Coating processes – Electrical product produced – Fluorescent or phosphorescent base coating
Reexamination Certificate
2001-07-03
2004-09-28
Cleveland, Michael (Department: 1762)
Coating processes
Electrical product produced
Fluorescent or phosphorescent base coating
C427S069000, C427S070000, C264S109000, C264S122000, C264S319000
Reexamination Certificate
active
06797314
ABSTRACT:
FIELD OF THE INVENTION
The present invention relates generally to a method of making an organic light-emitting device (OLED) and particularly to a method of forming solid pellets from powders of organic materials and using such pellets in thermal physical vapor deposition to make an organic layer on a structure which will form part of an OLED.
BACKGROUND OF THE INVENTION
An organic light-emitting device, also referred to as an organic electroluminescent device, can be constructed by sandwiching two or more organic layers between first and second electrodes.
In a passive matrix organic light-emitting device (OLED) of conventional construction, a plurality of laterally spaced light-transmissive anodes, for example indium-tin-oxide (ITO) anodes, are formed as first electrodes on a light-transmissive substrate such as, for example, a glass substrate. Two or more organic layers are then formed successively by vapor deposition of respective organic materials from respective sources, within a chamber held at reduced pressure, typically less than 10
−3
Torr. A plurality of laterally spaced cathodes are deposited as second electrodes over an uppermost one of the organic layers. The cathodes are oriented at an angle, typically at a right angle, with respect to the anodes.
Such conventional passive matrix organic light-emitting devices are operated by applying an electrical potential (also referred to as a drive voltage) between appropriate columns (anodes) and, sequentially, each row (cathode). When a cathode is biased negatively with respect to an anode, light is emitted from a pixel defined by an overlap area of the cathode and the anode, and emitted light reaches an observer through the anode and the substrate.
In an active matrix organic light-emitting device (OLED), an array of anodes are provided as first electrodes by thin-film transistors (TFTs) which are connected to a respective light-transmissive portion. Two or more organic layers are formed successively by vapor deposition in a manner substantially equivalent to the construction of the aforementioned passive matrix device. A common cathode is deposited as a second electrode over an uppermost one of the organic layers. The construction and function of an active matrix organic light-emitting device is described in U.S. Pat. No. 5,550,066, the disclosure of which is herein incorporated by reference.
Organic materials, thicknesses of vapor-deposited organic layers, and layer configurations, useful in constructing an organic light-emitting device, are described, for example, in U.S. Pat. Nos. 4,356,429; 4,539,507; 4,720,432; and 4,769,292, the disclosures of which are herein incorporated by reference.
Organic materials useful in making OLEDs, for example organic hole-transporting materials, organic light-emitting materials predoped with an organic dopant, and organic electron-transporting materials can have relatively complex molecular structures with relatively weak molecular bonding forces, so that care must be taken to avoid decomposition of the organic material(s) during vapor deposition.
The aforementioned organic materials are synthesized to a relatively high degree of purity, and are provided in the form of powders, flakes, or granules. Such powders or flakes have been used heretofore for placement into a thermal physical vapor deposition source for forming a vapor by sublimation or vaporization of the organic material, the vapor condensing on a structure to provide an organic layer thereon.
Several problems have been observed in using organic powders, flakes, or granules in thermal physical vapor deposition:
(i) powders, flakes, or granules are difficult to handle because they can acquire electrostatic charges via a process referred to as triboelectric charging;
(ii) powders, flakes, or granules of organic materials generally have a relatively low physical density (expressed in terms of weight per unit volume) in a range from about 0.05 to about 0.2 g/cm
3
, compared to a physical density of an idealized solid organic material of about 1 g/cm
3
;
(iii) powders, flakes, or granules of organic materials have an undesirably low thermal conductivity, particularly when placed in a vapor deposition source which is disposed in a chamber evacuated to a reduced pressure as low as 10
−6
Torr. Consequently, powder particles, flakes, or granules are heated only by radiative heating from a heated source, and by conductive heating of particles or flakes directly in contact with heated surfaces of the source. Powder particles, flakes, or granules which are not in contact with heated surfaces of the source are not effectively heated by conductive heating due to a relatively low particle-to-particle contact area; and
(iv) powders, flakes, or granules can have a relatively high ratio of surface area/volume of such particles and a correspondingly high propensity to entrain air and/or moisture between particles under ambient conditions. Consequently, a charge of organic powders, flakes, or granules loaded into a vapor deposition source which is disposed in a chamber must be thoroughly outgased by preheating the source once the chamber has been evacuated to a reduced pressure. If outgasing is omitted or is incomplete, particles can be ejected from the source together with a vapor stream during vapor-depositing an organic layer on a structure. An OLED, having multiple organic layers, can be or can become functionally inoperative if such layers include particles or particulates.
Each one, or a combination, of the aforementioned aspects of organic powders, flakes, or granules can lead to nonuniform heating of such organic materials in physical vapor deposition sources with attendant spatially nonuniform sublimation or vaporization of organic material and can, therefore, result in potentially nonuniform vapor-deposited organic layers formed on a structure.
SUMMARY OF THE INVENTION
It is an object of the present invention to provide a method of handling organic material adaptable for making an organic layer on a structure which will form part of an organic light-emitting device (OLED).
It is another object of the present invention to provide a method of agglomerating organic powder into a solid pellet.
It is a further object of the invention to provide a method of making an organic layer from a solid pellet of organic material and on a structure which will form part of an OLED.
It is a still further object of the present invention to provide a method of agglomerating into a solid pellet a mixture of a sublimable organic material powder and a thermally conductive non-sublimable material powder.
In one aspect, the present invention provides a method of handling organic material adaptable for making an organic layer on a structure which will form part of an organic light-emitting device, comprising the steps of:
a) providing the organic material in a powder form;
b) placing such organic powder into a die and applying sufficient pressure to the organic powder in the die to cause the organic powder to agglomerate into a solid pellet; and
c) removing the pellet from the die.
In another aspect, the present invention provides a method of making an organic layer from an organic material on a structure which will form part of an organic light-emitting device (OLED), comprising the steps of:
a) providing the organic material in a powder form;
b) placing such organic powder into a die and applying sufficient pressure to the organic powder in the die to cause the organic powder to agglomerate into a solid pellet;
c) removing the pellet from the die;
d) placing the pellet into a thermal physical vapor deposition source disposed in a chamber;
e) positioning the structure in the chamber and in a spaced relationship with respect to the source;
f) evacuating the chamber to a reduced pressure; and
g) applying heat to the source to cause a portion of the pellet to sublime to provide a vapor of the organic material from which the organic layer is made on the structure.
ADVANTAGES
A feature of the present invention is that the method of agglomerating or
Carlton Donn B.
Chatterjee Dilip K.
Ghosh Syamal K.
Van Slyke Steven A.
Cleveland Michael
Owens Raymond L.
LandOfFree
Method of handling organic material in making an organic... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Method of handling organic material in making an organic..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Method of handling organic material in making an organic... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3203743