ABSTRACT:
The invention relates to a method for producing moulded bodies from a matrix of a reactive plastics material, in particular polyurethane, with coarse-grained filler, such as gravel, quarry material, slag, comminuted rubble, foam concrete, plastics waste or similar, enclosed therein.
A proposal which has already been made for the production of synthetic stone blocks lies in mixing pieces of stone with an organic binder in a mixing device under vacuum and then, following compaction, pressing them into blocks in a vacuum mould through vibration (DE-A 35 22 910). Reactive plastics materials, in particular those with a high reaction rate, cannot be used as binders in a method of this kind, as the reaction would start while mixing the binder with the pieces of stone.
WO 91/18725 has proposed firstly feeding the filler into the mould and introducing the reactive mixture into the closed mould by means of hoses, which are withdrawn from the mould as the cavities remaining in the latter are filled. According to U.S. Pat. No. 5,328,648, bonding elements for concrete-encased steel pipes are produced by this method. In this case the steel pipes have non-encased ends which are welded together. The weld is then surrounded by a sleeve into which the feed hoses for the binder and gravel used as the filler are inserted. A reactive polyurethane mixture is subsequently fed in through the hoses, which are removed from the sleeve as the cavities between the filler are filled with reactive mixture. One disadvantage of this method lies in the fact that the feed hoses for the reactive mixture which are to be removed leave cavities which cause the binder to be inhomogeneously distributed, at least in the area where the hoses were originally located. Another disadvantage lies in the fact that the age of the binder in the moulded body is distributed over the geometry of the latter. When using quick-reacting reactive plastics materials, the part of the moulded body which is firstly filled with binder will already have solidified when the last part of the mould is filled with binder. This causes inhomogeneous forces within the moulded body which may lead to burning or even fracture. In order to counter this, U.S. Pat. No. 5,328,648 proposes extending the binder by substantial quantities of plasticizer, such as organic carbonates.
It has now been found that moulded bodies based on quick-reacting reactive plastics materials and having a high proportion of coarse-grained filler can easily be produced if the filler is at a temperature of 60 to 80° C., which accelerates the setting of the binder, while the latter is being fed into the mould.
The present invention accordingly provides a method for producing reactive plastics moulded bodies with a high proportion of coarse-grained filler which is characterised in that the filler is heated to a temperature of 60 to 80° C., the filler is then fed into the mould and possibly compacted, and the reactive plastics mixture is then introduced into the mould. The reactive plastics mixture is preferably introduced from the bottom of the mould. It is particularly preferable for the reactive plastics mixture to be produced in a countercurrent high-pressure mixing chamber just before being introduced into the mould. The temperature of the reactive plastics mixture may lie between 10 and 30° C., in particular at ambient temperature.
Moulded bodies which are substantially stress-free are obtained according to the invention. This is due to the fact that the reactive plastics mixture sets very quickly at the surface of the filler, which is at a higher temperature, yet the intermediate volume between the filler particles remains fluid and is further distributed by the direct pressure of the binder in the mould, where it reacts out at other filler surfaces. According to the invention this in the first place results in a uniform age distribution of the reactive plastics mixture due to the surfaces of the filler particles being covered by the binder which is fed in first and the interstices being occupied by the binder which is fed in last. Secondly, the moulded body always sets from the surfaces of the filler particles inwards towards the interstices. The moulded body can as a result adapt stress-free to the mould until it has completely set.
The reactive plastics mixture which is used is preferably a reactive polyurethane mixture. Generally suitable constituents of the reactive polyurethane mixture are disclosed in, for example, DE-A 1 694 138. The isocyanates used are preferably those based on diphenylmethane diisocyanate. Preferred polyols are polyether polyols. The mixture may also comprise expanding agents in quantities such that the resulting density of the set polyurethane is between 200 and 1,200 kg/m
3
, preferably 400 to 800 kg/m
3
. It is preferable to use water in quantities of 0.5 to 3 wt. %, related to the mixture, as the expanding agent.
The mixture is preferably produced in an injection mixing head, the outlet of which delivers directly into the mould. Mixing heads of this kind are basically known in polyurethane technology (see Becker/Braun, Kunststoff-Handbuch (Plastics Handbook), Vol. 7: Polyurethanes, 1993, p. 177 ff.) Depending on the complexity of the moulding to be produced, it may be necessary to provide a plurality of mixing heads simultaneously delivering into the mould in order to distribute the reactive mixture uniformly over the mould volume.
The advantages of the moulded bodies according to the invention with respect to concrete or conventional polymer concrete are higher productivity, due to rapid setting of the reactive polyurethane mixture, improved resistance of the moulded bodies to chemicals and abrasion, improved toughness and reduced weight.
Moulded bodies according to the invention may be produced as soundproof walls, sewers, gutters, shaft linings, dewatering systems, machine frames, bearing elements, feeding troughs or even grease separators. Because the reactive polyurethane mixture adheres particularly well to concrete, the method according to the invention is also highly suitable for bonding concrete elements in the building construction field or when laying concrete pipes. In this case the elements to be bonded are surrounded by sleeves which form the mould cavity.
REFERENCES:
patent: 3281515 (1966-10-01), Schmitz
patent: 4504283 (1985-03-01), Charvat
patent: 4588420 (1986-05-01), Charvat
patent: 4624818 (1986-11-01), Black et al.
patent: 4698010 (1987-10-01), Toncelli
patent: 4784814 (1988-11-01), Diethelm et al.
patent: 5328648 (1994-07-01), McBrien et al.
patent: 5328656 (1994-07-01), Thulin
patent: 5409654 (1995-04-01), Platusich
patent: 5503544 (1996-04-01), Platusich
patent: 5509441 (1996-04-01), Platusich
patent: 5834527 (1998-11-01), Sulzbach
Patent Abstract of Japan, vol. 18, No. 037, Jan. 20, 1994 & JP 05-269799, (Nippon Plast. Co. Ltd), Oct. 19, 1993.
Becker/Braun, Kunststoff-Handbuch, vol. 7, “Polyurehthanes”, pp. 177 to 179 (Undated).
Avar Geza
Franzen Reinhold
van Staveren Anthony Martinus Jacobus
Bayer Aktiengesellschaft
Brown N. Denise
Gil Joseph C.
Kuhns Allan R.
LandOfFree
Method for producing reactive plastic molded bodies with... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Method for producing reactive plastic molded bodies with..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Method for producing reactive plastic molded bodies with... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2571907