Plastic and nonmetallic article shaping or treating: processes – Including step of generating heat by friction
Patent
1986-07-16
1987-08-25
Derrington, James
Plastic and nonmetallic article shaping or treating: processes
Including step of generating heat by friction
264 63, 264332, 428367, C04B 3580
Patent
active
046891889
ABSTRACT:
Alternate layers of mats of specially coated SiC fibers and silicon monotapes are hot pressed in two stages: In the first a die is heated to about 600.degree. C. in a vacuum furnace and maintained at this temperature for about one-half hour to remove fugitive binder.
In the second stage the die temperature is raised to about 1000.degree. C. and the layers are pressed at between 35 MPa and 138 MPa. The resulting preform is placed in a rector tube where a nitriding gas is flowed past the preform at 1100.degree. C. to 1400.degree. C. to nitride the same.
REFERENCES:
patent: 3819786 (1974-06-01), May
patent: 3926656 (1974-10-01), Mangels
patent: 4004937 (1975-11-01), Masaki
patent: 4158687 (1979-06-01), Yajima et al.
patent: 4285895 (1981-08-01), Mangels et al.
patent: 4465650 (1984-08-01), Ohno
Derrington James
Manning John R.
Shook Gene E.
The United States of America as represented by the Administrator
LandOfFree
Method of preparing fiber reinforced ceramic material does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Method of preparing fiber reinforced ceramic material, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Method of preparing fiber reinforced ceramic material will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-1922179