Compositions – Water-softening or purifying or scale-inhibiting agents – Plant or organic material containing
Reexamination Certificate
1997-10-09
2004-09-28
Anthony, Joseph D. (Department: 1714)
Compositions
Water-softening or purifying or scale-inhibiting agents
Plant or organic material containing
C252S175000, C210S710000, C210S719000, C210S721000, C210S725000, C210S727000, C210S912000, C075S416000
Reexamination Certificate
active
06797195
ABSTRACT:
FIELD OF THE INVENTION
The present invention relates generally to a method for removing precious and non-precious metals from hazardous and non-hazardous waste streams, and more particularly to a method for recovering and separating such metals.
BACKGROUND OF THE INVENTION
Treatment and reduction of concentrations of metals in metal bearing industrial waste streams to environmentally acceptable levels has been a long term problem. It is important to be able to treat such wastes and remove metals, hazardous materials, and toxic substances, with minimal amounts of solid wastes remaining in a cost effective manner. The ultimate solution to such environmental problems, recovery, recycling, and reuse of metals contained within waste streams has been inadequately addressed.
In those instances where metals, compounds, and hazardous materials are not separated from waste streams, but are transported to special waste disposal facilities for treatment or storage, the metals are not recovered, leaving them to be disposed of with other unprocessed or partially processed wastes. As a result, not only is there no recycling with the attendant potential for economic profit or cost reduction, but waste disposal and waste storage problems are created as well. Such waste disposal and waste storage problems are associated with high cost and long, waste storage time periods. Often, the wastes generated are considered to be hazardous. Under many environmental statutes, hazardous, toxic, and/or dangerous wastes remain the liability of the waste generator, as long as these wastes exist in the environment. Such long term liability remains with the generator, even though the wastes may have been treated and placed in a secure landfill for disposal.
Processes for removing metals from waste streams including ion exchange and electrolysis have heretofore been known, but theses process are limited. Ion exchange is costly, slow, and cumbersome to use, and in order to be effective, the waste water being treated must be passed through a significant amount of ion-exchange resin, usually in the form of a filter bed, making it effective, in most cases, for only treating small volumes of waste water. The complex fabrication process and sophisticated synthetic chemistry required by ion exchange metal recovery technology significantly contributes to the expense of its use to purify liquid waste streams. The cost and complexity of ion exchange also limits the variety of resins available.
Although ion exchange resin beds may be regenerated, the waste waters from regeneration must often be retreated to remove bulk contaminats and then usually passed through the ion exchange resin again to eliminate hazardous materials. Thus, ion exchange is a cumbersome process, and therefore impractical, especially for large volumes of waste water in a continuous-treatment process, as compared to using ion-exchange in a batch-treatment process.
Electrolysis is also expensive, requires significant maintenance, employs other resources, may create its own waste disposal problems, and is energy intensive. Electrolytic recovery is, at best, 70%-80% efficient. Besides, the electrolyte systems available today are very sensitive to the presence of contaminants.
Use of either ion exchange or electrolytic recovery of metals from waste streams requires separation of streams for processing, thereby ultimately creating multiple waste streams. This multiplicity of streams results in a costly waste removal process for the waste stream generator.
In contrast to the ion exchange and electrolytic metal recovery processes, one of the more acceptable technologies for treating waste water is based on a settling process, using fixating agents such as hydroxide and sulfates. The fixating chemicals are added to water in a settling tank to absorb or otherwise transform the contaminants into materials which settle to the bottom of the tank. This technology uses comparatively simple equipment and permits the processing of large volumes of waste waters, without adding materials which would result in an environmentally undesirable effluent stream. However, in many cases, use of ordinary settling processes fails to reduce contaminant concentrations to levels low enough to meet the statutory requirements, without using excessive amounts of materials, over a protracted processing time. Current settling processes often produce undesirably large quantities of solid hazardous or toxic wastes in the form of sludge. The sludge cannot, for the most part, be effectively regenerated. Thus, using current settling techniques for waste water treatment, the resulting sludge product is yet another waste material that must be disposed of in a secure landfill without benefit of recycling. In turn, this process results ultimately in the necessity to clean the environment in the long term future.
As a result of problems associated with the above noted technologies, waste water generators have been forced to consider alternative methods which employ the addition of metal complexing agents to waste water streams and sludge of various industrial processes.
For example, U.S. Pat. No. 3,966,601 (Stevenson, et al.) discloses a purification process comprised of mixing a soluble heavy metal salt and a heavy metal dithiocarbamate. U.S. Pat. No. 4,387,034 (Unger, et al.) discloses a collector for use in concentrating metal values in ores by flotation, the collector being comprised of a mixture of 0-isopropyl N-ethylthionocarbamate and o-isobutyl N-methylthionocarbamate.
U.S. Pat. No. 4,578,195 (Moore, et al.) discloses a process for treating aqueous effluents to remove polluting metallic elements wherein the effluent is contacted with a poly(dithiocarbamate) chelating agent. U.S. Pat. No. 4,612,125 (Elfline) discloses a method for removing heavy metals from waste water streams, comprising treating the waste water with sulfur-containing compounds, such as sodium tri-thiocarbamate.
U.S. Pat. No. 4,678,584 (Elfline) discloses a method for treating a liquid containing a heavy metal comprising contacting the liquid with a mixture of sodium diethyldithiocarbamate and sodium tri-thiocarbanate. U.S. Pat. No. 4,943,377 (Legare) discloses a method for removing heavy metals from waste effluents comprising mixing the effluents with a solution of a sulfur compound such as sodium polythiocarbamate. U.S. Pat. No. 5,372,726 (Straten) discloses a method for treating water polluted by metal ions comprising the steps of adding thiocarbamide, potassium or sodium hydroxide, and potassium or sodium hyposulfite.
U.S. Pat. No. 5,264,135 (Mohn) discloses a method for treating sludge from industrial waste water streams comprising the steps of adding a metal complexing agent to the sludge such as dimethyl-dithiocarbamate or a salt thereof. The metal complexing agent is added to a sludge thickening tank prior to de-watering in a filter press to form a sludge that contains 60% to 85% moisture by weight. Mohn does not disclose use source separation of the effluent throughout the process and does not disclose adjusting the pH of the waste solution to the optimal point of insolubility for the various metals involved. Mohn characterizes the sludge as being fixated, thereby allowing disposal in landfills.
In addition, a number of metallurgical processes for recovering metal have also been disclosed. For example, U.S. Pat. No. 3,899,322 (Yosim et al.) discloses a process for recovery of noble metals from scrap comprising melting the scrap at a temperature between 800° F. and 1,800° F. U.S. Pat. No. 4,135,923 (Day) discloses a process for the extraction of metals from metallic materials comprising heating a lead-free mixture of metals and separating the metals in a molten state.
U.S. Pat. No. 5,008,017 (Kiehl, et al.) discloses a process for recovering metals from waste liquids, including a step for obtaining pure metal. A dewatered sludge is heated for a period from about thirty minutes to about one hour at 900° F., to recover substantially pure silver. However, this metallurgical process for recovering metals from a metalli
LandOfFree
Method for recovering and separating metals from waste streams does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Method for recovering and separating metals from waste streams, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Method for recovering and separating metals from waste streams will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3201967