Plastic and nonmetallic article shaping or treating: processes – Direct application of electrical or wave energy to work – Radio frequency
Reexamination Certificate
1999-12-23
2002-03-19
Theisen, Mary Lynn (Department: 1732)
Plastic and nonmetallic article shaping or treating: processes
Direct application of electrical or wave energy to work
Radio frequency
C264S113000, C264S119000, C264S127000, C264S171260, C264S245000, C264S296000, C264S320000
Reexamination Certificate
active
06358460
ABSTRACT:
BACKGROUND OF THE INVENTION
1. Field of the Invention
The present invention relates generally to tubular sheaths, and more particularly to tubular sheaths used for permitting percutaneus introduction of devices, e.g., a catheter, or the like, into a patient.
2. Background
Introducer sheaths are commonly used by medical personnel for permitting percutaneus insertion of devices such as catheters, or the like, into patients. Introducer sheaths advantageously allow medical personnel to insert such devices into vascular systems of patients without requiring invasive surgical procedures, thereby facilitating the use of such devices and minimizing the recovery time of the patient.
Various design configurations and processes for manufacturing have been used in the production of sheaths for medical applications. For example, in U.S. Pat. No. 4,306,562 (the '562 patent) issued Dec. 22, 1981, to Osborne, a flexible cannula is disclosed. In accordance with that disclosure, the flexible cannula comprises material which tears readily in a longitudinal direction and can thus be easily removed by pulling tabs on opposite sides of the cannula apart after the catheter or other device has been inserted into the body. The '562 patent further discloses that the cannula is disposed about a dilator having a distal end that is tapered for enlarging a puncture site to accommodate the cannula. Similarly, the cannula has a distal end where there is a slight taper to create an appropriately snug fit with the dilator and also to facilitate the enlarging of the puncture site to accommodate the cannula.
Moreover, the '562 patent discloses that the tapered distal end of the cannula is formed by measuring an appropriate length of tubing; applying a heat gun to the tubing; and, upon application of this heat, stretching the tubing, thereby yielding the tapered end. The tip is then cut at a point where the inside diameter of the cannula approximates the outside diameter of the dilator, which will be used with the particular cannula. The '562 patent discloses that the heat-formed tapered end of the cannula serves two purposes. First, it facilitates insertion of the cannula into the body. Second, a tight fit with a probe at this end minimizes blood loss.
In addition, in U.S. Pat. No. 4,581,025 (the '025 patent) issued Apr. 8, 1986, to Timmermans, a sheath is disclosed. In accordance with that disclosure, the sheath comprises a tubular structure formed of a flexible material that is compatible for insertion within the body and having proximal and distal ends. In one embodiment, the tubular structure includes one slit having an open and a closed end. The tubular structure is further comprised of a tab defined by the slit, whereby when the tab is pulled apart from any object extending through the lumen of the tubular structure, the tubular structure tears longitudinally removing the tubular structure from the object. In another embodiment, the tubular structure is cuffed between the closed end of the slit and the distal end of the tubular structure, the cuff defining the proximal end of the tubular structure. The cuff prevents the slit from tearing prematurely and further provides a blunt, smooth open end at the proximal end that permits closure thereof by thumb pressure only in order to temporarily block blood flow or air aspiration during use. The '025 patent further discloses that the distal portion of the sheath is provided with a rounded or tapered tip to ensure a desirably snug fit between a dilator and the sheath and facilitate smooth introduction of the sheath within the body.
Introducer sheaths have traditionally been made of thermoplastic materials, and various processes for manufacturing have been used with such thermoplastic materials. For example, in U.S. Pat. No. 5,139,407 (the '407 patent) issued Aug. 18, 1992, to Kim et al., an apparatus for reducing thermoplastic material compression mold cycle time is disclosed. In accordance with that disclosure, a thermoplastic sheet is placed between a pair of mold members each having a thermal insulator and a mating metal mold insert. Radio frequency (RF) energy is applied to the inserts to dielectrically heat and melt the thermoplastic sheet. The heated sheet is then deformed in a low-pressure press with the insulators. The insulators are then replaced with cool thermally conductive structures to shorten the cooling cycle time. The thermally conductive structures cool the sheet by pressing the sheet in a high-pressure press. The '407 patent further discloses that such thermoplastic materials include TEFLON™ polytetrafluoroethylene (PTFE), which is sold by and a trademark of the E.I. DuPont Co., Inc., Wilmington, Del., USA.
In addition, in U.S. Pat. No. 5,360,330 (the '330 patent) issued Nov. 1, 1994, a RF heated mold for thermoplastic materials is disclosed. In accordance with that disclosure, a source of RF energy is applied to a low thermal inertia heating element with high thermal conductivity, such as a spool, for rapidly heating the heating element to settable predetermined temperature, which temperature is maintained essentially constant. The heating element is detachably attached about the die of a mold for transferring heat to the die to form, mold, weld, or extrude thermoplastic material placed within the mold. Thermal chokes restrict heat transfer from the die to the remainder of the mold. One or more heat sinks draws and dissipates heat from the thermal chokes to maintain cool zones of the mold. Following the heating cycle, upon termination of application of RF energy to the spool, cooling may be accelerated by directing a stream of gas upon the heating element. The '330 patent further discloses a mold for the purpose of tapering an end of a thermoplastic sleeve, which is subsequently disposed about an intravenous catheter and is used for engaging the catheter with a vein of a patient. The tapered end of the thermoplastic sleeve facilitates sliding insertion of the end portion of the sleeve into the vein of the patient.
Although the various design configurations and manufacturing processes described above have been used in the production of introducer sheaths, we have recognized that forming tapered tips at the ends of introducer sheaths continues to be problematic, especially when introducer sheaths are made using preferred PTFE thermoplastic materials such as TEFLON™ PTFE. This is because PTFE thermoplastic materials generally have very high melting temperatures. Further, certain radiopaque substances, which are commonly added to the thermoplastic materials for facilitating x-ray or fluoroscopic visualization of the introducer sheaths, frequently cause discoloration of the introducer sheaths when the tapered tips are formed using heat or RF energy. As a result, processes for forming tapered tips of introducer sheaths that involve either heat or RF energy are often difficult to implement.
As an alternative to using heat or RF energy, tips of introducer sheaths may be tapered using a grinding process. However, introducer sheaths with formed tapered tips are generally regarded as being superior to introducer sheaths with ground tapered tips because the inner diameter of a formed tapered tip typically decreases around a forming mandrel, thereby resulting in an interference fit between the introducer sheath and a dilator disposed therein. This is advantageous when using the introducer sheath during the insertion of devices, e.g., a catheter, or the like, into a patient because there is essentially no gap between the sheath and the dilator that might get hung-up when the sheath and the dilator in combination penetrate the patient's skin or arterial/venous wall.
In contrast, because the inner diameter of a ground tapered tip typically does not decrease during the grinding process, it is very difficult to obtain a useful interference fit between an introducer sheath with a ground tip and a dilator disposed therein. This means that there is often a gap between the ground tip and the dilator that can ge
Hunt, Jr. William E.
Purtell George
Spohn Peter D.
Corless Peter F.
Lisa Swiszcz Hazzard Edwards & Angell, LLP
TFX Medical Incorporation
Theisen Mary Lynn
LandOfFree
Method for tip forming peelable PTFE tubing does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Method for tip forming peelable PTFE tubing, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Method for tip forming peelable PTFE tubing will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2862647