Method of making a coating of a microtextured surface

Details Method of making a coating of a microtextured surface Method of making a coating of a microtextured surface

2001-03-19

2004-11-02

Chen, Bret (Department: 1762)

Coating processes

Direct application of electrical, magnetic, wave, or...

Polymerization of coating utilizing direct application of...

C427S497000, C427S509000, C427S398100

Reexamination Certificate

active

06811829

ABSTRACT:

FIELD OF THE INVENTION
The present invention relates generally to a method of making plasma polymerized polymer films. More specifically, the present invention relates to making a plasma polymerized polymer film onto a microtextured surface via plasma enhanced chemical deposition with a flash evaporated feed source of a low vapor pressure compound.
As used herein, the term “(meth)acrylic” is defined as “acrylic or methacrylic.” Also, (meth)acrylate is defined as “acrylate or methacrylate.”
As used herein, the term “cryocondense” and forms thereof refer to the physical phenomenon of a phase change from a gas phase to a liquid phase upon the gas contacting a surface having a temperature lower than a dew point of the gas.
As used herein, the term “polymer precursor” includes monomers, oligomers, and resins, and combinations thereof. As used herein, the term “monomer” is defined as a molecule of simple structure and low molecular weight that is capable of combining with a number of like or unlike molecules to form a polymer. Examples include, but are not limited to, simple acrylate molecules, for example, hexanedioldiacrylate, or tetraethyleneglycoldiacrylate, styrene, methyl styrene, and combinations thereof. The molecular weight of monomers is generally less than 1000, while for fluorinated monomers, it is generally less than 2000. Substructures such as CH
3
, t-butyl, and CN can also be included. Monomers may be combined to form oligomers and resins, but do not combine to form other monomers.
As used herein, the term “oligomer” is defined as a compound molecule of at least two monomers that can be cured by radiation, such as ultraviolet, electron beam, or x-ray, glow discharge ionization, and spontaneous thermally induced curing. Oligomers include low molecular weight resins. Low molecular weight is defined herein as about 1000 to about 20,000 exclusive of fluorinated monomers. Oligomers are usually liquid or easily liquifiable. Oligomers do not combine to form monomers.
As used herein, the term “resin” is defined as a compound having a higher molecular weight (generally greater than 20,000) which is generally solid with no definite melting point. Examples include, but are not limited to, polystyrene resin, epoxy polyamine resin, phenolic resin, and acrylic resin (for example, polymethylmethacrylate), and combinations thereof.
BACKGROUND OF THE INVENTION
The basic process of plasma enhanced chemical vapor deposition (PECVD) is described in THIN FILM PROCESSES, J. L. Vossen, W. Kern, editors, Academic Press, 1978, Part IV, Chapter IV-1 Plasma Deposition of Inorganic Compounds, Chapter IV-2 Glow Discharge Polymerization, herein incorporated by reference. Briefly, a glow discharge plasma is generated on an electrode that may be smooth or have pointed projections. Traditionally, a gas inlet introduces high vapor pressure monomeric gases into the plasma region wherein radicals are formed so that upon subsequent collisions with the substrate, some of the radicals in the monomers chemically bond or cross link (cure) on the substrate. The high vapor pressure monomeric gases include gases of CH
4
, SiH
4
, C
2
H
6
, C
2
H
2
, or gases generated from high vapor pressure liquid, for example styrene (10 torr at 87.4° F. (30.8° C.)), hexane (100 torr at 60.4° F. (15.8° C.)), tetramethyldisiloxane (10 torr at 82.9° F. (28.3° C.), 1,3-dichlorotetramethyldisiloxane (75 torr at 44.6° F. (7.0° C.)), and combinations thereof that may be evaporated with mild controlled heating. Because these high vapor pressure monomeric gases do not readily cryocondense at ambient or elevated temperatures, deposition rates are low (a few tenths of micrometer/min maximum) relying on radicals chemically bonding to the surface of interest instead of cryocondensation. Remission due to etching of the surface of interest by the plasma competes with reactive deposition. Lower vapor pressure species have not been used in PECVD because heating the higher molecular weight monomers to a temperature sufficient to vaporize them generally causes a reaction prior to vaporization, or metering of the gas becomes difficult to control, either of which is inoperative.
The basic process of flash evaporation is described in U.S. Pat. No. 4,954,371 herein incorporated by reference. This basic process may also be referred to as polymer multi-layer (PML) flash evaporation. Briefly, a radiation polymerizable and/or cross linkable material is supplied at a temperature below a decomposition temperature and polymerization temperature of the material. The material is atomized to droplets having a droplet size ranging from about 1 to about 50 microns. An ultrasonic atomizer is generally used. The droplets are then flash vaporized, under vacuum, by contact with a heated surface above the boiling point of the material, but below the temperature which would cause pyrolysis. The vapor is cryocondensed on a substrate then radiation polymerized or cross linked as a very thin polymer layer.
According to the state of the art of making plasma polymerized films, PECVD and flash evaporation or glow discharge plasma deposition and flash evaporation have not been used in combination. However, plasma treatment of a substrate using a glow discharge plasma generator with inorganic compounds has been used in combination with flash evaporation under a low pressure (vacuum) atmosphere, as reported in J. D. Affinito, M. E. Gross, C. A., Coronado, and P. M. Martin, “Vacuum Deposition Of Polymer Electrolytes On Flexible Substrates,” Proceedings of the Ninth International Conference on Vacuum Web Coating, November 1995, ed. R. Bakish, Bakish Press 1995, pg. 20-36, and as shown in
FIG. 1
a
. In that system, the plasma generator
100
is used to etch the surface
102
of a moving substrate
104
in preparation to receive the monomeric gaseous output from the flash evaporation
106
that cryocondenses on the etched surface
102
and is then passed by a first curing station (not shown), for example electron beam or ultra-violet radiation, to initiate cross linking and curing. The plasma generator
100
has a housing
108
with a gas inlet
110
. The gas may be oxygen, nitrogen, water or an inert gas, for example argon, or combinations thereof. Internally, an electrode
112
that is smooth or having one or more pointed projections
114
produces a glow discharge and makes a plasma with the gas which etches the surface
102
. The flash evaporator
106
has a housing
116
, with a monomer inlet
118
and an atomizing nozzle
120
, for example an ultrasonic atomizer. Flow through the nozzle
120
is atomized into particles or droplets
122
which strike the heated surface
124
whereupon the particles or droplets
122
are flash evaporated into a gas that flows past a series of baffles
126
(optional) to an outlet
128
and cryocondenses on the surface
102
. Although other gas flow distribution arrangements have been used, it has been found that the baffles
126
provide adequate gas flow distribution or uniformity while permitting ease of scaling up to large surfaces
102
. A curing station (not shown) is located downstream of the flash evaporator
106
. The monomer may be an acrylate (
FIG. 1
b
).
These flash evaporation methods have traditionally been used on smooth surfaces or surfaces lacking microtextured features. A disadvantage of traditional PML (polymer multi-layer) flash evaporation methods is that during the time between condensation of the vapor to a liquid film and the radiation cross linking of the liquid film to a solid layer, the liquid tends to flow preferentially to low points and flatter regions because of gravity and surface tension (
FIG. 2
a
) so that the coating surface
150
is geometrically different from the substrate surface
160
. Reducing surface temperature can reduce the flow somewhat, but should the monomer freeze, then cross linking is adversely affected. Using higher viscosity monomers is unattractive because of the increased difficulty of degassing, stirring, and dispensing of the monomer.
Many devices have microtextured surfaces, for

Affiliated with

Also associated with

Rating

Method of making a coating of a microtextured surface does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Method of making a coating of a microtextured surface, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Method of making a coating of a microtextured surface will most certainly appreciate the feedback.

Rate now

Comments { 0 }

Profile ID: LFUS-PAI-O-3288663