Specialized metallurgical processes – compositions for use therei – Processes – Producing or treating free metal
Reexamination Certificate
2001-04-10
2003-08-05
Andrews, Melvyn (Department: 1742)
Specialized metallurgical processes, compositions for use therei
Processes
Producing or treating free metal
C075S500000, C075S504000
Reexamination Certificate
active
06602320
ABSTRACT:
BACKGROUND OF THE INVENTION
1. Field of the Invention
This invention relates to a method for producing reduced iron by heat-reducing an iron oxide such as iron ore with a carbonaceous reducing agent such as coke to obtain solid reduced iron, or further heating it, thereby separating a slag forming component as slag from the metallic iron to obtain granular metallic iron.
2. Description of the Background
As methods for producing reduced iron similar to this invention, it is known to pelletize raw material powders containing an iron oxide source such as iron ore and coke, and charge the raw material agglomerate into a heat reduction furnace as it is in an undried state to heat-reduce the green pellets, thereby successively performing the drying and heat reduction to produce reduced iron. Although this method has the advantage that the equipment or time required for drying the raw material agglomerates can be omitted, it requires a preheating zone serving also as drying zone before the heat reduction area, resulting in the inevitable enlargement of the whole furnace. It further requires the preparation of a shielding member such as curtain wall in order to obstruct the flow of a high-temperature gas from the heat reduction zone toward the preheating zone, and the structure of the furnace is consequently complicated, leading to the problem of an increase in equipment cost.
It is also known to enhance the heating efficiency by shaping the raw material layer charged on the hearth into ridges to extend the surface area of the raw material layer. In this method, however, the rate of heat transfer of burner heat or radiation heat into pellets is low even in raw material pellets having middle to large particle sizes of 10-20 mm, the pellets are barely stacked in several layers for all the formation of ridges, and a sufficient heat transfer effect cannot be necessarily obtained. It is further known to enhance the heating efficiency by plowing up the ridges in the middle of the heat reduction. However, the plowing up of the laminated part of the middle to large particle size pellets causes the breakage of the pellets, resulting in a reduction in yield of reduced iron.
Further, it is also proposed to supply the raw material powders onto the hearth while forming irregularities. However, the heat transfer property or reduction reactivity of this method is rather inferior, compared with the use of the agglomerate because the maximum accumulation thickness of the raw material is large, and the iron oxide source and the carbonaceous material of the raw material powders are only mixed together but not so closely in contact to each other.
In these methods, the raw material mixture is generally molded into a agglomerate having a diameter of about 10 mm or more, and it is supplied onto the hearth of a heat reduction furnace and heat-reduced. Since the raw material agglomerate having such a large diameter is apt to rupture by the influence of the moisture or volatile component contained therein when exposed to a high temperature of about 1300° C. or higher for efficiently progressing the reduction reaction. In most cases, therefore, the raw material agglomerate is preliminarily heated and then charged into the heat reduction furnace.
Further, the large size raw material agglomerate is generally difficult to pelletize, resulting in not only an increase in the cost required for pelletizing equipment or drying equipment but also an increase in the production cost. A binder is used in order to stably retain the shape after drying. However, an excessively large mixing quantity of the binder tends to hinder the uniform dispersion of the iron oxide source and carbonaceous material in the agglomerate and also causes the fear of affecting the efficiency of the heat reduction reaction. It is also proposed to omit the drying and supply the agglomerate to the heat reduction furnace in a green pellet state. However, this method cannot be said to be practically applicable in industrial scale because the green pellet is not only low in strength but also apt to cause a clogging by the mutual adhesion of the pellets or the adhesion to the hopper of a feeder with poor handling property.
The reduced iron obtained by the method as described above has a low Fe purity because a large quantity of the slag component included as gangue component in the raw material iron ore is contained therein, and requires the process for removing the slag component in the following refining treatment process. Further, the reduced iron obtained by this method is lacking in handling property in the merchandising as iron source because it is spongy and easy to break. To improve such a disadvantage, the spongy reduced iron must be worked into a briquette-like compact, which requires an extra apparatus.
Therefore, it is proposed to melt the metallic iron produced successively to the heat reduction of the reduced iron and coagulate the molten metallic iron while separating from the by-produced slag component to obtain granular metallic iron. However, a sufficient examination has not be necessarily performed in this method for how efficiently granular metallic iron is produced, taking into account the size or the like of the raw material agglomerate.
SUMMARY OF THE INVENTION
This invention has an object to provide a method capable of stably and efficiently performing the agglomerating of a raw material, the drying and heat reduction, and further the melting and coagulating by properly setting, particularly, the size or number of layers of raw material small agglomerates in the production of solid reduced iron (granular metallic iron, reduced iron containing slag) from a raw material containing an iron oxide source and a carbonaceous reducing agent.
Namely, a method for producing reduced iron according to this invention comprises agglomerating a raw material mixture containing a carbonaceous reducing agent and an iron oxide containing material into small agglomerates, charging the small agglomerates into a reduction furnace, and heating the small agglomerates in the reduction furnace, thereby solid reducing the iron oxide in the small agglomerates to produce solid reduced iron.
In the above method for producing reduced iron, the small agglomerates are mainly composed of those having particle sizes of less than 6 mm, or particle sizes of 3 mm or more and less than 6 mm, and the small agglomerates are charged in 2-5 layers depth.
In the above method for producing reduced iron, the small agglomerates are mainly composed of those having particle sizes of less than 3 mm, and the small agglomerates are charged onto the hearth of the reduction furnace in 3 layers depth or more.
In the above method for producing reduced iron, the small agglomerates are mainly composed of those having particle sizes of 3-7 mm, and the small agglomerates are charged onto the hearth of the reduction furnace so as to mutually overlap in a thickness of 10-30 mm.
In the above method for producing reduced iron, the small agglomerates are leveled so as to have 3-5 layers depth.
In the above method for producing reduced iron, the small agglomerates are charged into the reduction furnace without drying, the small agglomerates are charged onto the hearth after drying at least the surface thereof, mountain parts and valley parts are formed on the surface of the small mass layer charged on the hearth of the reduction furnace, the small agglomerates are charged after a powdery carbonaceous material is laid over the hearth of the reduction furnace, or the small agglomerates are charged onto the hearth with the carbonaceous material being adhered to the surface thereof.
According to this, the small agglomerates are used as the raw material, whereby the agglomerating of the raw material, the drying and heat reduction and further the melting can be stably and efficiently performed. The preferable particle size is 3-7 mm or less than 6 mm, but the particle sizes of the small agglomerates are more preferably set to 3 mm or more and less than 6 mm. In this case, the small agglomerates are
Fuji Kojiro
Kikuchi Shoichi
Kitajima Takaya
Tanaka Hidetoshi
Tsuchiya Osamu
Andrews Melvyn
Kabushiki Kaisha Kobe Seiko Sho (Kobe Steel Ltd).
LandOfFree
Method for producing reduced iron does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Method for producing reduced iron, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Method for producing reduced iron will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3107423