ABSTRACT:
A sheet metal made from a ferritic stainless steel alloy which has an improved corrosion resistivity and is suitable for use in manufacturing exterior building material, in particular, roofing material, by means of forming process such as roll-forming, without formation of pocket wave. The steel alloy comprises 10-32 wt % of Cr and 0.005-0.1%, in total, of C and N, the balance being Fe and unavoidable impurities. The sheet metal has been processed to present a mechanical property that, when tested in a tensile test conducted for a test piece sample in the widthwise direction of cold-rolling and measured at the elastic limit reached in the test, a strain ratio is equal to or greater than 2.5.
The method of making the sheet metal comprises the steps of: cold rolling a steel slab into a sheet metal, subjecting the thus obtained sheet metal to final annealing, subjecting the sheet metal to skin-pass rolling, and, subjecting the resulting sheet metal to aging process at a temperature of 200.degree.-550.degree. C. for a time period of more than 5 seconds and less than 48 hours.
REFERENCES:
patent: 4726853 (1988-02-01), Gressin et al.
Hino Masayuki
Kinoshita Noboru
Sone Yuji
Yazawa Yoshihiro
Yoshioka Keiichi
Kawasaki Steel Corporation
Yee Deborah
LandOfFree
Method of making stainless steel sheet for exterior building con does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Method of making stainless steel sheet for exterior building con, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Method of making stainless steel sheet for exterior building con will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-33722