ABSTRACT:
FIELD OF THE INVENTION
The invention relates to a process for preparing highly pure LiBF
4
in diethyl ether, and also to its use for producing lithium ion batteries.
LiBF
4
can be used as a conducting salt for electrolytes in primary cells or secondary cells. In particular, it is used in rechargeable lithium ion batteries. The electrolytes are non-aqueous solutions of LiBF
4
in organic media, e.g. in diethyl carbonate, dimethyl carbonate, ethylene carbonate or propylene carbonate or others, or mixtures of the solvents mentioned.
Very high requirements are placed upon the purity of the LiBF
4
for this application. A particular requirement is that the LiBF
4
has a very low content of free hydrogen fluoride, very low water content, and only very small amounts of foreign metal ions. Contamination with organic carbon compounds also has to be avoided.
DESCRIPTION OF THE RELATED ART
Various methods are known for preparing LiBF
4
.
JP-A 61 151023 and JP-A 61 151024 describe processes in which LiF is reacted with BF
3
in liquid HF to give LiBF
4
. Impurities then have to be removed in a second step by treatment with elemental fluorine in inert gases or in inert solvents. However, work with liquid HF and with elemental F
2
is dangerous, and complicated safety precautions are therefore necessary.
Preparation in organic solvents has also been described in order to avoid preparation in liquid HF.
SU 1013405 describes the preparation of LiBF
4
in tetrahydrofuran, in which LiBF
4
has good solubility, by reacting LiF with BF
3
in yields of from 86-89%. The product is isolated by concentrating the THF solution. This generally gives a product which still has considerable amounts of residual THF. To remove THF completely, drying in vacuo at from 70 to 80° C. for from 10 to 15 hours using specific temperature programs is proposed. Procedures of this type are inconvenient and expensive.
JP-A 56 145113 discloses a process for preparing LiBF
4
by reacting LiF with BF
3
in non-aqueous organic solvents in which LiBF
4
has good solubility and which can form complexes with BF
3
. Examples mentioned are tetrahydrofuran, dimethoxyethane, ethyl acetate and propylene carbonate. After the reaction of LiF with BF
3
, impurities are filtered off. LiBF
4
is crystallized out from the filtrate by saturating the solution with BF
3
. With the solvent BF
3
forms a complex in which LiBF
4
has low solubility, and crystallizes out. Problems with this process are the complete removal of any BF
3
adhering to the product and the need to use a considerable excess of BF
3
. Diethyl ether is not used for the process mentioned since the solubility of LiBF
4
in diethyl ether at 25° C. is only 1.3 g/100 ml (JACS, 75 (1953) 1753).
A process has also been disclosed (JACS, 75 (1953) 1753) for preparing LiBF
4
in diethyl ether by reacting lithium carbonate with boron trifluoride according to the reaction equation 3 Li
2
CO
3
+8 BF
3
→6 LiBF
4
+3 CO
2
+B
2
O
3
. The B
2
O
3
formed as coproduct, and also undissolved LiBF
4
, are filtered off and the filtrate is concentrated to obtain LiBF
4
. Further amounts of LiBF
4
have to be isolated by extracting the filtered-off B
2
O
3
/LiBF
4
mixture with diethyl ether. However, this process is not cost-effective. Firstly, the low solubility of LiBF
4
in diethyl ether means that large amounts of solvent have to be used and then evaporated, and this does not remove the requirement for an additional extraction of the residue. Besides this, some of the BF
3
is converted into B
2
O
3
coproduct.
BRIEF SUMMARY OF THE INVENTION
It is an object of the present invention to provide a simple process for cost-effective preparation of highly pure LiBF
4
which can be used for producing lithium ion batteries.
We have found that this object is achieved by means of a simple and cost-effective process in which, despite the low solubility of LiBF
4
in diethyl ether, LiF can be reacted virtually completely with BF
3
etherate and LiBF
4
prepared with a high level of purity.
The invention therefore provides a process for preparing highly pure LiBF
4
by preparing a solution of BF
3
etherate in diethyl ether, suspending LiF in this solution, reacting to give solid LiBF
4
, and then separating off the solid LiBF
4
formed.
The novel process uses BF
3
etherate. The BF
3
etherate is preferably diluted with diethyl ether. The solution of BF
3
etherate in diethyl ether can be prepared by diluting pure BF
3
etherate with diethyl ether. It is also possible to pass the desired amount of gaseous BF
3
into diethyl ether. The molar ratio of diethyl ether to BF
3
etherate is preferably from 0.1 to 3, particularly preferably from 0.5 to 1.5.
Finely divided LiF is added to this solution and suspended in the solution. The LiF is advantageously ground before addition. However, it is also possible to suspend LiF in diethyl ether and to add this suspension to pure BF
3
etherate or to a solution of BF
3
etherate in diethyl ether, or to pass BF
3
gas into the suspension. The amount of BF
3
etherate used is at least stoichiometrically equivalent to that of LiF. It is advantageous to work with a small excess of BF
3
etherate, but the molar ratio of BF
3
etherate to LiF should not be greater than 1.2. The molar ratio of BF
3
etherate to LiF is preferably from 1 to 1.1.
The reaction is generally carried out with heating, preferably heating to reflux. The reaction time depends on the temperature selected. The reaction is generally allowed to continue for from 4 to 10 h. However, it is also possible to work at room temperature with a corresponding increase in reaction time.
The suspending of LiF and the reaction to give LiBF
4
are advantageously carried out with intensive mixing, for example with the aid of stirrers or of dispersing equipment. Mixing devices and apparatuses of this type are known per se.
The LiBF
4
obtained from the reaction, substantially suspended in diethyl ether, is separated off by processes known per se, such as filtration, pressure filtration, centrifuging or decanting, and dried. Before filtering off it is advantageous to cool the suspension at least to room temperature.
Surprisingly, in spite of the low solubility of LiBF
4
in diethyl ether, the suspended LiF reacts virtually completely with the BF
3
to give LiBF
4
. The proportion of LiF in the final LiBF
4
product is not more than 2% by weight, generally less than 1%. The final product also has only low proportions of acid impurities, low moisture and low proportions of heavy metals. The highly volatile diethyl ether is easily removed from the final product. The residual proportion of organic carbon (total organic carbon, TOC) is less than 0.1% by weight.
This purity gives the LiBF
4
prepared by the novel process excellent suitability for use as a conducting salt in lithium ion batteries.
DETAILED DESCRIPTION OF THE INVENTION
REFERENCES:
patent: 56-145113 (1981-11-01), None
patent: 61-151023 (1986-07-01), None
patent: 61-151024 (1986-07-01), None
patent: 11-157830 (1999-06-01), None
patent: 1013405 (1983-04-01), None
patent: 1655083 (1994-07-01), None
JACS, 75 (1953), 1753, No Month Available.
Friedrich Holger
Simon Joachim
BASF - Aktiengesellschaft
Kalafut Stephen
Keil & Weinkauf
Tsang-Foster Susy
LandOfFree
Method for producing highly pure LiBF4 does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Method for producing highly pure LiBF4, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Method for producing highly pure LiBF4 will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3039886