Method for producing sliders

Details Method for producing sliders Method for producing sliders

2000-10-19

2002-08-06

Gulakowski, Randy (Department: 1746)

Etching a substrate: processes

Forming or treating article containing magnetically...

C216S101000, C216S102000, C134S002000, C252S079100

Reexamination Certificate

active

06428715

ABSTRACT:

BACKGROUND OF THE INVENTION
1. Field of the Invention
The present invention relates to an improved method for manufacturing sliders. More particularly, the invention relates to an improved method for removing unwanted alumina from the alumina overcoat on a slider.
2. Description of the Background Art
Digital magnetic recording devices for data storage generally comprise a thin film magnetic recording disk and a head or transducer which is moved above the surface of the rotating disk to electromagnetically read and write information on the disk. Advanced thin film magnetic recording disks generally comprise a rigid substrate, a magnetic layer such as a cobalt-based metal alloy, a protective amorphous carbon layer and a lubricant layer, such as a perfluoropolyether disposed on the carbon overcoat.
During operation of the disk drive system, an actuator mechanism moves the magnetic transducer to a desired radial position on the surface of the rotating disk where the head electromagnetically reads or writes data. Usually, the head is integrally mounted in a carrier or support referred to as a “slider”. The slider is generally rectangular in shape and consists of two portions, i.e., a slider portion and a head portion formed on an end face of the slider portion. Typically, this end face of the slider will constitute the slider trailing edge when the slider is suspended adjacent to a rotating recording disk.
The slider portion, which constitutes the bulk of the thin film head slider, is made of a ceramic material such as Al
2
O
3
—TiC or another suitable material. The head portion of the slider typically is a thin layer of alumina formed on the trailing edge face of the slider portion in which the magnetic portion of the head is embedded.
A slider generally serves to mechanically support the head and any electrical connections between the head and the rest of the disk drive system. The slider is aerodynamically shaped to glide over moving air in order to maintain a uniform distance from the surface of the rotating disk, thereby preventing the head from undesirably contacting the disk.
Typically, a slider is formed with an aerodynamic pattern of protrusions (air bearing design) on its air bearing surface (ABS) which enable the slider to fly at a constant height close to the disk during operation of the disk drive.
The recording density of a magnetic disk drive is dependent on the distance between a transducer and the magnetic media. One goal of air bearing slider design is to “fly” a slider as closely as possible to a magnetic medium while avoiding physical impact with the medium. Smaller spacings, or “fly heights”, are desired so that the transducer can distinguish between the varying magnetic fields emanating from closely spaced regions on the disk.
However, the benefit of a closer spacing is constrained by the adverse effect on the mechanical reliability. As the distance between the slider and the disk decreases, as it does with every generation of storage device, the probability of contact between the two increase which causes wear on both contacting surfaces that could ultimately lead to loss of data.
The point on the slider that has the highest probability of coming in contact with the disk is the alumina overcoat on the trailing surface because sliders fly with a positive pitch. The probability of contact between the slider and disk increase when the alumina on the trailing edge protrudes above the air bearing surface of the slider. Referring to
FIG. 1
, there is shown a slider
10
comprising slider portion
12
and head portion
14
together forming the air bearing surface
16
of the slider. The head portion
14
of the slider comprises an alumina undercoat
20
, read and write head elements
22
,
24
and
26
, and the alumina overcoat
28
. Referring to
FIG. 2
, there is shown an alumina overcoat
28
of slider
10
protruding above the ABS surface of slider portion
12
, thereby substantially increasing the probability of contact with the disk. Protrusion of the overcoat of alumina can result from (i) lapping of the air bearing surface (ABS) or (ii) from operation of the slider. During operation of the slider, there is an increase in the temperature of the slider and the differences in coefficient of thermal expansion of the slider components can result in protrusion of the alumina overcoat.
In the manufacturing of sliders, a large number of sliders are fabricated from a single wafer having rows of the magnetic transducers deposited simultaneously on the wafer surface using semiconductor-type process methods. In one process embodiment, after deposition of the heads is complete, the wafer is cut into four quadrants. Each quadrant is then bonded to a lapping fixture and lapped on a lapping plate to provide accurate head dimensions. After lapping, single row bars of sliders are cut from the wafer quadrant. These row bars may then be lapped again on the ABS, and the ABS design is etched in each slider using art-known lithographic techniques. Lastly, the row bars are adhered to suitable tape; and each bar is diced, i.e., separated with a diamond-cut saw into individual sliders, each having a magnetic head terminating at the ABS. Each slider is then cleanly removed from the tape, inspected to insure operability of the magnetic head, and attached to an actuator for use in a magnetic disk drive.
Unfortunately, as discussed above, the lapping process can result in an alumina overcoat protrusion which will increase the probability of contact between the disk and slider. Therefore, there still is a need in the art for a slider manufacturing process which results in sliders without alumina overcoat protrusion.
It is, therefore, an object of the present invention to provide an improved method for the manufacturing of magnetic sliders. Other objects and advantages will become apparent from the following disclosure.
SUMMARY OF THE INVENTION
The present invention relates to a method for producing magnetic sliders without alumina overcoat protrusion. After lapping of the ABS of the slider, the method of the present invention involves contacting the trailing alumina (ABS) surface of the slider with an aqueous base solution having a pH of about 9 to about 13, preferably about 10 to about 11. Preferably the base solution is buffered. Preferably the solution is aqueous potassium carbonate/bicarbonate. The method of the present invention can be practiced without the need for any masking of the ABS surface to protect the surface, e.g. patterned portions of the surface.
A more thorough disclosure of the present invention is presented in the detailed description which follows and the accompanying figures.


REFERENCES:
patent: 3653095 (1972-04-01), Dupre et al.
patent: 4048121 (1977-09-01), Chang
patent: 4091954 (1978-05-01), Wallace
patent: 4124407 (1978-11-01), Binns
patent: 4301353 (1981-11-01), Suenaga et al.
patent: 4317685 (1982-03-01), Ahuja et al.
patent: 4349448 (1982-09-01), Steele
patent: 4457322 (1984-07-01), Rubin et al.
patent: 4477290 (1984-10-01), Carroll et al.
patent: 4564585 (1986-01-01), Blaske et al.
patent: 4599116 (1986-07-01), King et al.
patent: 4619731 (1986-10-01), Buttry et al.
patent: 4787942 (1988-11-01), Wray
patent: 4894740 (1990-01-01), Chhabra et al.
patent: 4912883 (1990-04-01), Chang et al.
patent: 4914868 (1990-04-01), Church et al.
patent: 4940493 (1990-07-01), Neidffer et al.
patent: 5203119 (1993-04-01), Cole
patent: 5335458 (1994-08-01), Stoffers et al.
patent: 5462636 (1995-10-01), Chen et al.
patent: 5567333 (1996-10-01), Hira et al.
patent: 5650893 (1997-07-01), Bolasna et al.
patent: 5665251 (1997-09-01), Robertson et al.
patent: 5687045 (1997-11-01), Okai et al.
patent: 5835315 (1998-11-01), Cohen et al.
patent: 5872684 (1999-02-01), Hadfield et al.
patent: 5910864 (1999-06-01), Hira et al.
patent: 6051148 (2000-04-01), Perry et al.
patent: 6069770 (2000-05-01), Cui et al.
patent: 6190237 (2001-02-01), Huynh et al.
patent: 6322687 (2001-11-01), Heimann et al.

Affiliated with

Also associated with

Rating

Method for producing sliders does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Method for producing sliders, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Method for producing sliders will most certainly appreciate the feedback.

Rate now

Comments { 0 }

Profile ID: LFUS-PAI-O-2966476