Coating processes – Coating by vapor – gas – or smoke
Reexamination Certificate
1999-09-14
2001-07-03
Meeks, Timothy (Department: 1762)
Coating processes
Coating by vapor, gas, or smoke
C427S255180, C117S084000, C117S105000, C118S724000, C118S725000
Reexamination Certificate
active
06254933
ABSTRACT:
BACKGROUND OF THE INVENTION
1. Field of the Invention
The present invention relates to a method of a chemical vapor deposition, where a reactant raw material gas(es) is transported onto a semiconductor crystalline substrate(s) to grow a semiconductor crystalline thin film(s) thereon, and to a reactor therefor.
2. Description of the Prior Art
A horizontal chemical vapor deposition reactor, as shown conceptually in a simplified form in
FIG. 6
is comprised of a cold-wall type reaction chamber
3
being composed of a gas inlet
5
for a reactant raw material gas(es)
4
at one end and a gas outlet
6
at the other end being aligned horizontally and holding a semiconductor crystalline substrate(s)
1
(hereafter simply referred to as a substrate) roughly horizontally in the chamber
3
, and grows a desired semiconductor thin film(s)
2
on the substrate(s)
1
, while the substrate(s)
1
is heated and the reactant raw material gas(es)
4
is flown through the substrate(s)
1
in one direction in the reaction chamber
3
.
In a horizontal reactor for a chemical vapor deposition of the prior art, as shown conceptually in a simplified form as well in
FIG. 7
, which is a front view of the chamber
3
in section shown in
FIG. 6
as seen from the side of the gas inlet
5
, the internal height H of the chamber
3
is so determined as to accommodate a susceptor (not shown) laid on the bottom of the reaction chamber
3
on which a substrate(s)
1
is held and a mechanical driving device for a substrate transportation (both not shown).
With respect to the internal width W of the chamber
3
as shown in
FIG. 7
it is so determined that a proper gap is added to a diameter of a susceptor (not shown) or a diameter D of a substrate(s)
1
thereon for receiving or drawing out.
In a chemical vapor deposition using a traditional type of the reaction chamber
3
designed in. such a manner as described above, when, in particular, a low impurity content semiconductor thin film(s)
2
is grown on a substrate(s)
1
having a high impurity content whose concentration is higher than that of the thin film(s)
2
by at least two figures, a transition width T located at the interface between the substrate
1
and the semiconductor thin film
2
, where the impurity level in the semiconductor thin film
2
changes gradually from the concentration of the substrate
1
to a desired concentration, is unfavorably spread and thus many trials have been carried out to reduce the transition width T.
To find a better condition for minimizing the transition width T, there have to be done a study about the causes of the transition width T. Traditionally two causes have been raised for the formation of the transition width T, which are out-diffusion O in a solid and autodoping A.
The out-diffusion O in a solid is a phenomenon that an impurity diffuses into a semiconductor thin film
2
from a substrate
1
depending on a growth temperature of the semiconductor thin film
2
.
This phenomenon is always dependent on impurity concentration, heating temperature and heating time.
To diminish the phenomenon, one of two ways is chosen, either lowering temperature or shortening heating time.
However, when the heating temperature is lowered in order to suppress the out-diffusion O, automatically affecting to the growth rate to be lowered by itself, the growth rate is required to be reduced further to prevent the surface appearance of a crystalline thin film from roughening.
Under the conditions, the growth time (in other words, the heating time extended to attain a desired thickness of the film) causes not only the enhancement of the out-diffusion in a solid, which reduces the suppression effect of the out-diffusion, but also the reduction of the production efficiency.
On the other hand, the autodoping A is a phenomenon that an impurity moved out from the substrate
1
into the gas phase therearound is incorporated back into the growing surface of a semiconductor crystalline thin film
2
.
This phenomenon is also able to be suppressed by either lowering heating temperature or by shortening heating time.
But, both of the means are not better ways to be adopted, because as same as the case of the out-diffusion O mentioned above, both of the means give only small suppression effect to the autodoping A, and also cause a decrease of the production efficiency by lowering the growth rate.
In company with the recent general trend of increasingly higher integrated electronic devices using the semiconductor single crystalline thin films produced by a gas phase epitaxial deposition, much thinner semiconductor crystalline film has been required, and more recently, there has arose a new requirement that the film thickness is equal to or thinner than the transition width T of generally available in the past.
SUMMARY OF THE INVENTION
It is an object of the present invention to provide a method of a chemical vapor deposition and a reactor therefor, whereby a semiconductor crystalline film having a transition width smaller than that grown by the traditional chemical vapor deposition technique is obtained in the same reaction condition.
The present invention is directed to a method of chemical vapor deposition which is conducted in a cold-wall type reaction chamber that is equipped with a gas inlet for a reactant raw material gas(es) at one end and a gas outlet for a reaction gas at the other end, installed in roughly horizontal, holding a semiconductor substrate(s) in the chamber with a main surface of the substrate aligned in roughly horizontal, flowing a reactant raw material gas(es) in roughly horizontal in one direction, and growing a desired semiconductor crystalline thin film(s) on the heated semiconductor substrate(s),
characterized in that the substrate(s) is arranged in a range of (L+W) from the gas inlet of the reactant raw material gas(es) in the flowing direction and in a location of W/G ratio is 15 or larger, where W indicates an internal width of the reaction chamber, L indicates a distance from the gas inlet of the reactant raw material gas(es) to the leading edge of the substrate located at the most upstream position on the inlet side and G indicates the distance between the main surface of the substrate and a ceiling thereabove.
The present invention is further directed to a method of chemical vapor deposition which is characterized in that the semiconductor substrate(s) is so selected that the diameter thereof is less than the internal width W of the reaction chamber.
The present invention is further directed to a method of chemical vapor deposition which is characterized in that each of the gaps between the semiconductor substrate(s) and the internal side walls is so selected as to be 3 cm or wider.
A reactor for a chemical vapor deposition according to the present invention comprises of a cold-wall type reaction chamber that is equipped with a gas inlet for a reactant raw material gas(es) at one end and a gas outlet for a reaction gas at the other end, installed in roughly horizontal, and a supporting means for a semiconductor substrate(s) being held in the chamber with a main surface of the substrate aligned in roughly horizontal, flowing a reactant raw material gas(es) in roughly horizontal in one direction, and growing a desired semiconductor crystalline thin film(s) on the heated semiconductor substrate(s),
characterized in that the supporting means for the substrate(s) is arranged in a range of (L+W) from the gas inlet of the reactant raw material gas(es) in the flowing direction and in a location of W/G ratio is 15 or larger, where W indicates an internal width of the reaction chamber, L indicates a distance from the gas inlet of the reactant raw material gas(es) to the leading edge of the substrate located at the most upstream position on the gas inlet side and G indicates the distance between the main surface of the substrate and a ceiling thereabove.
The present invention is further directed to a reactor for chemical vapor deposition which is comprised of a cold-wall type reaction chamber that is equipped
Habuka Hitoshi
Katayama Masatake
Mayuzumi Masanori
Tate Naoto
Baker & Daniels
Chen Bret
Meeks Timothy
Shin-Etsu Handotai, Ltd.
LandOfFree
Method of chemical vapor deposition does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Method of chemical vapor deposition, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Method of chemical vapor deposition will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2442794