Method of making a metallic press fitting element

Details Method of making a metallic press fitting element Method of making a metallic press fitting element

2000-07-21

2003-02-25

Hughes, S. Thomas (Department: 3726)

Metal working

Method of mechanical manufacture

Gas and water specific plumbing component making

C029S890140, C029S508000

Reexamination Certificate

active

06523261

ABSTRACT:

CROSS-REFERENCES TO RELATED APPLICATIONS
This application claims the priority of German Patent Applications, Serial Nos. DE 199 34 899.5, filed Jul. 22, 1999, DE 100 29 479.0, filed Jun. 15, 2000 and DE 100 29 480.4, filed Jun. 15, 2000, the subject matter of which is incorporated herein by reference.
BACKGROUND OF THE INVENTION
The present invention relates, in general, to a method of making a metallic press fitting element.
Press fitting elements, involved here, come in various designs and are shown by way of example in
FIGS. 1
to
8
.
FIG. 1
shows a sleeve
1
, and
FIG. 2
shows a sliding sleeve
2
. Both these press fitting elements
1
,
2
are characterized by a hook-shaped region
3
of substantially roof-shaped cross section for insertion of an O-ring gasket (not shown), and a cylindrical region
4
formed inwardly of the hook-shaped region
3
at a distant to the insertion end of a pipe (not shown) that is intended for connection to the sleeve
1
or sliding sleeve
2
.
FIG. 3
shows a representation of a street union
5
with internal thread, and
FIG. 4
shows a street fitting
6
with outer thread. Both, the street union
5
and the street fitting
6
are characterized by a hexagon zone
7
for attachment of a wrench (not shown) to establish the connection. The extent of material removal can be reduced when using a starting material which has an outer hexagon profile either across its entire length or reduced to this zone.
FIGS. 5 and 6
show press fitting elements
8
,
9
of a type that is identical to the fittings of
FIGS. 3 and 4
but for the additional provision of a short cylindrical region
10
upon the hook-shaped region
3
.
FIG. 7
shows a 90° branch
11
with internal thread, and
FIG. 8
shows a side view of a ceiling elbow
12
which includes an attachment plate
13
. Also the press fitting elements
11
,
12
are suitable for manufacture by the method according to the present invention, even though the extent of material removal is necessarily increased compared to purely rotationally symmetrical press fitting elements. The attachment plate
13
for the ceiling elbow
12
is made separately and connected to the actual press fitting element by welding or soldering.
According to a publication, issued by Mannesmann and entitled “Pressfitting-System/Sanitär”, ed. 8/1994, press fittings are known to be made from carbon steel or high alloy steel for installation in buildings. A core element of the described system is a press fitting which is made from a pipe section and is plastically deformable, for use as sleeve, bend, tee or reducer. A drawback of these conventional fittings is the need to make the fitting in several forming steps from a portion of a particularly manufactured pipe in order to meet the high requirements with respect to surface and dimensional tolerances. The initial pipe from which the fitting is made is normally a seamless pipe or a pipe made through straight bead welding and has narrow tolerances and a high-grade surface. The initial pipe is cut into sections, and the final configuration of the fitting is realized by carrying out several shaping steps, e.g. necking, flanging, pressing. As the starting material is already of fairly high quality, the resultant fitting becomes relatively expensive. Another drawback of this manufacturing process is its applicability for only standard fittings. For other fittings that may include threads such as street fittings or bends as well as ceiling elbows and street elbows, the afore-mentioned manufacturing method is not applicable.
German Pat. No. 39 19 496 C1 describes a manufacturing process by which the area that is specific for the type of fitting is made from a base body cast from a metallic material and securely fixed to a standardized adapter made of sheet metal. The connection may be realized by welding, soldering or cementing. This manufacturing process suffers also shortcomings because of the need to make a separate adapter, the need for a connection, and the problems associated with a control of the connection seam.
European Pat. No. 0 343 395 B1 described a press-fit arrangement in which a connection piece of an armature or a fitting of cast metal is pressed onto an unreinforced pipe which does not have any substantial changes to the wall thickness in the area of the press-fit. The compressive yield point of the connection piece is thereby at best as great as that of the pipe. The wall thickness of the connection piece is so sized as to withstand a recovery in shape of the pipe due to its elasticity after stress removal. Examples of cast metal include a red brass alloy which contains approximately 2% Sn, 8% Zn, 5% Pb, 2.2-3.0% Ni and the rest copper. Red brass is basically a brittle material which cannot plastically deform without cracking. As a consequence, the wall thickness should be thin enough in the pressing zone of the connection piece, on the one hand, and should be thick enough to withstand the elastic recovery of the pipe. Moreover, the red brass alloy should have a sufficient Ni-content to enhance the fracture strain.
German patent publication DE-AS 11 87 870 describes a method of making a pipe joint comprised of a plastically deformable metallic coupling sleeve of steel, which is made through compression molding. As an alternative, a turning process may also be use to make the coupling sleeve. The produced coupling sleeve has a hook-shaped region of substantially roof-shaped cross section for receiving an O-ring gasket, and a cylindrical region formed inwardly of the hook-shaped region at a distant to the insertion end of a steel pipe to be joined to the coupling sleeve. A non-detachable tight joint between the coupling sleeve and the steel pipe is implemented by suitably attaching and closing two clamping jaws. During squeezing action, the clamping jaws act upon the hook-shaped region with inserted O-ring gasket and the cylindrical region of the coupling sleeve, thereby reducing the diameter of both contacted regions. A drawback of this process resides in the fact that the O-ring gasket is only slightly compressed during the squeezing action, so that the seal is sufficient only for small pressures. A further drawback associated in particular in conjunction with coupling sleeves of steel is the creation during the turning process of a flow chip which can get wedged into the hook-shaped region. As a result, the turning process is impaired and the lathe tool may ultimately be destroyed. Thus, extended breakdown periods and shutdown periods are experienced, so that the costs for the press fitting element are increased.
German Pat. No. DE 295 04 502 U1 describes a method of making a compressible fitting made of malleable cast iron. This fitting has all the features of a conventional press fitting made of sheet metal. A drawback of this manufacturing process is the need to subject the blanks to an annealing process to impart a useable structure. Subsequently, the blanks are machined to remove the outer crust and to correct dimensional inaccuracies. These types of press fittings of malleable cast iron are not permitted for internal pressures exceeding 25 bar.
SUMMARY OF THE INVENTION
It is thus an object of the present invention to provide an improved method of making a metallic press fitting element, obviating the afore-stated drawbacks.
In particular, it is an object of the present invention to provide an improved method of making a metallic press fitting element irrespective of the used metallic material.
It is yet another object of the present invention to provide an improved method of making in particular rotationally symmetrical press fitting elements in a cost-efficient and reproducible manner for application at operating pressures of up to 40 bar.
These objects, and others which will become apparent hereinafter, are attained in accordance with the present invention by a method which includes as starting material a solid or hollow bar which is machined, or alternatively machined and shaped without material removal, to form a finished press fitting element with a pre

Affiliated with

Also associated with

Rating

Method of making a metallic press fitting element does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Method of making a metallic press fitting element, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Method of making a metallic press fitting element will most certainly appreciate the feedback.

Rate now

Comments { 0 }

Profile ID: LFUS-PAI-O-3167319