaka et al.
patent: 4927577 (1990-05-01), Ohtaka et al.
patent: 5046946 (1991-09-01), Yasuda et al.
patent: 5114643 (1992-05-01), Beall et al.
patent: 5114644 (1992-05-01), Beall et al.
patent: 5258150 (1993-11-01), Merkel et al.
patent: 5262102 (1993-11-01), Wada
patent: 5332703 (1994-07-01), Hickman et al.
patent: 5409870 (1995-04-01), Locker et al.

Affiliated with

Also associated with

Rating

Method of producing fast-fired cordierite bodies does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Method of producing fast-fired cordierite bodies, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Method of producing fast-fired cordierite bodies will most certainly appreciate the feedback.

Rate now

Comments { 0 }

Profile ID: LFUS-PAI-O-501887