Specialized metallurgical processes – compositions for use therei – Compositions – Loose particulate mixture containing metal particles
Reexamination Certificate
2000-10-06
2002-06-25
Jenkins, Daniel J. (Department: 1742)
Specialized metallurgical processes, compositions for use therei
Compositions
Loose particulate mixture containing metal particles
C075S228000, C419S030000, C419S035000, C419S064000, C148S513000, C428S402000
Reexamination Certificate
active
06409796
ABSTRACT:
FIELD OF THE INVENTION
This invention is generally in the field of physical-chemical treatment, and relates to a method of obtaining tantalum, niobium or tantalum-niobium powders with a highly developed surface. The invention is particularly useful for manufacturing electrolytic capacitors.
BACKGROUND OF THE INVENTION
Capacitors serve for storing an electrical charge for a later use. Electrolytic capacitors are typically manufactured from aluminum or tantalum powder. Tantalum and niobium (as well as tantalum-niobium) capacitors have become the preferred type, due to their relatively high reliability, long service life, and high capacitance and voltage ranges at relatively small dimensions, as compared to the aluminum ones. More specifically, tantalum capacitors have as much as three times better capacitance/volume efficiency than the aluminum capacitors.
Generally, a capacitor is formed by two spaced-apart conducting surfaces (usually metal plates) serving as electrodes, and the space between them is filled with an insulating or dielectric material. The dielectric used in tantalum capacitors is tantalum pentoxide that possesses high dielectric strength and a high dielectric constant. As capacitors are being manufactured, a film of tantalum pentoxide is applied to the electrodes by means of an electrolytic process.
The capacitance, C, of a capacitor is determined by the surface area of the two electrodes, the distance therebetween and dielectric constant of the insulating material, that is
C
=
ϵ
·
A
t
wherein &egr; is the dielectric constant, A is the surface area; and t is the distance between the electrodes.
In tantalum electrolytic capacitors, the distance between the electrodes is very small, since it is only the thickness of the tantalum pentoxide film. As the dielectric constant of the tantalum pentoxide is extremely high (&egr;≈26), the capacitance of the tantalum capacitor is also very high and can be increased even more, if the surface area of the electrodes is increased.
Tantalum capacitors contain either liquid electrolytes (sulfuric acid) or solid electrolytes forming the cathode electrode, while the anode is formed by the tantalum pellet provided with a lead wire embedded in or welded to the pellet. This anode has an enormous surface area for its size because of the way it is made. The entire construction is enclosed in a hermetically sealed case.
The above construction, utilizing for example a liquid electrolyte, is typically manufactured in the following manner. Tantalum powder of suitable fineness, typically 2-5 &mgr;m, (sometimes mixed with a binding agent) is machine-pressed into pellets. The next step is a sintering operation in which binders, impurities and contaminants are vaporized, and the tantalum particles are sintered (welded) into a porous mass with a very large internal surface area. During this step, metallic links and electrical contacts between tantalum particles are created. In addition, a tantalum wire is introduced into the powder prior to sintering so as to form a contact of the future anode. In some cases, the lead is embedded during pressing of the pellet before sintering. A film of tantalum pentoxide is electrochemically formed on the surface area of the fused tantalum particles. Provided that sufficient time and current are available, the oxide will grow to a thickness determined by the applied voltage. The pellet is then inserted into a tantalum or silver can, which contains an electrolyte solution. Most liquid electrolytes are gelled to prevent the free movement of the solution inside the container and to keep the electrolyte in intimate contact with the capacitor cathode. A suitable end-seal arrangement prevents the loss of the electrolyte.
As to the solid electrolyte based tantalum capacitors, the electrolyte is usually a manganese dioxide formed on a tantalum pentoxide dielectric layer. This construction is manufactured by impregnating the pellet with a solution of manganous nitrate, and then heating the pellets in an oven, thereby converting the manganous nitrate into manganese dioxide. The pellet is next coated and sealed.
The tantalum capacitor can be either of a volume or of a foil type, in which case the anode is formed by a tantalum foil.
Various techniques for the manufacture of tantalum powders have been developed. They typically include the following stages:
dissolving the ore;
extraction and precipitation of tantalum hydroxide;
calcination of tantalum hydroxide and conversing it into tantalum pentoxide; and
reduction of the pentoxide into tantalum metal powder, e.g., with sodium vapor.
It is understood that the capacitance of a tantalum capacitor depends on the total surface area of a tantalum powder used in the manufacture of this capacitor. The larger the total surface area, the larger the capacitance. The total surface area of the tantalum powder can be increased either by decreasing the particles' size, or by developing their surface area. However, the decrease of the particles' size is limited to that (0.5.-1.0 &mgr;m) required for providing electrical contact between the particles. When lowering the particle size, the possibility of contact breaking significantly increases. The reduction in particle size also suffers from the unavoidable requirement of high-energy treatment that is very complicated and expensive.
The surface developing techniques include the production of flakes or fragmentation-like powders with the particle size of 2÷50 &mgr;m. Known techniques of surface development allow for achieving a roughness factor not exceeding 2. Maximal surface area of the tantalum powder that is obtainable by the conventional techniques is about 0.1-0.5 m
2
/g (BET).
Techniques aimed at increasing the surface area of a tantalum powder have been developed, and are disclosed, for example, in U.S. Pat. Nos. 5,261,942; 5,580,367 and 5,211,741. According to this technique, the BET surface area of a tantalum powder is developed up to 0.6 m
2
/g by producing a flaked tantalum and reducing the flake size by fracturing without substantially reducing the thickness or tapering the peripheral edges of the flakes. This is implemented by embrittling the conventional tantalum flake by hydriding, oxidizing, cooling to low temperatures or the like to enhance breakage when reducing flake particle size by mechanical means. Thereafter, the so treated tantalum powder is treated by mechanical means such as a vibratory ball mill, and then an additional temperature treatment is applied to the mechanically treated tantalum powder.
Further increase of the surface area of tantalum powder is desired. This, on the one hand, would allow miniaturization of electronic devices utilizing tantalum capacitors, and, on the other hand, would enable to obtain the same operational parameters of the capacitor whilst saving such an expensive raw material as tantalum.
SUMMARY OF THE INVENTION
There is accordingly a need in the art for a technique enabling to increase the surface area of a tantalum, niobium or tantalum-niobium powder.
The present invention takes advantage of the use of the principles of a mechanical alloying technique for developing the surface area of a selected metal powder obtained by any known technique.
The term “selected metal” used herein signifies a metal selected from a group consisting of tantalum, niobium, and mixtures thereof with the tantalum
iobium composition ratio (Ta:Nb) ranging between 1:9 and 9:1.
The main idea of the present invention is based on the following. The mechanical alloying technique generally consists of alloying powders of different metals without resorting to external heating or chemical processing. The present invention utilizes equipment commonly used in mechanical alloying processes, such as different mills, attritors, grinders, but uses a specific operational mode and specific additional powders to obtain a solid solution in which the selected metal particles are at least partly wetted with the additional powder. This additional powder is preferably a metal, such as Fe
Advanced Alloy Technologies, Ltd.
Jenkins Daniel J.
LandOfFree
Method for production of tantalum and niobium powders with... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Method for production of tantalum and niobium powders with..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Method for production of tantalum and niobium powders with... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2983372