Method of preparing glass fiber filter

Details Method of preparing glass fiber filter Method of preparing glass fiber filter

2000-10-05

2002-10-29

Savage, Matthew O. (Department: 1723)

Liquid purification or separation

Processes

Liquid/liquid solvent or colloidal extraction or diffusing...

C210S651000, C210S767000, C436S079000, C436S177000, C436S178000, C422S105000, C065S031000, C065S472000, C501S039000

Reexamination Certificate

active

06471868

ABSTRACT:

BACKGROUND OF THE INVENTION
This invention relates to a method of preparing a glass fiber filter suitable for the preparation of plasma or serum by filtering whole blood.
The type or concentration of blood components, such as metabolites, proteins, lipids, electrolytes, enzymes, antigens, and antibodies, is measured, in general, using a plasma or serum sample obtained by centrifuging whole blood. However, centrifuging takes labor and time. Particularly, centrifuging is unsuitable for an urgent case of measuring a small number of samples promptly and in site inspection, because of requiring a centrifuge and electricity. Thereupon, it has been investigated to separate plasma or serum from whole blood by filtration.
Several filtration methods using glass fiber filter have been developed wherein whole blood is charged into the glass fiber filter put in a column from one side of the column, and pressurized or evacuated to obtain plasma or serum from the other side (Japanese Patent KOKOKU Nos. 44-14673, 5-52463, Japanese Patent KOKAI Nos. 2-208565, 4-208856).
However, practical filtration methods capable of obtaining an amount of plasma or serum from whole blood necessary for measuring by an automatic analyzer have not been developed except a part of items, such as blood sugar.
On the other hand, the inventors developed a blood filter unit composed of a filter holder and a syringe. The filter holder is composed of a holder body which contains filter material and a cap which is screwed on the holder body. The filter material consists of, e.g. two sheets of glass fiber filter, one sheet of cellulose filter and one sheet of polysulfone microporous membrane (FIG. 1 of EP 785430 A1)
Another blood filter unit composed of a holder body and a cap was also developed. The holder body consists of a plasma receiver located on the upper side and a filter chamber located on the underside. The filter material put in the filter chamber is composed of six sheets of glass fiber filter and one sheet of polysulfone microporous membrane (Example 1 of EP 785012A1).
Incidentally, the electrolytes to be measured for clinical assay include calcium, sodium, potassium, chlorine and so on. However, as a result of investigating commercial glass fiber filters, the inventors found that some of them are eluted into blood to cause analytical errors.
SUMMARY OF THE INVENTION
An object of the invention is to provide a method of preparing a glass fiber filter which does not influence blood component analysis, such as calcium, sodium, potassium and chlorine, even when using for blood filtration.
The inventors investigated in order to solve the above problems, and first, they attempted to wash glass fiber filter with purified water by ion-exchange resins. As a result, sodium was removed by the washing with water, but calcium and potassium were increased conversely. Thereupon, they further investigated, and found that organic acid, mineral acid and hot water are very effective for the removal of calcium, sodium, potassium and so on, to succeed in obtaining a glass fiber filter which has solved the problem of errors caused by these ions.
Thus, the present invention provides a method of preparing a glass fiber filter of which the elution quantity of calcium, sodium and potassium is small, which comprises treating the filter with an organic acid, mineral acid or hot water.
DETAILED DESCRIPTION OF THE INVENTION
Preferable glass fiber filter has a density of about 0.02 to 0.5 g/cm
3
, preferably about 0.03 to 0.2 g/cm
3
, more preferably about 0.05 to 0.13 g/cm
3
, a retainable particle size of about 0.6 to 9 &mgr;m m preferably 1 to 5 &mgr;m.
As an indicator corresponding to v6id volume or filtrate volume of plasma, water permeation speed is suitable. The water permeation speed is determined by putting a glass fiber filter with a definite area in a closed filter unit of which the inlet and outlet can be connected by a tube, adding a definite volume of water, and pressurizing or sucking at a constant pressure. The water permeation speed is filtrate volume per unite area and time, and expressed by ml/sec.
For example, glass fiber filter 20 mm &phgr; in diameter is put in a filter unit, and a 100 ml syringe containing 60 ml water is connected to the top of the filter unit. Water flows down naturally, and volume of water passing through the glass filter from 10 sec to 40 sec after starting is measured as the water permeation volume, and the water permeation speed per unit area is calculated from it.
Glass fiber filters particularly suitable for plasma or serum separation have a water permeation speed of about 1.0 to 1.3 ml/sec, and illustrative of the glass fiber filters are Whatman GF/D, Toyo Roshi GA-100, GA-200 and the like. Furthermore, the glass fiber filter can be prepared by suspending glass fibers of a commercial glass fiber filter in hot water, and then making the glass fibers into a low density sheet (density: about 0.03 g/cm
3
) on a nylon net. The glass fiber filter thus prepared shows good plasma separating ability.
A suitable thickness of the glass fiber filter is about 0.1 to 10 mm, preferably about 0.3 to 8 mm.
Suitable organic acids are various carboxylic acids, amino acids and the like, such as acetic acid, citric acid, succinic acid, malic acid, maleic acid and ethylenediaminetetraacetic acid, and particularly, acetic acid is preferable. A suitable concentration of the organic acid is about 0.1 &mgr;M to 1 M, preferably about 1 &mgr;M to 100 mM, particularly preferably 10 &mgr;M to 10 mM. The diluent for adjusting the concentration as above is usually water, and the organic acid used in the invention is usually an aqueous solution.
Suitable mineral acids are hydrochloric acid, nitric acid, sulfuric acid and the like, and a suitable concentration of the mineral acid is about 0.1 &mgr;m to 10 mM, preferably about 0.01 to 0.5 mM. When the concentration of the mineral acid exceeds 10 mM, the analytical values of potassium and calcium become to low. The diluent for adjusting the concentration as above is also usually water, and the mineral acid is usually an aqueous solution.
The treatment of the glass fiber with the organic acid or mineral acid is carried out by contacting the glass fiber filter with the organic acid or mineral acid, such as immersing or showering, if necessary with moderate stirring or circulating. Suitable treating conditions are, in the case of the organic acid, at 5 to 80° C., preferably for 10 to 60° C. for 1 second to 60 minutes, preferably for 10 seconds to 20 minutes, and in the case of the mineral acid, at 5 to 80° C., preferably at 10 to 60° C., for 1 second to 60 minutes, preferably 0.5 to 20 minutes. A suitable quantity of the organic acid or mineral acid is about 0.1 to 50 l, preferably about 0.2 to 10 l per 10 g glass fiber. During treating, the acid is preferably exchanged once to several times.
After the treatment with the acid, the glass fiber filter is washed with water to remove adhered materials to the glass fiber filter such as the acid. The water for washing is purified water not containing calcium, sodium, potassium and the like at least up to the degree influencing analysis, and demineralized water, such as purified by ion-exchange resins, distilled water or the like is used. The temperature of washing water is about 5 to 80° C., usually ordinary temperature.
When glass fiber filter is treated with hot water, purified water is used as the hot water. The purified water does not contain calcium, sodium, potassium at least up to the degree influencing analysis, and demineralized water, such as purified by ion-exchange resins, distilled water or the like is used.
The treatment of the glass fiber filter with the hot water is also carried out by contacting the glass fiber filter with the hot water, such as immersing or showering, if necessary with moderate stirring or circulating. Suitable treating conditions with the hot water are at about 35 to 100° C., preferably at about 60 to 100° C., for about 1 second to 60 minutes, preferably for about 0.5 to 20 minutes. A suitable quant

Affiliated with

Also associated with

Rating

Method of preparing glass fiber filter does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Method of preparing glass fiber filter, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Method of preparing glass fiber filter will most certainly appreciate the feedback.

Rate now

Comments { 0 }

Profile ID: LFUS-PAI-O-2995236