Powder metallurgy processes – Powder metallurgy processes with heating or sintering – Sintering which includes a chemical reaction
Patent
1994-08-17
1995-09-26
Nelson, Peter A.
Powder metallurgy processes
Powder metallurgy processes with heating or sintering
Sintering which includes a chemical reaction
419 25, 419 38, 419 43, 419 46, 419 56, B22F 700, B22F 704
Patent
active
054532434
ABSTRACT:
A process for producing titanium aluminide weld rod comprising: attaching one end of a metal tube to a vacuum line; placing a means between said vacuum line and a junction of the metal tube to prevent powder from entering the vacuum line; inducing a vacuum within the tube; placing a mixture of titanium and aluminum powder in the tube and employing means to impact the powder in the tube to a filled tube; heating the tube in the vacuum at a temperature sufficient to initiate a high-temperature synthesis (SHS) reaction between the titanium and aluminum; and lowering the temperature to ambient temperature to obtain a intermetallic titanium aluminide alloy weld rod.
REFERENCES:
patent: 4909842 (1990-03-01), Dunmead et al.
patent: 4915903 (1990-04-01), Brupbacher et al.
patent: 4985202 (1991-01-01), Moshier et al.
patent: 5198188 (1993-03-01), Holt et al.
patent: 5256368 (1993-10-01), Oden et al.
patent: 5342572 (1994-08-01), Stangle et al.
Argetsinger Edward R.
Hansen Jeffrey S.
Turner Paul C.
Bluni Scott T.
Nelson Peter A.
The United States of America as represented by the Secretary of
LandOfFree
Method for producing titanium aluminide weld rod does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Method for producing titanium aluminide weld rod, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Method for producing titanium aluminide weld rod will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-1550834