Specialized metallurgical processes – compositions for use therei – Compositions – Consolidated metal powder compositions
Reexamination Certificate
2000-08-09
2002-01-15
Mai, Ngoclan (Department: 1742)
Specialized metallurgical processes, compositions for use therei
Compositions
Consolidated metal powder compositions
C075S246000, C419S011000, C419S028000, C419S029000, C419S039000, C419S055000
Reexamination Certificate
active
06338747
ABSTRACT:
STATEMENT REGARDING FEDERALLY SPONSORED RESEARCH OR DEVELOPMENT
Not applicable.
TECHNICAL FIELD AND INDUSTRIAL APPLICABILITY OF THE INVENTION
The present invention is directed to a method for producing a material from a metallurgical powder and to the material produced by the method. More particularly, the present invention is directed to a method for producing a material from a metallurgical powder including iron, copper, and graphite, and wherein the method generally includes providing a sintered compact of the powder, densifying at least a portion of the compact, and subsequently increasing the surface hardness of the compact to greater than RC 25, and preferably at least RC 30. Material produced by the method exhibits high rolling contact endurance limit and/or high tensile strength. Specific examples of applications in which the method and material may be applied include races, gears, sprockets, and cam lobes.
DESCRIPTION OF THE INVENTION BACKGROUND
The “sinterhardening” process is a known process in which iron-based alloys having high hardness are produced by consolidating and sintering metallurgical powders. The alloying element and carbon contents of the metallurgical powder and the cooling rate of the sintered parts within the sintering furnace are carefully balanced to produce parts having a surface hardness greater than about Rockwell C (RC) 25 directly from the sintering furnace, without the requirement for a conventional quench-and-temper treatment. Parts having surface hardness greater than RC 25 are typically produced by sinterhardening using a furnace that is specially designed to gas cool the hot sintered parts at an accelerated rate, in the 120-200° F./minute range. More recently, sinterhardening processes have been designed to utilize metallurgical powders with higher alloy contents that can be hardened to greater than RC 25 on cooling using conventional sintering furnaces providing standard cooling rates, typically about 40° F./minute.
Sinterhardened parts are normally hard and strong (tensile strengths in the 120 to 160 ksi range). A primary advantage of the sinterhardening process is that the conventional quench-and-temper cycle is unneeded, reducing the number of processing steps and reducing the cost of finished parts. A second advantage is that gas cooling is less severe and causes less warpage than liquid cooling. Because sinterhardened parts are gas cooled rather than liquid cooled, there is generally less dimensional distortion in the parts and size control is enhanced. In addition, because there is no need to dispose of an oil or other liquid quenching medium, the impact on the environment is lessened.
A distinct shortcoming of parts produced by sinterhardening is relatively low rolling contact endurance limits, usually in the 160 to 190 ksi range. The rolling contact endurance limit, also referred to herein plainly as the “endurance limit,” is the theoretical maximum stress that a material can withstand for an infinitely large number of compressive fatigue cycles. The endurance limit of a material may be assessed by, for example, the method described in U.S. Pat. No. 5,613,180, the entire disclosure of which is hereby incorporated herein by reference. The testing method generally described in the '180 patent was used to measure the endurance limit of the materials described herein.
Rolling contact endurance is particularly important in powder metal parts such as races, gears, sprockets, and cam lobes. The relatively low rolling contact endurance limit of sinterhardened materials is not entirely unexpected because the endurance limit is strongly dependent on material density. Denser materials typically have higher endurance limits. Parts produced by sinterhardening commonly have apparent densities of about 7.0 g/cc or less, which may be compared with typical theoretical densities of about 7.9 g/cc for sinterhardening alloys.
Materials produced by sinterhardening may have tensile strength significantly greater than powder metal materials of comparable density produced by conventional quench-and-temper techniques. Tensile strength of sinterhardened parts typically falls in the range of 130 to 150 ksi. This may be compared with the 100-110 ksi tensile strength of conventional quenched and tempered powder metal material at 7.0 g/cc. Conventional materials, because they are based on “softer” powders and do not harden on sintering at 1400-1600° F., can be double processed to densities in the 7.3-7.5 g/cc range. Increasing part density can provide increased tensile strength, and also can increase endurance limit. Heat treated double pressed/double sintered parts, for example, can achieve heat treated tensile strengths of 160-200 ksi. The higher tensile strength that may result from increased density may be desirable in parts used as races, gears, sprockets, cam lobes, connecting rods, and in other high load-bearing applications. Such applications usually also require high endurance limit. In contrast, increasing the density of sinterhardened parts to provide higher endurance limits and tensile strength is problematic. The metallurgical powder grades used in sinterhardening are highly alloyed and, therefore, are not highly compressible. Also, because sinterhardened parts emerge from the sintering furnace relatively hard, they are not easily densified by mechanical working techniques such as sizing. Cost and other benefits derived by avoiding a quench-and-temper cycle are, in part, offset by the difficulties faced when densifying sinterhardened parts. Thus, although the sinterhardening process provides distinct advantages, it is not widely used to produce powder metal parts for the heaviest duty races, gears, sprockets, and cam lobes, applications requiring high rolling contact endurance limits and/or high tensile strength.
Accordingly, a need exists for a process for producing parts from consolidated metallurgical powder wherein the parts are of high density and surface hardness greater than about RC 25, without the need for a conventional liquid quench-and-temper treatment. A need also exists for a process for producing powder metal parts having high rolling contact endurance limits and/or high tensile strength, and wherein the parts are surface hardened to greater than RC 25 without the need for a conventional liquid quench-and-temper treatment.
BRIEF SUMMARY OF THE INVENTION
In order to address the above-described needs, the present invention provides a novel method for producing a material from a metallurgical powder. The method includes providing a metallurgical powder that includes iron, 1.0 to 3.5 weight percent copper, and 0.3 to 0.8 weight percent carbon. The carbon in the metallurgical powder preferably is wholly or predominantly in the form of graphite. The copper in the metallurgical powder preferably is wholly or predominantly in the form of elemental copper powder. The metallurgical powder also may include, for example, nickel, molybdenum, chromium, manganese, and vanadium. The metallurgical powder preferably includes molybdenum and/or nickel in the form of a pre-alloyed iron-base powder.
At least a portion of the metallurgical powder is compressed at a pressure of 20 tsi to 70 tsi to provide a compact. The compact is heated to a temperature of 2000-2400° F. and is maintained at the temperature for at least 15 minutes. The heated compact is then cooled at a cooling rate no greater than 60° F./minute. The rate of cooling is selected so that the compact, once cooled, has hardness no greater than RC 25, and preferably no greater than RC 20. Subsequent to cooling the compact, the density of at least a surface region of the compact is increased to at least 7.6 grams/cc. The density of the compact may be increased by, for example, mechanically working the sintered compact. The mechanical working technique that is used may be one or more of, for example, sizing, rolling, roller burnishing, shot peening, extruding, laser impacting, swaging, and hot forming. The densification technique may be applied to increase the density of a surface region o
Keystone Investment Corporation
Kirkpatrick & Lockhart LLP
Mai Ngoclan
LandOfFree
Method for producing powder metal materials does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Method for producing powder metal materials, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Method for producing powder metal materials will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2872465