Method for producing melt iron

Specialized metallurgical processes – compositions for use therei – Processes – Producing or treating free metal

Reexamination Certificate

Rate now

  [ 0.00 ] – not rated yet Voters 0   Comments 0

Details

C266S160000, C266S177000

Reexamination Certificate

active

06582492

ABSTRACT:

The invention relates to a method for producing molten pig iron.
For many years, considerable efforts have been made to develop reduction-melting methods capable of replacing the blast furnace in the production of molten pig iron, particularly using production units of smaller volume and avoiding the preparation of materials, i.e. directly using fines from ore and coal. Such methods are of interest, since it is possible in principle to avoid installations that need sizeable investment such as coke production plants and ore pelletisation plants.
The methods currently available have some disadvantages.
One of the difficulties of such a method for producing pig iron directly lies in the fact that the two components of the method—the direct reduction and the melting—require different operating conditions. This is because, during the reduction of the iron ore particles, an attempt is made to maintain a reducing atmosphere, while during the melting, large amounts of oxygen must be injected so that the energy in the carbon-containing fuels can be exploited efficiently.
In the known methods, the gases from the melting furnace are injected into the pre-reduction furnace. As the gases from the melting furnace are poor in carbon monoxide and rich in carbon dioxide, the injection of large amounts of such gases into the pre-reduction furnace upsets the reduction of the iron ore.
In an improved version of this method, the hot gases from the melting furnace are enriched in carbon monoxide before being injected into the pre-reduction furnace. The gases rich in carbon dioxide from the melting furnace are put into contact with some coal, and a large proportion of the carbon dioxide is converted into carbon monoxide by reacting with the coal. The increased reducing power of the gases from the melting furnace of course promotes the reaction inside the pre-reduction furnace. However, this operation is energetically expensive.
It would be advantageous to have available an optimised method for producing pig iron directly from the pre-reduced iron particles.
The document WO 97/17473 relates to a method of producing metals and metal alloys from metallic oxides. In a first step of the method, metallic oxides and/or partially-reduced metallic oxides and a solid carbonaceous material are injected into a pre-reduction vessel in order to reduce partially metallic oxides and/or partially-reduced metallic oxides, and release at least part of the volatile fraction of the solid carbonaceous material. In a second step, the reduction of the partially-reduced metallic oxides is continued in order to produce molten metal. To achieve this, the partially-reduced metallic oxides and the solid carbonaceous material at least partially devolatilised in the first stage are injected into a reduction/melting vessel containing a bath of molten metal and slag.
The first stage of the method in WO 97/17473 preferably comprises a drying, preheating and partial reduction stage for the metallic oxides in a first pre-reduction vessel, with gases from the reduction/melting furnace and/or the second pre-reduction vessel. After that, the pre-reduced, dried and pre-heated metallic oxides are transferred, together with the solid carbonaceous material, to the second pre-reduction vessel in order to continue the reduction of the metallic oxides and the at least partial liberation of the volatile fractions in the solid material containing carbon.
Document DE 42 40 197-A relates to a method of producing pig iron from metallic oxides. The iron ore is first treated in a reduction unit and then introduced into a melting unit.
In the reduction unit, a reducing gas comprising carbon monoxide and hydrogen flows from bottom to top. The iron ore and, and optionally additives, passes from top to bottom, where it is discharged for subsequent treatment in the melting unit. Reducing gas is taken from the melting unit. The reduction unit comprises a set of gas distribution platforms, arranged obliquely in a zigzag cascade, along which iron ore, and optionally additives, passes downwards through the furnace. Coarse-grained metallic oxides and any necessary additives are introduced into the upper part of the reduction unit. Metallic oxides of finer granulometry are introduced into the central part of the reduction unit, and the optional additives of finer granulometry are introduced into the central or lower part of the reduction unit.
The reducing gas, which rises through reduction unit, thus passes through layers of iron ore optionally mixed with additives, moving down from the top to the bottom of the furnace, and in this way effects the reduction and simultaneously frees itself from most of the carried dust in this layers.
JP 62 188714-A discloses a method for producing molten pig iron. A fixed-bed reduction/coking reactor is charged with iron ore and coal in order to pre-reduce the iron ore and convert the coal to coke. Pre-reduced iron ore and coke is then used to charge a refining furnace to melt them using oxygen injection.
The objective of the present invention is to propose an optimised method for the production of pig iron.
In conformity with the invention, this objective is achieved by a method of producing molten pig iron comprising the following steps:
(a) reduction of iron ore particles to form pre-reduced iron containing surplus free carbon.
(b) transfer while hot of the pre-reduced iron to a melting furnace,
(c) melting of the pre-reduced iron particles in a melting furnace in order to obtain the molten pig iron.
According to an important aspect of the invention, step (a) comprises the following steps:
(a1) the iron ore is introduced into a multiple-hearth furnace with several superimposed hearths and it is deposited on the uppermost hearth of the multiple-hearth furnace,
(a2) the iron ore is gradually transferred to the lower hearths,
(a3) a carbon-containing reducing agent is added to one or more of the lower hearths in sufficient amounts to reduce the iron ore and to ensure that there is surplus free carbon,
(a4) the multiple-hearth furnace is heated and the iron ore is reduced on contact with the carbon-containing reducing agent and the gases produced by the carbon-containing reducing agent at adequate temperatures,
(a5) the excess gas produced by the carbon-containing reducing agent is burnt in the upper part of the multiple-hearth furnace and advantage is taken of the resultant heat to dry and pre-heat the iron ore in the upper hearths.
Slag-forming agents may also be added during step (a) or step (b). These slag-forming agents are chosen preferably from among a group consisting of lime, limestone flux and magnesia as well as mixtures of them.
Advantageously, the pre-reduced iron is compacted before its transfer to the melting furnace. Briquettes are formed which contain the pre-reduced iron, the surplus free carbon and, if necessary, the slag-forming agents. Since the briquettes have a higher density than the particles from which they are formed, they have the following advantages: they more easily penetrate the bath of molten pig iron contained in the melting furnace, a smaller amount of pre-reduced iron is trapped in the layer of slag covering the molten pig iron and a smaller proportion of the iron and free carbon is carried away by the gases escaping from the melting furnace.
The surplus carbon at the end of step (a) advantageously lies between 7 percent and 15 percent, and is preferably close to 10 percent.
The solid carbon-containing reducing agent is chosen from among coal or liquid or solid petroleum products. The volatile fractions contained in the carbon-containing reducing agent are eliminated during their residence inside the multiple-hearth furnace, and the sulphur is also partly eliminated.
Part of the surplus carbon is consumed during step (c).
According to a particular method of execution, the melting furnace is an electric arc furnace.
Oxygen is injected during step (c) in order to burn the surplus free carbon and thus to contribute a large proportion of the energy necessary for the melting during step (c). Moreo

LandOfFree

Say what you really think

Search LandOfFree.com for the USA inventors and patents. Rate them and share your experience with other people.

Rating

Method for producing melt iron does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Method for producing melt iron, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Method for producing melt iron will most certainly appreciate the feedback.

Rate now

     

Profile ID: LFUS-PAI-O-3129377

  Search
All data on this website is collected from public sources. Our data reflects the most accurate information available at the time of publication.