ABSTRACT:
A continuous spin-draw process of making dimensionally stable polyester fiber having high strength and low shrinkage by melt spinning polyethylene terephthalate and drawing comprising multiple drawing stages of at least two stages where the spun yarn is passed from the takeup roller to a first pair of drawing rollers, then to a final pair of drawing rollers, then to a pair of relaxation rollers and then to yarn take up means; the surface temperature of said final pair of drawing rollers being maintained at 10.degree. to 60.degree. C. lower than the melting point of the drawn fiber; a non-contct type heated plate whose surface temperture is heated to 250.degree. to 500.degree. C. is positioned 20 to 100 mm separated from the yarn, thereby heating the yarn to obtain the relaxation heat treatment; and applying a commingling treatment to the drawn fiber by installing a commingling treatment apparatus between the final pair of drawing rollers and the pair of relaxation rollers.
REFERENCES:
patent: 3739056 (1973-06-01), Evans et al.
patent: 3966867 (1976-06-01), Munting
patent: 4003974 (1977-01-01), Chantry et al.
patent: 4414169 (1983-11-01), McClary
patent: 4491657 (1985-01-01), Saito et al.
Nishikawa Kinsaku
Takahashi Masami
Yokoyama Hiroshi
Lorin Hubert C.
Unitika Limited
LandOfFree
Method of making polyester fibers does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Method of making polyester fibers, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Method of making polyester fibers will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-1368701