ABSTRACT:
FIELD OF INVENTION
The present invention relates to a process for the manufacture of double-sided and multilayer printed circuit boards and compositions useful in that process. The process contemplates the use of an immersion or electroless silver deposit which serves both as an etch resist and as a final finish solderability preservative. The process also contemplates the use of a specific type of alkaline etchant, which is particularly compatible with the immersion or electroless silver deposit. The proposed process is particularly versatile in reducing the number of steps, variety of chemicals, and waste necessary to produce these circuit boards.
BACKGROUND OF INVENTION
In the manufacture of printed circuit boards, it is now commonplace to produce printed circuitry on one or both sides of a planar rigid or flexible insulating substrate. The manufacture of multi-layer printed circuits, which consist of parallel, planar, alternating inner layers of insulating substrate material and conductive metal is of increased importance. The exposed outer sides of the laminated structure are provided with circuit patterns and any inner layers themselves may contain circuit patterns.
In terms of providing the desired circuit pattern on the board, and any inner layers, the art has developed a variety of manufacturing sequences, many of which fall into the broad categories of subtractive or additive techniques. Common to the subtractive processes is the need to etch away (or subtract) metal to expose the desired circuit patterns.
When utilizing a subtractive technique to form circuit patterns the starting material is typically a copper clad laminate or a multilayer circuit board with copper foil clad to the outer surfaces thereof. In either case, the copper cladding must be imaged in the form of the desired circuit patterns. One method of forming the desired image is to apply a plating mask in the negative (or opposite) image of the desired circuitry pattern. The plating masks used in this regard are typically photo-polymer materials. Once the plating mask is applied in the negative image of the desired circuitry pattern, a metal etch resist is plated onto the exposed copper surfaces (i.e. in the positive image of the desired circuitry pattern) and the plating resist is stripped away. The result is copper cladding with a metal etch resist plated upon it in the pattern of the desired circuitry with the metal etch resist covering select areas of the copper cladding in the image of the desired circuitry and exposed areas of copper cladding in the negative image of the desired circuitry. Typically, metal etch resist materials include tin and tin/lead alloys. The copper clad laminate (or multilayer board) with the metal etch resist on it is then contacted with a copper etchant such that all of the exposed copper surfaces are etched away leaving behind the metal etch resist covered circuitry which are revealed in relief. Upon creation of the circuit pattern as noted above, the etch resist is stripped away revealing the desired copper circuit patterns.
After formation of the circuitry pattern, the printed circuit fabricator is required to arrange that portions of the circuitry generally including through-holes, pads, lands and other points of connection, are receptive to subsequent soldering processes. Soldering is used to electrically and physically connect electronic components and leads to the through-holes, surrounding pads, lands and other points of connection (collectively, “areas of connection”). Thus these areas of connection must be readily wettable by the solder and permit an integral conductive connection with the leads or surfaces of the electronic components. Because of these needs, printed circuit fabricators have devised various methods of preserving and enhancing the solderability of these areas of connection.
One method of arranging good solderability of these surfaces is to plate them with a final finish coating of a precious metal such as gold, palladium, or silver. U.S. Pat. No. 5,235,139 (Bengston, et al.), the teachings of which are incorporated herein by reference, proposes a final finish consisting of a plated layer of nickel followed by a precious metal coating such as gold. In this regard reference is also made to U.S. Pat. No. 4,940,181 (Juskey, Jr. et al.), the teachings of which are incorporated herein by reference in their entirety, were a final finish consists of copper plate followed by nickel followed by gold.
Another method of preserving the solderability of these areas of connection is described in U.S. Pat. No. 5,935,640 (Ferrier, et al.), the teaching of which are incorporated herein by reference in their entirety. Ferrier, et al. proposes a process for preserving and enhancing the solderability of a surface through use of immersion silver deposits. The silver deposits are used alone or in combination with a second deposit of a more noble metal upon the immersion silver deposit.
The invention herein have now found a way to combine the etch resist and the final finish while using a novel copper etchant which is particularly compatible with the combined etch resist/final finish. In doing so, the proposed process and related compositions are particularly versatile in reducing the number of steps, variety of chemicals and waste necessary in producing printed circuit boards.
SUMMARY OF INVENTION
The current invention proposes the use of one immersion silver deposit to serve as both the etch resist and the final finish solderability preservative. The immersion silver dual etch resist/final finish is used in conjunction with a copper etchant which is particularly compatible with the silver material. The proposed copper etchant is a chloride (halide) free alkaline copper etchant preferably in an ammonium hydroxide matrix.
The process proposed is a versatile, efficient, low cost method for effectively combining the etch resist material with the final finish material. The process reduces the number of steps, the variety of chemicals and the costs involved in producing printed circuit boards.
DETAILED DESCRIPTION OF THE INVENTION
It has been discovered that immersion (or electroless) silver deposits are capable of acting as etch resist materials while also providing the function of a final finish solderability preservative, particularly when used in conjunction with an alkaline ammonium hydroxide based, chloride free, copper etchant.
Thus the invention proposes a sequential process for forming printed circuit boards comprising:
1. apply a plating mask to the outer copper surfaces of a copper clad laminate, or a multilayer printed circuit board, such that the plating mask covers only portions of the copper surfaces in the negative image of the circuitry pattern desired, thereby yielding exposed copper surfaces in the positive image of the desired circuitry pattern and plating mask covered copper surfaces in the negative image of the desired circuitry pattern;
2. plating a silver deposit onto the exposed copper surfaces in the positive image of the desired circuitry pattern;
3. stripping the plating mask;
4. contacting the copper clad laminate (or multilayer printed circuit board) with an etchant for copper which is substantially free of chloride and other halide ions and preferably comprises ammonium hydroxide such that the exposed copper areas are etched away leaving the silver coated copper circuitry pattern in relief;
5. optionally, but preferably cleaning the silver surfaces.
As noted, the process of this invention may be utilized in the manufacture of single sided, double sided and/or multilayer printed circuit boards. In the case of single sided printed circuit boards the starting material is a plastic, or paper impregnated with plastic, non-conducting substrate which is clad on one side with copper foil. In the case of a double-sided printed circuit board the non-conducting substrate is clad on both sides with copper foil. In the case of a multilayer printed circuit board, the starting material is a multilayer package of innerlayers which is ultimately clad on the
Letize Raymond
Toscano Lenora
Ahmed Shamim
Carmody & Torrance LLP
LandOfFree
Method for the manufacture of printed circuit boards does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Method for the manufacture of printed circuit boards, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Method for the manufacture of printed circuit boards will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3156100