ABSTRACT:
FIELD OF THE INVENTION
This invention relates to the restoration of concrete slabs, especially with respect to restoring load transfer capability at joints or cracks in concrete slabs.
BACKGROUND OF THE INVENTION
Concrete serves as the primary material for foundations and roadways. Unfortunately, concrete possesses several inherent drawbacks. First, concrete shrinks when it hardens which often results in cracking. Cracks may be controlled by placing joints (pre-planned cracks) in the concrete slab. Further cracks may develop over the life of the slab due to concrete's low tensile strength, shrinkage, and thermal expansions and contractions.
Joints and cracks in concrete are normally the weakest part of a concrete slab. A non-reinforced joint or crack cannot transfer loads from one slab to the next. Concrete pavements with poor load transfer often suffer from faulting at the joint. Joint faulting is a well known type of premature fatigue failure caused by the passage of traffic over transverse joints in concrete roads without sufficient load transfer. Advanced stages of faulting can lead to further cracking, crumbling, and damage of the concrete slab.
Modern pavements reduce the possibility of faulting by improving the sub-base support, including dowels to transfer loads between the slabs at the joints, and sealing the joints. Properly designed joints, along with regular maintenance programs, have made possible the construction of durable, high-quality concrete pavements that will perform well for many years.
Unfortunately, many roads designed in the past and currently used do not contain adequate design features. Many roads did not use dowels. For some of the roads with dowels the dowels have failed. Other roads have cracked under severe or unpredicted use. Many of these roads have developed faulting problems.
Faulting was originally cosmetically repaired with asphalt overlays and diamond grinding. These methods covered up or removed the fault differential, but they did not address the poor load transfers at the joints and cracks. As a result, faulting often reoccurred.
Newer concrete pavement restoration techniques attempt to address the problem of poor load transfer. Highway agencies have tried to retrofit dowels, double-V shear devices, figure-eight devices, and miniature I-beam devices to restore load transfer with some success. The problems with these techniques lie within the implanted devices and the material holding the devices in place. In these techniques, the implanted device transfers the vast majority load across the joint. These devices may fail if they are subject to unpredicted loads or are improperly placed in the encasing medium. Often it is difficult to ensure that the implanted device is properly positioned. Furthermore, many of these devices are made of material which could corrode and fail or, even worse, pose a safety hazard should one come loose. Finally, load transfer devices sometimes do not effectively bond with the material encasing it. Without bonding, the surrounding material cannot help to bear the load across the joint.
The second problem with current load transfer restoration techniques is with the material used to encase the load bearing device. The materials used often cannot effectively bear tensile loads and/or are difficult to handle in the field. Material used to encase load transfer devices include cementitious grout and polymer concretes containing polyesters, epoxy or methacrylate. These materials are designed to match the thermal expansion modulus of concrete, but cannot bear sufficient tensile loads or are not flexible enough to distribute loads throughout the material. Furthermore, these materials are too viscous to flow into narrow slots and cracks in concrete. The primary function of the filler materials is to bond the load-carrying device to the adjacent slabs and to keep the load-carrying device in place. Nothing suggests using filler material to transfer loads across concrete joints. What is needed is an improved method of restoring or improving load transfer across joints in concrete pavement.
SUMMARY OF THE INVENTION
The present invention improves load transfer between two adjoining slabs by cutting a slot perpendicular to the joint between the two slabs, and integrally filling the slot and joint with polymer concrete. The present invention may be performed with other steps, including removing excess material such as filler material, rubble, and dust from the slot and joint after cutting the slot, drying the slot and joint, using aggregate in the slots and joints to improve the characteristics of the polymer concrete, and cutting a joint slot generally along the joint or crack to remove the excess material from the joint slot and fill the joint and slot with polymer concrete.
It is a further object of this invention to improve the load transfer capabilities of the polymer concrete in the slots by placing a joint tie in the slot and encasing it in polymer concrete. The joint tie should extend into the portions of the slots defined by the cuts into the two adjoining slabs. The joint tie may be a fiberglass reinforced plastic tie containing a hole or a pattern of holes or slots through which polymer concrete can flow and interlock with the joint tie.
It is a further object of this invention to locate the slot in areas of normal tire travel where the majority of the load experienced by a road slab is felt.
It is a further object of this invention to use disclosed method for transverse joints, horizontal joints, cracks or any other place in any type of concrete slab that has lost its ability to effectively transfer load over a particular area.
It is a further object of this invention to use a high strength, flexible, and low viscosity polymer concrete to bear the load transfer across a joint. The polymer concrete may contain surfactants with isocyanate reactive sites, low viscosity plasticizers, and polymerization accelerating catalysts.
REFERENCES:
patent: 1223045 (1917-04-01), Ferguson
patent: 3581631 (1971-06-01), Samson
patent: 3849016 (1974-11-01), Cochrane
patent: 3915582 (1975-10-01), Clarke
patent: 4147009 (1979-04-01), Watry
patent: 4353666 (1982-10-01), Brandley
patent: 4453360 (1984-06-01), Barenberg
patent: 4556338 (1985-12-01), Fahey
patent: 4567708 (1986-02-01), Haekkinen
patent: 4630963 (1986-12-01), Wyman
patent: 5464303 (1995-11-01), Wells
patent: 5476340 (1995-12-01), Contrasto
patent: 5492431 (1996-02-01), Rasmussen et al.
patent: 5660498 (1997-08-01), Freeman
patent: 6052964 (2000-04-01), Ferm et al.
patent: 6312541 (2001-11-01), Hemphill
patent: 6354760 (2002-03-01), Boxall et al.
ERES Consultants, Inc. “Techniques for Pavement Rehabilitation,” May 1993, pp. 379-381, Dec. 5, 2000.
Percol Polymerics, Inc., “Percol Concrete Welder™,” USA/Dec. 1996.
Ferm Carl A.
Krauss Paul Donald
Rogalla Ernest Albert
Wyman Ransome J.
Fulbright & Jaworski L.L.P.
Horton Yvonne M.
LandOfFree
Method for restoring load transfer capability does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Method for restoring load transfer capability, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Method for restoring load transfer capability will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3049243