Plastic and nonmetallic article shaping or treating: processes – Direct application of electrical or wave energy to work – Molecular aligning or molecular orientating
Reexamination Certificate
2000-08-12
2002-10-15
Fiorilla, Christopher A. (Department: 1731)
Plastic and nonmetallic article shaping or treating: processes
Direct application of electrical or wave energy to work
Molecular aligning or molecular orientating
C264S040100, C264S436000
Reexamination Certificate
active
06464925
ABSTRACT:
BACKGROUND OF THE INVENTION
1. Field of the Invention
The present invention relates to a method of polarization-treating a piezoelectric body for use in a ceramic filter, a ceramic oscillator, and other suitable devices.
2. Description of the Related Art
For polarization-treatment of piezoelectric ceramic substrates (block, unit, or other forms) of PZT and PT types, conventionally, after a piezoelectric ceramic substrate is fired, electrodes are provided on both of the opposite surfaces of the piezoelectric ceramic substrate. A plurality of piezoelectric ceramic substrates are simultaneously dipped into a polarization liquid at a temperature of 60° C. to 100° C., and a voltage of 2 kV/mm to 8 kV/mm is applied for about 10 to 30 minutes to obtain a desired polarization degree.
Polarization treatment of a piezoelectric body may be performed by in-liquid polarization which is carried out in a polarization liquid having insulation properties as described above, in-air polarization which is conducted in the atmosphere or in an gas atmosphere. In the in-air polarization, a desired electric field intensity can not be attained, since discharge occurs at a voltage of about 1 kV/mm or higher. For this reason, in general, the in-liquid polarization is carried out in order to obtain a high polarization degree.
However, in the case of the in-liquid polarization, the polarization degree of a piezoelectric body can not be measured during polarization. This is because the vibration of the piezoelectric body placed in the liquid is damped, due to the liquid, and the frequency characteristic can not be measured. For this reason, conventionally, the in-liquid polarization is a constant-time polarization in which the polarization is carried out for a predetermined time period. As a result, there arises the problem that the polarization degree can not be exactly controlled, causing the firing and composition of the piezoelectric body to be dispersed, which results in dispersion of the polarization degree.
In Japanese Patent No. 2656041, a polarization method includes measuring a piezoelectric constant (for example, electromechanical coupling coefficient K) during polarization, and the application of a voltage is stopped when the constant reaches the predetermined level which is decided by a correlation between the value K obtained immediately after the polarization is stopped and the stable value K obtained after a lapse of time. By this, dispersion of the polarization degree, caused by dispersion of materials and firing conditions, can be reduced. Accordingly, a piezoelectric body having constant qualities can be produced.
However, in the above-described method, it is necessary to determine the piezoelectric constant value based on the frequency during the polarization, which requires a long measurement time. Accordingly, when many piezoelectric bodies are simultaneously polarized, it is likely that over-polarization occurs due to a measurement lag.
Moreover, there arises the problem that it is necessary to provide an impedance analyzer, an AC signal source, an AC/DC separation circuit, a change-over circuit, and so forth in order to measure the piezoelectric constant during polarization, and the measuring device is complicated and is expensive.
SUMMARY OF THE INVENTION
To overcome the problems described above, preferred embodiments of the present invention provide a method of polarization-treating a piezoelectric body in which dispersion of the polarization degrees of respective piezoelectric bodies are greatly reduced, and a target polarization degree is attained very precisely.
Further, preferred embodiments of the present invention provide a method of polarization-treating a piezoelectric body in which over-polarization caused by a measurement lag is prevented.
According to a preferred embodiment of the present invention, a method of polarization-treating a piezoelectric body having the characteristic that current flowing through the piezoelectric body, caused by application of a direct current (DC) voltage to the piezoelectric body is increased, the method including the steps of applying a DC voltage to the piezoelectric body, measuring current flowing through the piezoelectric body caused by the application of the DC voltage, and stopping the application of the DC voltage at the time when the measured current value reaches a set level.
In the case where a piezoelectric body made of a material such as piezoelectric ceramics is polarized, as current flows through the piezoelectric body during the polarization, the current tends to be increased exponentially over time, as shown in
FIG. 1
, as an example.
One of the reasons for the current increase as shown in
FIG. 1
is that with the progression of the polarization, the internal orientation of a crystal proceeds in the electric field direction, which causes the insulation resistance of the piezoelectric body to decrease over time, and the decrease of the insulation resistance causes the current value to increase. The current increase during the polarization appears more distinctly as the temperature becomes higher.
In the case of a piezoelectric body having current flowing through the piezoelectric body caused by the application of a DC voltage, is increased as shown in
FIG. 1
, the polarization degree of the piezoelectric body can be predicted based on the current value. In particular, since the current flowing through the piezoelectric body and the polarization degree have a high correlation, the polarization degree can be made to approach a target value by stopping the polarization at the time when the current value reaches a set level, and dispersion of the polarization degree can be reduced.
Moreover, it is unnecessary to measure the polarization degree (frequency characteristics) during polarization as conventionally required. It is only necessary to measure the current. Thus, the measurement time can be significantly shortened, and over-polarization, caused by measurement lag when many piezoelectric bodies are polarized, are prevented.
In addition, since it is unnecessary to measure the frequency during polarization, the apparatus for polarization according to preferred embodiments of the present invention is greatly simplified.
According to preferred embodiments of the present invention, either method of in-liquid polarization or in-air polarization may be used, since measurement of the frequency characteristics of a piezoelectric body is unnecessary.
FIG. 2
shows the variation of the polarization degree of a piezoelectric body in the steps ranging from polarization to aging to ordinary temperature restoration.
As seen in
FIG. 2
, the polarization degree increases to the maximum during the polarization, and is reduced by the aging, and is partially restored in the ordinary temperature restoration so as to be stabilized. The maximum polarization degree &Dgr;f
1
in the polarization and the maximum current value (current limit value) i
L
at the maximum polarization degree &Dgr;f
1
have a high correlation. Further, the maximum polarization degree &Dgr;f
1
and the stable polarization degree &Dgr;f
2
obtained after the ordinary temperature restoration have a high correlation. Accordingly, the current limit value i
L
and the stable polarization degree &Dgr;f
2
obtained after the ordinary temperature restoration have a high correlation. In the above example, the polarization degree of a piezoelectric body is determined based on the frequency difference &Dgr;f between the resonance frequency fr and the anti-resonance frequency fa. A piezoelectric constant such as an electromechanical coupling coefficient K, a center frequency, or the like may be used to determine the polarization degree.
FIG. 3
shows a correlation between the current limit value i
L
in the polarization and the polarization degree &Dgr;f
2
obtained after the application to the aging to the ordinary temperature restoration, following the current value reaching the current limit value. The correlation was determined under the following conditions:
piezoelectric bod
Fujii Naoki
Tomohiro Hiroshi
LandOfFree
Method of polarization-treating piezoelectric body does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Method of polarization-treating piezoelectric body, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Method of polarization-treating piezoelectric body will most certainly appreciate the feedback.