Synthetic resins or natural rubbers -- part of the class 520 ser – Synthetic resins – From carboxylic acid or derivative thereof
Reexamination Certificate
2001-08-09
2003-02-25
Hampton-Hightower, P. (Department: 1711)
Synthetic resins or natural rubbers -- part of the class 520 ser
Synthetic resins
From carboxylic acid or derivative thereof
C528S312000, C528S319000, C528S320000, C528S322000, C528S323000, C528S324000, C528S170000
Reexamination Certificate
active
06525167
ABSTRACT:
Nylon-6 is used for the manufacture of fiber, film and moldings. The polymers obtained by melt polymerization include a high level of &egr;-caprolactam and of low molecular weight reaction products (oligomer) because of the chemical equilibria. Since caprolactam oligomer and caprolactam monomer are soluble and extractable in water, the level of low molecular weight constituents in the polymer is also known as its extractables content.
To prevent any impairment to product quality and processing properties, for example during injection or extrusion molding or during spinning, the extractables content has to be lowered.
The requisite extraction is usually carried out with water at elevated temperatures, as described for example in DE-A-25 01 348 or DE-A-27 32 328. To increase the yield of the polymerization and to avoid any adverse impact on the environment, aqueous extracts are frequently not disposed of as waste, but are recycled.
The lower solubility of oligomer and especially dimer is not the least reason why complicated and energy-intensive processing steps have to be used for the extraction in order that polyamides of satisfactory quality may be obtained. In existing processes, caprolactam monomer is used as a solubilizer for lactam oligomer in the extraction of nylon-6. DE-A-43 24 616 therefore proposes adding caprolactam monomer to the water at the start of the extraction.
Processes are also known in which the extractables content is lowered by vaporizing the monomer and oligomer out of the polymer. DE-A-29 48 865 discloses a demonomerization process wherein the polymer is subjected to a vacuum in the molten state and in the form of thin films.
All the processes mentioned have the disadvantage of requiring in some instances multistage, costly and energy-intensive steps to demonomerize the polymer and to work up the aqueous extract.
A further problem is the change in the product properties on further processing extracted nylon-6 having a low residual extractables content and a defined viscosity. The polymer is usually processed, for example for extrusion or spinning, by reheating and liquefying it. The high temperatures are known to change or increase the viscosity and the residual extractables and residual monomer content. This viscosity instability and remonomerization have an adverse effect not only on processing operations but also on product quality.
It is an object of the present invention to provide a process for producing polyamides which have a reduced extractables and dimer content even in the unextracted state, so that the technical and economic effort needed to extract the low molecular weight constituents and to work up the aqueous extract is reduced, and which, under customary processing temperatures and conditions, have a higher viscosity stability and a lower increase in the residual extractables content than known polyamides.
We have found that this object is achieved according to the invention by a process for producing low-monomer and -oligomer nylon-6 by continuous hydrolytic poly-merization of aminonitriles, preferably &ohgr;-aminocapronitrile, ACN in short, and optionally further polyamide-forming monomers in the presence of metal oxides. The metal oxides are used in a form which permits mechanical removal from the reaction mixture.
The novel continuous process for producing polyamides by reacting at least one aminonitrile with water comprises the following steps:
(1) reacting at least one aminonitrile with water at a temperature of from 200 to 290° C. at a pressure of from 40 to 70 bar in a flow tube containing a Brönsted acid catalyst selected from a beta-zeolite, sheet-silicate or metal oxide catalyst in the form of a fixed bed,
(2) diabatically or adiabatically expanding the reaction mixture from step (1) into a first separation zone to a pressure of from 20 to 40 bar, the pressure being at least 10 bar lower than the pressure in step (1), and to a temperature within the range from 220 to 290° C. by flash evaporation and removal of ammonia, water and any aminonitrile monomer and oligomer,
(3) further reacting the reaction mixture from step (2) in the presence of water at a temperature of from 200 to 290° C. and a pressure of from 25 to 55 bar and in the presence or absence of a Brönsted acid catalyst selected from a beta-zeolite, sheet-silicate or metal oxide catalyst in the form of a fixed bed,
(4) diabatically or adiabatically expanding the reaction mixture from step (3) into a second separation zone to a pressure of from 0.01 to 20 bar, the pressure being at least 20 bar lower than the pressure in step (3), and to a temperature within the range from 220 to 290° C. by flash evaporation and removal of ammonia, water and any aminonitrile monomer and oligomer.
The process preferably further includes the following step:
(5) postcondensing the product mixture from step (4) at a temperature of from 230 to 280° C. and a pressure of from 0.01 to 10 bar.
The aminonitrile monomers and oligomers removed by flash evaporation in steps (2) and (4) are preferably returned into the reaction.
According to the invention, the heterogeneous catalysts used can be known metal oxides, such as zirconium oxide, aluminum oxide, magnesium oxide, cerium oxide, lanthanum oxide and preferably titanium dioxide as well as silicates, such as beta-zeolites and sheet-silicates. Particular preference is given to titanium dioxide in the anatase form. The anatase fraction is preferably at least 70% by weight, particularly preferably at least 90%, especially essentially 100%. It was further found that even silica gel, zeolites and doped metal oxides, doped with ruthenium, copper or fluoride, for example, distinctly improve the reaction of the reagents mentioned. Suitable catalysts are particularly notable for the fact that they are slightly Brönsted acidic and have a large specific surface area. According to the invention, the heterogeneous catalyst has a macroscopic form which permits mechanical separation of the polymer melt from the catalyst, for example by means of sieves or filters. The proposal is for the catalyst to be used in extrudate chip form or as coating on packing elements.
The individual process steps will now be more particularly described.
Step (1): Reaction of the reaction mixture in a flow tube which is fitted out with metal oxide catalysts and which is preferably operated as a single liquid phase, at a temperature of from 200 to 290° C., preferably from 210 to 260° C., particularly preferably from 225 to 235° C. The pressure is preferably set to within the range from 20 to 100 bar, especially from 40 to 70 bar. The catalyst material is present as a fixed bed and remains in the reactor.
Step (2): The pressurized reaction mixture is subsequently expanded adiabatically into a separation zone. The pressure in this separation zone is generally within the range from 20 to 40 bar, preferably within the range from 25 to 35 bar. The residence time in this first separation zone is generally within the range from 0.5 to 5 hours, preferably from 2 to 4 hours, while the temperature should be within the range from 220 to 290° C., preferably from 240 to 270° C. The process of expansion is accompanied by a flash evaporation (utilizing the heat stored in the reaction mixture) of ammonia and water quantities still present in the reaction mixture. They contain volatile constituents such as aminocapronitrile monomer and oligomer. Rectification via a column can be used to remove the water and ammonia vapors from the system and return the organics into the process, preferably into step 1.
Step (3): The pressurized mixture is subsequently transferred via a heat exchanger, together with added, likewise preheated water, into a further reactor, where it is further reacted at temperatures of from 200 to 290° C., preferably from 210 to 260° C., particularly preferably from 225 to 235° C. The pressure in the reactor is preferably again set so that the reaction mixture is present as a single liquid phase. The pressure is generally within the range from 25 to 55 bar, preferably within the rang
Hildebrandt Volker
Mohrschladt Ralf
Yamamoto Motonori
BASF - Aktiengesellschaft
Hampton-Hightower P.
Keil & Weinkauf
LandOfFree
Method for producing polyamide 6 of a low extract content,... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Method for producing polyamide 6 of a low extract content,..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Method for producing polyamide 6 of a low extract content,... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3135990