ABSTRACT:
BACKGROUND
This invention relates to a process for the production of nickel hydroxides by anodic dissolution of metallic nickel in an electrolysis cell with completely intermixed electrolysis brine.
Two processes are in particular known for the production of nickel hydroxides, namely chemical precipitation of the hydroxides from nickel salt solutions by addition of alkali metal hydroxide solutions and, secondly, anodic dissolution of nickel in an electrolysis cell, wherein hydrogen is liberated at the cathode providing the corresponding hydroxide ions.
The chemical precipitation process has the disadvantage that the neutral salts produced in stoichiometric quantities from the neutralisation reaction must be disposed of or worked up. In contrast, in electrolytic processes, it is largely possible to circulate the brine containing conductive salts by separating the precipitated hydroxide, such that the formation of secondary and waste products may largely be avoided. At least in theory, electrolytic processes should give rise to more uniform products due to the lower concentrations of the reaction partners in the precipitation suspension (electrolysis brine). However, electrolytic processes do disadvantageously exhibit a tendency towards forming anodic and/or cathodic deposits or deposits on optionally present diaphragms or membranes due to the great variations in concentration, potential and/or pH values prevailing at the corresponding boundary layers, so hindering the establishment and maintenance of process conditions which are optimal with regard to product properties or which even prevent the electrolysis from being operated at equilibrium.
It is furthermore known, for example from Japanese published patent application 56-143 671 dated 9 Nov. 1981, to produce denser nickel hydroxide powders by performing chemical precipitation from aqueous solutions of nickel ammine complex salts from which nickel hydroxide precipitates at a substantially reduced precipitation rate, such that a denser particle structure is formed Moreover, the modified crystallisation/solution equilibrium brought about by the presence of ammonia in the precipitation solution favours the formation of spheroidal agglomerates.
If the complexing agent is used in the electrolytic process, the process may be disrupted as Ni(II) in Ni(II) ammine complexes is more readily cathodically reduced than in the Ni(II) hexaaquo complex ion. The precipitated Ni forms loose deposits on the cathode. This problem is remedied according to EP-A684 324 by dividing the electrolysis cell into an anode compartment and a cathode compartment by means of a membrane permeable to hydroxide ions. In order to avoid the formation of nickel hydroxide deposits both on the membrane and on the anode, it is necessary in this process to use very high ammonia concentrations, such that the hydroxide precipitates with an increase in temperature only once it has left the reactor. Disadvantages of the membrane electrolysis process include the increased electrolysis voltage entailed by the membrane and the use of the membrane itself which is technically problematic (clogging problems), increases process costs and thus complicates commercial application.
DESCRIPTION
It has now been found that spherical nickel hydroxide may be produced by anodic dissolution of nickel directly in a completely intermixed electrolysis cell if the electrolysis brine exhibits comparatively low ammonia contents of 1 to 5 g/l and moreover the chloride ion content, pH value and temperature of the brine are maintained within certain limits.
It is apparently essential to the process according to the invention for a quasi steady-state deposit of basic nickel salt to form on the anode, which clearly assumes the function of a cation exchange membrane, i.e. is impermeable to chloride and hydroxide ions. The anodically dissolved nickel ions collide with the deposit from the anode side and are incorporated therein as basic nickel chloride. Nickel ammonium complexes which have fewer than 4 ligands and are thus relatively unstable, are obviously dissolved from the electrolyte side. Formation of the ammine complex is here apparently favoured by a boundary layer which forms on the electrolyte side of the “membrane” and, in comparison with the brine concentration, has a low OH ion content. On leaving the boundary layer with a low OH ion content, the ammine complexes dissociate before nickel is deposited on the cathode.
The present invention accordingly provides a process for the production of spherical nickel hydroxide by anodic dissolution of a nickel electrode and precipitation of nickel hydroxide in a completely intermixed electrolysis cell, which process is characterised in that that an electrolysis brine is used which has a content of 20 to 50 g/l of chloride ions and 1 to 7 g/l of ammonia with a pH value of 9.5 to 11.5 and a temperature of 45 to 60° C. The molar ratio of chloride ions to ammonia should preferably be from 2 to 10.
Sodium sulfate may additionally be added to the electrolyte in order to dope the product with sulfate.
The electrolysis brine preferably exhibits a pH value of below 11, particularly preferably between 10 and 10.5 (at reaction temperature). The chloride ion concentration is provided by an aqueous solution of alkali metal chlorides. The pH value is established by apportioning an alkali metal hydroxide solution or hydrochloric acid as a function of continuous pH measurement.
According to the invention, a “completely intermixed electrolysis cell” is taken to mean a single electrolysis cell in which the anode and cathode are in contact with substantially the same brine, i.e. in which there is no structural separation of the cell volume into an anode and a cathode compartment by diaphragms or membranes. This disregards the membrane function of the deposits of basic nickel salt formed in situ. According to the invention, “completely intermixed” furthermore means that, with the exception of boundary layer effects in the vicinity of the anode surfaces, the brine itself is of a uniform composition, which is ensured by turbulent intermixing. This is achieved by continuously withdrawing brine from the electrolysis cell by means of a piping system comprising a pump and arranged outside the cell and returning the brine to the cell, i e. the brine is recirculated through the electrolysis cell. The brine recirculation rate is preferably at least 100 times the filling volume of the cell, in particular more than 200 times and particularly preferably 400 to 1000 times the filling volume of the electrolysis cell. The elevated recirculation rate in the cell of at least 20 cm/s ensures that the same brine parameters prevail in the electrolysis cell as in the recirculation circuit outside the cell. The elevated recirculation rate in particular ensures that the increase in temperature of the brine is minimal on a single passage. Temperature control is provided by a heat exchanger arranged in the recirculation circuit outside the cell.
Hydrogen deposited at the cathode is produced as the secondary product of the process and is withdrawn from the cell above the brine. The dispersed hydrogen bubbles provide additional turbulent mixing of the brine.
The average residence time of the brine is for example 3 to 5 hours, i.e. some ⅓ to ⅕ respectively of the filling volume of the cell is discharged from the recirculation circuit each hour, the nickel hydroxide particles are separated from the discharged brine and the brine returned to the recirculation circuit.
The nickel hydroxide particles may be separated by filtration or by using centrifugal forces, for example in a centrifugal decanter. The separated nickel hydroxide is then washed first with completely deionised water, then with dilute, for example 1 molar, sodium hydroxide solution and then again with completely deionised water before subsequently being dried.
Electrolytic dissolution of the nickel is preferably performed at a current density of 500 to 2000 A/m
2
. Depending upon electrode spacing, the requisite voltage
Gille Gerhard
Meese-Marktscheffel Juliane
Olbrich Armin
Schmoll Josef
Schrumpf Frank
Akorli Godfried R.
Eyl Diderico van
H. C. Starck GmbH
Phasge Arun S,.
LandOfFree
Method for producing nickel hydroxides does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Method for producing nickel hydroxides, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Method for producing nickel hydroxides will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3319972