Metal fusion bonding – Process – Metal to nonmetal with separate metallic filler
Patent
1997-12-01
1999-10-19
Ryan, Patrick
Metal fusion bonding
Process
Metal to nonmetal with separate metallic filler
228121, 2281221, 2281241, 228190, 228208, 228209, B23P 1704
Patent
active
059674008
ABSTRACT:
The method provides a process for fabricating metal matrix composites. First the process coats the fibers with nickel by electrodeposition or gaseous deposition to form nickel-coated fibers. Over-plating the nickel-coated fibers with aluminum by either electrodeposition in a non-aqueous electrolyte or gaseous deposition forms aluminum-coated-nickel-coated fibers. Sintering this product under compression, perpendicular to the fiber's central axis, forms the final metal matrix composite. The metal matrix composite has a nickel-aluminum matrix, very few voids and extended unbroken lengths of fibers within the nickel-aluminum matrix.
REFERENCES:
patent: 3894677 (1975-07-01), La Iacona
patent: 3918141 (1975-11-01), Pepper et al.
patent: 3953647 (1976-04-01), Brennan et al.
patent: 4489138 (1984-12-01), Yamatsuta et al.
patent: 4761206 (1988-08-01), Forrest
patent: 4831707 (1989-05-01), Goddard et al.
patent: 5326525 (1994-07-01), Ghosh
patent: 5385195 (1995-01-01), Bell et al.
patent: 5501906 (1996-03-01), Deve
Baker et al., "Carbon-fibre/metal-matrix composites: fabrication by electrodeposition," COMPOSITES, (1971) pp. 154-160.
Lamotte et al., "Continuously Cast Aluminum-Carbon Fibre Composites and their Tensile Properties," Journal of Materials Science 7 (1972), pp. 349-349.
Pepper et al., "Mechanical Properties of Aluminum-Graphite Composites Prepared by Liquid Phase Hot Pressing," J. Composite Materials, vol. 8 (1974) pp. 29-36.
Pepper et al., "Development and Evaluation of Aluminum-Graphite Fine Wire and Strip (RIBBON)," U.S. Contract N00024-75-C-5067 (1975).
Pierson, "Aluminum Coatings by the Decomposition of Alkyls," Thin Solid Films, 45 (1977) pp. 257-263.
Ohsaki et al., "The Properties of Carbon Fiber Reinforced Aluminum Composites Formed by the Ion-Plating Process and Vacuum Hot Pressing, " Thin Solid Films, 45(1977) pp. 563-568.
Suzuki et al., "Formation of Al Films on Pitch-base Carbon Fibers from Tri-iso-butyl Aluminum by the Reduced-pressure CVD," Auger elcetron spectroscopy, tensile testing of monofilament, (1986) pp. 577-583.
Sikka et al., "Processing and Mechanical Properties of Ni.sub.3 Al-Based Intermetallic Composites, PLM Aerosp. Def. Technol. Proc.," (1991) pp. 137-145.
Bell et al., "Nickel-Coated Carbon Fiber Preforms for Metal Matrix Composites," 3.sup.rd International SAMPE Metals Processing Conference (1992).
Nishiyama et al., "Fabrication and Mechanical Properties of Cf NiAl and siCw/NiAl Composites," Proc. Jpn. U.S. Conf. Compos. Mater. 6.sup.th (1993) pp. 417-424.
Bell James Alexander Evert
Cushnie Kirt Kenneth
Hansen George Clayton
Warner Anthony Edward Moline
Biederman Blake T.
Inco Limited
Ryan Patrick
Steen Edward A.
Stoner Kiley
LandOfFree
Method of forming metal matrix fiber composites does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Method of forming metal matrix fiber composites, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Method of forming metal matrix fiber composites will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2045888