Method of forming a superconductor

Details Method of forming a superconductor Method of forming a superconductor

1994-11-21

2001-12-04

Garrett, Felisa (Department: 1763)

Superconductor technology: apparatus, material, process

Processes of producing or treating high temperature...

With melting

C117S084000

Reexamination Certificate

active

06326334

ABSTRACT:

BACKGROUND OF THE INVENTION
This invention relates generally to layered perovskite superconductors and, more particularly, to substrates on which layered perovskite superconductors are deposited to form high-frequency electronic devices and circuits.
Materials exhibiting superconductivity at temperatures above the advantageous liquid-nitrogen temperature of 77 K were discovered only recently and have triggered a world-wide explosion in scientific and technological research. The first material to exhibit superconductivity above the temperature of liquid nitrogen was an oxygen-depleted layered perovskite compound of yttrium, barium, copper and oxygen, identified by the formula Y
1
Ba
2
Cu
3
O
7
. Since this discovery, other similar layered perovskite copper oxide compounds, identified by the formula R
1
Ba
2
Cu
3
O
7
, where R is a rare earth element, have also been found to be superconductive at temperatures above the liquid-nitrogen temperature. This particular group of layered perovskite superconductors is commonly referred to as “1-2-3” compounds, because of the number of atoms of each metal element in the copper oxide compound.
Still other layered perovskite copper oxide compounds, with even higher critical temperatures (the temperature at which superconductivity occurs), have been more recently discovered. These newer compounds contain four metallic elements instead of the three metallic elements contained in the “1-2-3” compounds, and they do not contain a rare earth element. In place of the rare earth element, these newer compounds contain metals such as bismuth or thallium.
The major advantage of the layered perovskite superconductors is that superconductive temperatures can be maintained using liquid nitrogen, which is considerably less expensive and troublesome than using liquid helium, as required in the past. Therefore, these superconductors can be expected to find many new applications. One major application already being investigated is integrated circuits, in which thin films of these new superconductors are deposited on substrates to form, for example, Josephson junctions, waveguides and microwave transmission lines. These superconductor circuit elements can be combined to form high-speed, high-frequency and low-power integrated circuits with unparalleled performance.
However, thin films of the layered perovskite superconductors can only be grown with optimal properties on substrates having crystal structures and lattice constants that closely match those of the superconductors. Strontium titanate (SrTiO
3
) is one such material, and is currently being used as a substrate. Unfortunately, strontium titanate is unsuitable at high frequencies because it is very lossy and has an extremely high dielectric constant at superconductive temperatures. Accordingly, there has been a need for a substrate material having good high frequency characteristics and a crystal structure and lattice constant that closely match the crystal structures and lattice constants of the layered perovskite superconductors. The present invention clearly fulfills this need.
SUMMARY OF THE INVENTION
The present invention resides in a substrate of lanthanum aluminate (LaAlO
3
) on which thin films of layered perovskite copper oxide superconductors are formed. Lanthanum aluminate, with a pseudo-cubic perovskite crystal structure, has a crystal structure and lattice constant that closely match the crystal structures and lattice constants of the layered perovskite superconductors. Therefore, it promotes epitaxial film growth of the superconductors, with the crystals being oriented in the proper direction for good superconductive electrical properties, such as a high critical current density. In addition, LaAlO
3
has good high frequency properties, such as a low loss tangent and low dielectric constant at superconductive temperatures. Finally, lanthanum aluminate does not significantly interact with the superconductors. Lanthanum aluminate can also be used to form thin insulating films between the superconductor layers, which allows for the fabrication of a wide variety of superconductor circuit elements.
It will be appreciated from the foregoing that the present invention represents a significant advance in the field of superconductors. Other features and advantages of the present invention will become apparent from the following more detailed description, taken in conjunction with the accompanying drawings, which illustrate, by way of example, the principles of the invention.


REFERENCES:
patent: 4421785 (1983-12-01), Kroger
patent: 4851794 (1989-07-01), Williams et al.
patent: 4962087 (1990-10-01), Belt et al.
patent: 5024894 (1991-06-01), Chien
patent: 5030613 (1991-07-01), Chai
patent: 5126315 (1992-06-01), Nishino et al.
patent: 5159413 (1992-10-01), Calviello et al.
patent: 5256635 (1993-10-01), Sheng et al.
patent: 0345441 (1989-12-01), None
patent: 6417314 (1989-01-01), None
patent: 9001809 (1990-02-01), None
Amoto, “High-TcSuperconductors Get Squeezed,”Science,vol. 261, Oct. 1, 1993, p. 31.
Bednorz, J.G., et al., “Phase Diagram of the (LaAlO3)1-x(SrTio3)xSolid-Solution System, for X≦0.8,”Mat. Res. Bull.,18:181-187 (1983).
Belt, R.F., et al., “Investigation of LaAl1-xScxO3for a Laser Host,”Journal of Crystal Growth,70:471-475 (1984).
Brandle, C.D., “Czochralski Growth of LaAlO3,” Final Report, Union Carbide Corporation (Jul. 29, 1969).
Brown, R., et al., “Low-loss Substrate for Microwave Application of High-temperature Superconductor Films,”Applied Physics Letter,57(13):1351-1353 (1990).
Cava, R.J., et al., “Bulk superconductivity at 36 K in La1.8Sr0.2CuO4,”The American Physical Society, Physical Reviews Letters,58(4):408-410 (Jan. 26, 1987).
Doss, “Engineer's Guide to High Temperature Superconductivity,” Wiley & Sons, 1989, pp. 104-109 and 152-157.
Edelstein, et al., “Formation of the Structure of the Superconducting Phase of La-Sr-Cu-O by DC Sputtering,”J. Crystal Growth,85:619-622 (1987).
Faucher, M., et al., “Optical Study of LaAlO3:Eu at Temperatures Approaching the Rhombohedric → Cubic Transition,”The Journal of Chemical Physics,63(1):446-454 (1975).
Fisk, et al., “Superconductivity of Rare Earth-Barium-Copper Oxides,”Solid State Communications,vol. 62, No. 11, pp. 743-744, 1987.
Fritsche, E.T., et al., “Liquidus in the Alumina-rich System La2O3-Al2O3,”Journal of the American Ceramic Society,50(3):167-168 (1967).
Fulton, T.A., et al., “The Flux Shuttle—A Josephson Junction Shift Register Employing Single Flux Quanta,”Proceedings of the IEEE,61(1):28-35 (1973).
Geballe, “Paths to Higher Temperature Superconductors,”Science,vol. 259, Mar. 12, 1993, pp. 1550-1551.
Geller, S., et al., “Crystallographic Studies of Perovskite-like Compounds. II. Rare Earth Aluminates,”Acta. Cryst.,9:1019-1025 (1956).
Geller, S., “Crystallographic Studies of Perovskite-like Compounds. IV. Rare Earth Scandates, Vanadites, Galliates, Orthochromites,”Acta Cryst.,10:243-248 (1957).
Gulyaev, Yu V., et al., “YBa2Cu3O7-xFilms with a High-temperature Superconductivity Synthesized by Magnetron Sputtering,”Sov. Tech. Phys. Lett.,14(4):339-340 (Apr. 1988).
Gurvitch, M., et al., “Preparation and Substrate Reactions of Superconducting Y-Ba-Cu-O Films,”Appl. Phys. Lett.,51(13):1027-1029 (1987).
Hashimoto, T., et al., “Thermal Expansion Coefficients of High-TcSuperconductors,”Japanese Journal of Applied Physics,27(2):L214-L216 (1988).
Hazen et al., “100-K Superconducting Phases in the Tl-Ca-Ba-Cu-O System,”Physical Review Letters,vol. 60, No. 16, Apr. 18, 1988, pp. 1657-1660.
Höhler, A., et al., “Fully Textured Growth of Y1Ba2Cu3O7-&dgr;Films by Sputtering on LiNbO3Substrates,”Appl Phys. Lett.,54(11):1066-1067 (1989).
Holstein, W.L., et al., “Effect of Single Crystal Substates on the Growth and Properties of Superconducting TI2Ba2CaCu2O8Films,”J. Mater. Res.,8(5):962-972 (May 1993).
Kilner, J.A., et al., “Electrolytes for the High Temperature Fuel Cell; Experimental and Theoretical Studies of the Perovskite LaAlO3,”Journal of Power Sources,3:67-80 (1978).
Koinuma, H., et al., “Chemical Interaction between Ba2

Affiliated with

Also associated with

Rating

Method of forming a superconductor does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Method of forming a superconductor, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Method of forming a superconductor will most certainly appreciate the feedback.

Rate now

Comments { 0 }

Profile ID: LFUS-PAI-O-2576966